Understanding the influence of boron in additively manufactured GammaPrint®-700 CoNi-based superalloy
Boron is commonly added to superalloys in small amounts to enhance creep resistance, but can lead to cracking at high concentrations, especially during the additive manufacturing process. Two variants of CoNi-based GammaPrint®-700 superalloy with different B contents (0.08 at% vs 0.16 at%) were printed via laser powder bed fusion (LPBF) with the same printing parameters, with only the high B alloy exhibiting solidification cracking. Atom probe tomography (APT) revealed stronger segregation behaviors in the high B alloy compared to the low B alloy at both the inter-dendritic regions and grain boundaries (GBs). The segregation behavior at inter-dendritic regions was well captured with Scheil simulation and can correlate with the existing cracking susceptibility index (CSI) on cracking tendencies, although high angle GBs are where cracking occurs according to electron backscatter diffraction (EBSD) measurements. Additionally, the extent of GB segregation was compared between the high B and low B alloy. Higher B additions led to significantly more GB B segregation in the high B alloy compared to the low B alloy. Further, for the high B alloy, the cracked region of one GB exhibited higher levels of B compared to the uncracked region of the same GB. However, much higher B contents were also found in two other uncracked GBs in the high B alloy, which demonstrates that higher GB B concentrations are not fully responsible for the cracking. A much larger variance in GB B segregation content was found in the high B alloy compared to the low B alloy. These phenomena were explained with a solidification model with the GB segregation content expressed explicitly by a modified Langmuir-McLean equation. This model linked the GB segregation content with solidification undercooling, which can be used as quantitative cracking criteria for future builds.
36 MATERIALS SCIENCE↗
On the role of geometrically necessary dislocations in void formation and growth in response to shock loading conditions in wrought and additively manufactured Ta
This study investigates the role of geometrically necessary dislocations (GNDs) and microstructure on void nucleation and growth in wrought and additively manufactured (AM) tantalum subjected to high-strain rate loading. Multi-modal 3D data was collected using TriBeam tomography to calculate GND densities and their spatial relationship to voids. A microstructural comparison between the wrought and AM samples identified distinct void shapes and locations, with intragranular voids and more spherical voids frequently observed in the AM dataset. Results indicate that voids preferentially form at both high-angle grain boundaries and low-angle subgrain boundaries, the latter of which are frequently observed in the AM material. Through a radial distribution analysis of all voids in the datasets, significant GND localization to near-void-surface regions was observed in both samples. 3D crystal plasticity simulations were employed to extend the experimental observations, revealing higher void growth rates in [111] oriented grains when compared to [001] grains. The simulations also suggest that GNDs can be generated as part of the void growth process, with more GND accumulation for growth in a [111] grain than a [001] grain. These findings provide valuable insights into the links between nanoscale void nucleation, mesoscale void growth, and microstructural effects in dynamically loaded tantalum.
36 MATERIALS SCIENCE↗
Quantification of melt pool dynamics and microstructure during simulated additive manufacturing
Not Available
Lamb, James (ORCID:0000000214099799)↗
Deformation mechanisms and defect structures in Heusler intermetallic MnCu 2 Al
Not Available
Materials Science↗
Complex concentrated alloys and chemical short-range ordering
Abstract Complex concentrated alloys (CCAs) are materials comprising three or more elements in similar proportions and possessing structural but no chemical long-range order. Fascination with CCAs has grown over the last 20 years and to date, CCAs have opened a new materials design paradigm and horizon for discovery of materials to meet the demands of applications in aggressive environments. Understanding the fundamental mechanisms controlling their response, however, is challenging due to the chemical and structural variations that wildly fluctuate over fine atomic and nanoscales. This issue focuses on the experimental, computational, and theoretical investigations that aim to uncover phenomena and processes determining the structure, kinetics, mechanics, or deformation mechanisms in CCAs at the atomic scale. At the atomic scale at which they operate, chemical short-range ordering can be influential. This issue further addresses the capabilities, as well as the debatable need, to characterize, predict, and relate short-range ordering to material performance. Collectively, the articles in this issue highlight the insights, understanding, and experimental and computational tools that attempt to create property-tunable CCAs “from the atom up” by treating short-range ordering and engineering atomic-scale mechanisms. Graphical abstract
36 MATERIALS SCIENCE↗
Inducing skyrmion flop transitions in Co 8 Zn 8 Mn 4 at room temperature
Magnetic skyrmions are topologically-protected spin textures that manifest in certain noncentrosymmetric ferromagnets under the right conditions of temperature and field. In thin-film skyrmion hosts, demagnetization effects combined with geometric confinement can result in two distinct types of spin textures: those with their axis of symmetry in the plane of the film (IP) and those with their axis pointing out-of-plane (OOP). Here we present Lorentz transmission electron microscopy evidence in conjunction with numerical modeling showing a flop transition between IP and OOP skyrmions in Co 8 Zn 8 Mn 4 at room temperature. Further, we show that this skyrmion flop transition is controllable via the angle of the external field relative to the film normal and we illustrate how this transition depends on thickness. Finally, we propose a skyrmion-writing device that utilizes the details of this transition.
36 MATERIALS SCIENCE↗
Slip localization behavior at triple junctions in nickel-base superalloys
Incipient slip localization in the vicinity of hundreds of grain boundary triple junctions (TJs) in a lightly deformed nickel-base superalloy IN718 is studied using a combination of three-dimensional (3D) crystal plasticity finite element (CPFE) modeling, high resolution digital image correlation (HR-DIC) and 3D electron back-scatter diffraction tomography (3D EBSD). A 3D reconstruction method enables identification of thousands of TJs and correspondence of any observed slip bands with their originating TJ lines below the specimen surface. Here, we present a large-scale CPFE model of the experimental 3D microstructure composed of high-fidelity representation of the TJ lines and the boundaries and interiors of the parent grains and use it to calculate the local micromechanical response and slip activity of all TJs at the onset of macroscopic yielding. Statistical analysis of the calculated quantities reveal TJs develop larger stress concentration and grain-average re-orientation than grain interiors and grain boundaries, however no substantial differences in cumulative slip were found among these microstructural regions. We find that TJs with observed slip bands generate lower grain-average re-orientation, fewer active slip systems, and more localized slip on a single system than those without. The distinctions in the reorientation and slip activity are stronger in TJs that experience more intense slip.
36 MATERIALS SCIENCE↗
Minor Elements and Solidification Cracking During Laser Powder-Bed Fusion of a High $\gamma ^{\prime }$ CoNi-Base Superalloy
Here, the cracking behavior of a high γ' volume fraction CoNi-base superalloy fabricated via laser powder bed fusion (LPBF) is studied in relation to the content of carbon and boron. Severe cracking occurred with the increase in boron content from 0.08 to 0.16 at. pct (0.015 to 0.029 wt pct), while compositions with 0.1 to 0.36 at. pct C (0.02 to 0.076 wt pct) and 0.08 at. pct B exhibited minimal cracking. Assessment of cracks in the high-boron composition shows a variation in crack density with printing parameters, and alignment of the cracks with the build direction. Scanning electron microscopy (SEM) of the crack surfaces shows evidence of a solidification cracking mode. Differential thermal analysis (DTA) reveals a decreased incipient melting temperature for the high-boron composition, and atom probe tomography (APT) is used to measure the enrichment at grain boundaries, revealing distinct boron segregation. Scheil-Gulliver solidification simulations for the different C and B levels are consistent with the incipient melting behavior observed with DTA. Evaluation of the solidification cracking susceptibility from the simulations allow for comparison of the CoNi alloy behavior to Ni-base superalloys studied for LPBF fabrication and displays how such metrics may aid in the design of new precipitation-strengthened superalloys for additive manufacturing (AM).
36 MATERIALS SCIENCE↗
Determination of peak ordering in the CrCoNi medium-entropy alloy via nanoindentation
Not Available
36 MATERIALS SCIENCE↗
Subgrain geometrically necessary dislocation density mapping in spalled Ta in three dimensions
Here, in this work, the intragranular distributions of the densities of geometrically necessary dislocations (GNDs) generated in a polycrystalline tantalum (Ta) sample loaded in shock compression to spall are investigated. The sample studied is a highly resolved three-dimensional (3D) map of the orientations, grain boundary morphology, and voids across a 0.276mm 3 (with sample dimensions of 688.5µm x 669µm x 600µm) region of the microstructure about the spall plane obtained by TriBeam tomography. We present a formulation for calculating the crystallographic screw and edge character GND densities at a material point within body centered cubic (BCC) crystals when provided any number of potential slip systems or modes. Combining the 3D characterization, GND formulation, and a sample containing ≈ 6000 grains, we sought statistically relevant correlations between GND density per grain with grain size, grain orientation, void formation, and proximity from the spall plane. We show that GND density per grain increases with decreasing distance from the spall plane. Most grains had heterogeneously distributed GND densities but were free of any detectable voids, at least within the ≈ 1.5µm resolution of the characterization technique. It is found that the GND density for most grains is insensitive to grain size and grain orientation. Only the fraction of grains with the highest GND densities tended to have a [001] parallel to shock-direction orientation. Intragranular 3D maps of GNDs reveals that grains that contain voids have high GND density concentrations in the intragranular region immediately surrounding the void. The local intragranular GND mapping also showed voids that are connected to grain boundaries preferred to grow into the grain with the larger size, regardless of orientation.
36 MATERIALS SCIENCE↗
Scan strategies in EBM-printed IN718 and the physics of bulk 3D microstructure development
Three-dimensional (3D) characterization provides opportunities for understanding processing-structure relationships in additively manufactured (AM) materials. Bulk samples of Inconel 718 were fabricated via electron beam melting (EBM) in order to study microstructural development as a function of energy input and beam scan strategy. TriBeam tomography of bulk Inconel 718 microstructures built under steady-state growth conditions reveals the sensitivity of microstructure formation and evolution to machine process parameters. Here, samples manufactured using a narrow range of energy input per unit build area result in varied grain morphologies and crystallographic textures. Using TRUCHAS, a thermal simulation software, the thermal history of bulk scan strategies was predicted, and combined with a calibrated microstructure-processing map to accurately predict bulk grain morphologies. The solidification parameters and the 3D measured nucleation density are used to predict the transition between columnar and equiaxed grain morphologies, providing a process map to guide AM parameter choices to locally control as-printed microstructure. A two-dimensional metric for characterizing bulk grain morphology was also found to agree well with predictions from the process map calibrated by 3D data. Combined with 3D tomography and thermal modelling, the physics of structure development were understood at a new level of detail with respect to the competing processes of grain nucleation and epitaxial growth.
36 MATERIALS SCIENCE↗
Boundary characterization using 3D mapping of geometrically necessary dislocations in AM Ta microstructure
Additive manufacturing (AM) of high strength metallic materials produces microstructures and defects that deviate substantially from those created through conventional manufacturing methods. It has recently been demonstrated that with application of extreme energy densities, a high-temperature refractory metal, tantalum (Ta), can be printed to a fully dense state with exceptionally low porosity. Here we employ a combination of three-dimensional electron backscattered diffraction (EBSD) TriBeam technology and crystallographic geometrically necessary dislocation (GND) theory to characterize the microstructure and defect boundaries of this unusual AM product. Two-dimensional (2D) EBSD and these three-dimensional (3D) measurements indicate that the microstructure of AM Ta is highly oriented <111> along the build direction, yet at the same time contains large crystallographic orientation gradients that span mm’s across the build. Crystallographic GND density analysis of the 3D microstructure reveals that highly misoriented subboundaries exist within this strongly textured microstructure that have large dislocation densities of 1×10 16 m –2 , just as large as those comprising the high-angle grain boundaries (HAGBs) in the same material. The 3D crystallographic GND density mapping reveals these subboundaries are part of a complex, finely spaced network that extends throughout the entire microstructure. Here, the orientation of these boundaries can be related to the scan strategy used during printing. TEM measurements corroborate an extremely high dislocation density at the microscale and indicate a cell-like dislocation network structure existing in the AM Ta at the sub-μm scale.
36 MATERIALS SCIENCE↗
Development of grain-scale slip activity and lattice rotation fields in Inconel 718
Using a combination of in-situ high-resolution digital image correlation (HR-DIC), Heaviside-DIC method (H-DIC), and crystal plasticity finite element (CPFE), we investigate the evolution of intragranular lattice rotations and slip activity during monotonic and cyclic loading in a high performance, polycrystalline face centered cubic material. The CPFE employs a quasi-3D model microstructure, which is a highly resolved mirror representation of the experimental in-situ test sample. In agreement, the measurements and calculations reveal that most grains, regardless of their size and lattice orientation, develop intragranular lattice rotation gradients that span the grain. For a small cluster of grains on the deformed material, we perform HR-DIC analysis of slip lines to demonstrate agreement in the active slip systems and changes in this local slip activity across the individual grains. The combined analysis reveals that deforming grains are divided into sub-granular regions of uniform lattice rotation and these regions are most often associated with only one or two active slip systems. The gradient lines that divide them correspond to changes in the predominant slip system. The model is used to examine the evolution of intragranular lattice rotation in a single fully reversed tension-compression cycle. The calculations indicate that intragranular gradients intensify during the reverse loading path as nearest neighboring regions appear to shed lattice rotation, increasing the lattice rotation in some regions, while shutting down rotation in neighboring regions. So these findings provide insight into the irreversible changes that develop within deforming grains at the scale of the grain, particularly the heterogeneous development of intragranular lattice rotation in early stages of deformation, which could serve as precursors to localization.
36 MATERIALS SCIENCE↗
Recent Developments in Femtosecond Laser-Enabled TriBeam Systems
Streams of multimodal three-dimensional (3D) and four-dimensional (4D) data are revolutionizing our ability to design and predict the behavior of a broad array of advanced materials systems. Over the last 10 years, a new 3D imaging platform consisting of a femtosecond (fs) pulsed laser coupled with a focused ion beam scanning electron microscope (FIB SEM) has been developed by UC Santa Barbara in collaboration with Thermo Fisher Scientific (formerly FEI). The femtosecond-laser-enabled FIB SEM, called the TriBeam, has become one of the only 3D serial sectioning methods available that can gather millimeter-scaled multimodal datasets at sub-μm voxel resolutions; these length scales are critical for many materials problems. Multimodal chemical, crystallographic, and morphological information can be gathered rapidly on a layer-by-layer basis and reconstructed in 3D. Large (gigabyte to terabyte scale) 3D datasets have been generated for a broad array of materials systems, including metallic alloys, ceramics, biomaterials, polymer- and ceramic-matrix composites, and semiconductors. The research tasks conducted have resulted in a completely new design, operating with a dual-wavelength femtosecond-pulsed laser on a plasma focused ion beam (PFIB) platform.
36 MATERIALS SCIENCE↗
Crystallography and elastic anisotropy in fatigue crack nucleation at nickel alloy twin boundaries
Not provided.
Materials Science↗
Modeling lattice rotation fields from discrete crystallographic slip bands in superalloys
Here in this work, we investigate the relationship between an intense slip band (ISB) and the zone of large lattice rotations that forms ahead of the tip of the ISB. We develop a crystal plasticity finite element model of a discrete ISB lying within an oligocrystalline assembly and calculate the local crystalline stress and lattice rotation fields generated by the ISB. The calculations demonstrate that, first, a region of severe lattice rotations, commonly referred to as a microvolume, does not form without the ISB, and second, large amounts of accumulated slip in the ISB are required to enlarge the microvolume to sizes and rotation magnitudes observed experimentally. Ahead of the ISB tip, the quintessential plastic zone always forms, but the atypical microvolume forms when non-concentrated and spatially diffuse slip is activated by the ISB-induced stress field. This result suggests that the detrimental ISB/microvolume pair will likely appear in pairs of crystals in which transmission of the slip from the ISB is severely blocked by the grain boundary, a hypothesis that we verify with a few target cases.
36 MATERIALS SCIENCE↗
Multimodal 3D characterization of voids in shock-loaded tantalum: Implications for ductile spallation mechanisms
Predicting the failure of crystalline materials at high strain rates requires knowledge of the underlying failure mechanisms and their dependence on microstructure. However, little experimental consensus exists on the underlying micromechanics of spallation. In this study, a 3D-EBSD characterization experiment is performed on tantalum prior to and after partial spallation by plate impact, which allowed for the statistical assessment of the microstructural neighborhoods surrounding incipient voids. In analyzing the resulting dataset containing 5884 grains and 467 voids, it is observed that the voids were roughly spherical and consistent in size throughout the spalled material. The voids mostly resided at quadruple points, at triple junctions, at grain boundaries, and within grains, in decreasing order of prevalence. Moreover, voids tended to form at grain boundaries with high degrees of plastic incompatibility, growing into the plastically soft grain but orienting primarily with or perpendicular to the loading direction. Here, the statistics from these analyses of 3D microstructural data support dynamic cavitation models for ductile spallation.