Microstructure, electrical resistivity, and tensile properties of neutron-irradiated Cu–Cr–Nb–Zr

High strength, high conductivity copper alloys that can resist creep at high temperatures are one of the primary candidates for efficient heat exchangers in fusion reactors. Cu–Cr–Nb–Zr (CCNZ) alloys, which were designed to improve the strength and creep life of ITER Cu–Cr–Zr (CCZ) reference alloys, have been found to have comparable electrical conductivity and tensile properties to CCZ alloys. The measured creep rupture times for these improved alloys is about ten times higher than the ITER reference alloys at 90–125 MPa at 500 °C. However, the effects of neutron irradiation on these alloys, and the ensuing material properties, have not been studied; thus, their utility in a fusion reactor environment is not well understood. This study characterizes the room temperature mechanical and electrical properties of a neutron-irradiated CCNZ alloy and compares them to a neutron-irradiated ITER reference heat sink CCZ alloy. Tensile specimens were neutron irradiated in the High Flux Isotope Reactor (HFIR) to 5 dpa between 250 °C and 325 °C. Post-irradiation characterization included electrical resistivity measurements, hardness, and tensile tests. Microstructural evaluation used scanning electron microscopy, energy dispersive x-ray spectroscopy, and atom probe tomography to characterize the irradiation-produced changes in the microstructure and investigate the mechanistic processes leading to post-irradiation properties. Transmutation calculations were validated with composition measurements from atom probe data and used to calculate contributions to the increased electrical resistivity measured after irradiation. Comparisons with CCZ alloys in the same irradiation heat found that the post-irradiated CCNZ and CCZ alloys had comparable electrical resistivity. Although CCNZ alloys suffered more irradiation hardening than CCZ, the overall tensile behavior deviated very little from non-irradiated values in the temperature range studied.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Strength-ductility synergy through microstructural and compositional heterogeneity in directed energy deposition additive manufacturing of face-centered cubic materials

Directed energy deposition (DED) is an additive manufacturing (AM) process based on welding technology and offers the advantages of large build volume, high deposition rate, and ability to fabricate multi-material parts. Epitaxial continuous columnar grain growth is a characteristic microstructural feature of DED processed alloys. In this study, a bamboo-like microstructure (periodic alternation of equiaxed and columnar structure) was produced by adopting an intermittent deposition strategy in 316L stainless steel and Inconel 625. The formation of a bamboo-like alternating microstructure was confirmed through electron backscattered diffraction (EBSD) analysis. Hardness mapping showed that the columnar to equiaxed transition (CET) occurred at the region right below the fusion line. A finite element (FE) model was used to investigate the relationship between the temperature gradient (G) and the solidification rate (R). The FE model showed a low G/R ratio at the region right below the interface promoting the CET. The grain size and material-dependent deformation behaviors are analyzed using digital image correlation (DIC). The lower deformation on the fine-grain regions observed in DIC analysis is attributed to a higher strain hardening rate, which is confirmed through dislocation density analysis on a tensile-interrupted specimen. The periodically alternating grain size coupled with the microstructural changes caused by intermittent deposition strategy result in a better strength-ductility synergy in both single-material and bimetallic specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Experimental and Numerical Characterization of High Temperature Deformation Behavior of 347H Stainless Steel

This study investigates how temperature affects the plasticity and thermal creep behavior of 347H stainless steel under uniaxial tension. The research combined experimental testing with advanced computational modeling. Two types of experiments were conducted: uniaxial tensile tests at temperatures from 100°C to 750°C using strain rates of ~10⁻⁴ s⁻¹, and creep tests at temperatures between 600°C and 750°C under various stress levels. These experimental results were used to develop and validate a new integrated mechanistic model that can predict material behavior under any loading condition while accounting for both stress and temperature effects. The model was implemented using a polycrystalline microstructure simulation framework based on elasto-viscoplastic Fast Fourier Transform (EVPFFT). It incorporates three key deformation mechanisms: thermally activated dislocation glide, dislocation climb, and vacancy diffusional creep. The model accounts for internal stress distribution within single crystals and considers how precipitates and solute atoms (both interstitial and substitutional) affect dislocation movement. After validation against experimental data, the model was used to generate Ashby-Weertman deformation mechanism maps for 347H steel, providing new insights into how microstructure influences the activation of different creep mechanisms.

Joy, Jobin K.↗
DOE OSTI2024

Characterization of Precipitation-Strengthening Heat-Resistant Austenitic Stainless Steels for Life-Prediction Modeling

In this study, the role of minor alloying additions in 347H stainless steels (UNS34709, ASTM A240/240M) on creep-rupture properties at 650-750°C and microstructure evolution during isothermal exposure at 750°C has been investigated, aiming to provide the experimental dataset as boundary conditions of physics-based modeling for material/component life prediction. Four different 347H heats containing various amounts of boron and nitrogen additions were prepared and evaluated. The combined additions of B and N are found to stabilize the strengthening secondary M23C6 carbides and retarding the transition from M23C6 to sigma phase precipitates during thermal exposure. The observed kinetics of microstructure evolution reasonably explains the improvement of creep-rupture properties of 347H stainless steels with the B and N additions.

Yamamoto, Yukinori↗
DOE OSTI2024

The many faces of θ' -Al 2 Cu precipitates: Energetics of pristine and solute segregated Al/ θ' semi-coherent interfaces

θ'-Al 2 Cu precipitates in Al-Cu alloys have various distorted octagon shapes, which can be explained by the competition between {100} and {110} type semi-coherent interfaces with the Al matrix. While most prior studies on the semi-coherent Al/θ' interfaces have focused on the {100} orientation, little is known about the {110} interface. We have investigated the energetics of pristine and solute-segregated {110} semi-coherent Al/θ' interfaces with advanced characterization and first-principles studies. We report interfacial, strain, and solute segregation energetics of the {110} Al/θ' semi-coherent interface for 39 elements and compared them with previously reported values of the {100} interface. We discuss the atomic features and atomic local structures to identify similarities and differences between the two types of Al/θ' semi-coherent interfaces. Here, the isotropy in pristine Al/θ' semi-coherent interfacial energy and the anisotropy resulting from solute segregation provide insight into the formation of different types of θ' precipitate “faces” reported in the literature.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Understanding the influence of boron in additively manufactured GammaPrint®-700 CoNi-based superalloy

Boron is commonly added to superalloys in small amounts to enhance creep resistance, but can lead to cracking at high concentrations, especially during the additive manufacturing process. Two variants of CoNi-based GammaPrint®-700 superalloy with different B contents (0.08 at% vs 0.16 at%) were printed via laser powder bed fusion (LPBF) with the same printing parameters, with only the high B alloy exhibiting solidification cracking. Atom probe tomography (APT) revealed stronger segregation behaviors in the high B alloy compared to the low B alloy at both the inter-dendritic regions and grain boundaries (GBs). The segregation behavior at inter-dendritic regions was well captured with Scheil simulation and can correlate with the existing cracking susceptibility index (CSI) on cracking tendencies, although high angle GBs are where cracking occurs according to electron backscatter diffraction (EBSD) measurements. Additionally, the extent of GB segregation was compared between the high B and low B alloy. Higher B additions led to significantly more GB B segregation in the high B alloy compared to the low B alloy. Further, for the high B alloy, the cracked region of one GB exhibited higher levels of B compared to the uncracked region of the same GB. However, much higher B contents were also found in two other uncracked GBs in the high B alloy, which demonstrates that higher GB B concentrations are not fully responsible for the cracking. A much larger variance in GB B segregation content was found in the high B alloy compared to the low B alloy. These phenomena were explained with a solidification model with the GB segregation content expressed explicitly by a modified Langmuir-McLean equation. This model linked the GB segregation content with solidification undercooling, which can be used as quantitative cracking criteria for future builds.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Coexistence and Interplay of Two Ferroelectric Mechanisms in Zn 1-x Mg x O

Ferroelectric materials promise exceptional attributes including low power dissipation, fast operational speeds, enhanced endurance, and superior retention to revolutionize information technology. However, the practical application of ferroelectric-semiconductor memory devices has been significantly challenged by the incompatibility of traditional perovskite oxide ferroelectrics with metal-oxide-semiconductor technology. Recent discoveries of ferroelectricity in binary oxides such as Zn 1-x Mg x O and Hf 1-x Zr x O have been a focal point of research in ferroelectric information technology. Here, this work investigates the ferroelectric properties of Zn 1-x Mg x O utilizing automated band excitation piezoresponse force microscopy. This findings reveal the coexistence of two ferroelectric subsystems within Zn 1-x Mg x O. A “fringing-ridge mechanism” of polarization switching is proposed that is characterized by initial lateral expansion of nucleation without significant propagation in depth, contradicting the conventional domain growth process observed in ferroelectrics. This unique polarization dynamics in Zn 1-x Mg x O suggests a new understanding of ferroelectric behavior, contributing to both the fundamental science of ferroelectrics and their application in information technology.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Strengthening mechanisms for microstructures containing unimodal and bimodal γ' precipitates in ATI 718Plus

Here, the influence of γ' precipitate size distribution on the deformation mechanisms under tensile loading in ATI 718Plus was studied. A set of aging treatments within the temperature range of 720 °C–900 °C was performed on solution-treated samples to obtain various γ' precipitate size distributions. Unimodal and bimodal γ' precipitate size distributions were achieved through single-step and two-step aging sequences, respectively, and such microstructures were tensile tested to failure to assess their yield strength, ultimate tensile strength, and elongation-to-failure. Some of the tensile samples were interrupted after achieving 3–4 % plastic strain, and the deformed microstructures were examined using transmission electron microscopy to investigate the γ' precipitate-dislocation interactions. For the unimodal γ' precipitate size distribution samples with the smaller γ' precipitates (radius ~ 7 nm), dislocations sheared through the precipitates. Both dislocation loops and paired dislocations were observed for the microstructures containing larger γ' precipitates (radius ~ 24 nm). The microstructure containing a bimodal γ' precipitate size distribution, which included average γ' precipitate radii of ~6 nm and ~28 nm, exhibited shearing as the dominant deformation mechanism, and this microstructure exhibited the highest strength values. The experimental observations were rationalized based on the theoretically-calculated critical resolved shear stress values for shearing and looping and a modified model for predicting the yield strength for bimodal microstructures was introduced.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effect of impurities on phase transformation and precipitation in a low-carbon steel

Impurity elements have been added to a commercial low carbon steel grade to simulate the levels that could arise as a result of increased scrap recycling during steel production. In this study, continuous cooling transformation (CCT) diagrams were constructed for the steels with varying levels of impurities, and it is shown that impurities suppress the phase transformation across a wide range of cooling rates. It was found that a step was formed in the start temperature curve, separating the reconstructive and displacive transformations. The influence of impurities on both the reconstructive transformation and displacive transformation are discussed. Additionally, Cu precipitates were observed using scanning transmission electron microscopy (STEM) in the highest impurity-containing steel after slow cooling (0.05°C/s), fast cooling (5°C/s) and interrupted cooling. It was found that the precipitation kinetics is in the following order: cementite within the secondary phase and cementite at secondary phase-ferrite interface> ferrite grain boundaries> ferrite grain matrix. Atom-probe tomography (APT) revealed Cu precipitates formed on the surface of cementite lamellae, but not within it. This work offers insights for the phase transformation control and precipitation regulation during the thermomechanical processing of low carbon steels containing impurity elements due to scrap recycling.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Microstructural evolution in doped high entropy alloys NiCoFeCr-3X (X=Pd/Al/Cu) under irradiation

Commonly studied equatomic single-phase FCC high entropy alloys based on 3d transition metals like NiCoFeCr do not provide adequate strength and radiation resistance at high doses for nuclear structural applications. In the current study, the major alloying effects like lattice distortion, ordering and clustering tendencies were investigated by adding low concentration of Pd, Al, or Cu respectively to study the doping effects on the ion irradiation response of NiCoFeCr alloy. The alloys were irradiated with 3 MeV Ni 2+ ions at 500 °C to a fluence of 1 × 10 17 /cm 2 at a beam flux of approximately 2.8 × 10 12 ions/cm 2 /s. The microstructural evolution upon irradiation i.e., formation of dislocation networks, radiation induced segregation and precipitation, and void formation were studied in detail. Further, post-irradiation characterization results showed that a Pd addition leads to a high void nucleation rate but controlled void growth, which may be attributed to increased lattice distortion. In Al added HEA, our microstructural analysis indicates that radiation induced ordered L1 2 precipitates do not affect void swelling significantly. Cu addition led to Cu precipitation that drastically suppressed dislocation density and void swelling of the alloy. Additionally, a model was developed to qualitatively describe the trend in void swelling of typical FCC alloys under ion irradiation. This model was able to qualitatively explain the suppression and reappearance of void swelling in ion irradiated alloys that generally occurs near the region with peak implanted ion concentration.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Laser powder bed fusion of oxide dispersion-strengthened IN718 alloys: A complementary study on microstructure and mechanical properties

In this study, two new grades of oxide dispersion strengthened (ODS) Inconel 718 (IN718) alloys were designed by the thermochemical CALPHAD method and produced by laser powder bed fusion (LPBF) technique. Alloys designated as IN718-YF and IN718-YFH, that consist Y 2 O 3 –FeO and Y 2 O 3 –FeO–Hf, respectively, were fabricated with >99.9 % densification using optimized process parameters. CALPHAD calculations were highly consistent with experimental findings, highlighting the formation of Al-containing Y–Ti–O and Y–Hf–O nano-oxides in both alloy types. Texture analyzes revealed no significant texture development in as-built (AB) or heat-treated (HT) alloys. Heat treatment was applied at 1050 °C for 1 h to enhance nano-oxide density. Further, the nano-oxide number density remained similar in IN718-YF while it decreased in IN718-YFH alloy as a result of carbide formation after the heat treatment. Besides, formation of secondary γ' particles was observed in the IN718-YFH/HT alloy. Even though the yield strengths of IN718-YF and IN718-YFH alloys in both AB and HT conditions were similar, the ductility of IN718-YFH was ~50 % less in almost all conditions compared to the ductility of IN718-YF. This has been shown to be as a result of irregular shaped micron-sized Y-Hf-O oxides, martensite formation in AB condition, increased amount of carbides and existence of secondary γ' particles in HT condition in IN718-YFH. High density of stacking faults (SF) forming at the interface of the nano-oxides have been detected in IN718-YF alloys. Besides dislocation/nanoparticle interactions, SFs which are responsible for the delocalization of the deformation improve the ductility of IN718-YF alloys. Overall, high temperature mechanical tests exhibit that both alloys have higher strength with improved ductility compared to the standard IN718 alloys, indicating the contribution of the nano-oxides.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effect of microalloying additions on microstructural evolution and thermal stability in cast Al-Ni alloys

Enhancement of thermal stability in Al-Ni alloys through microalloying with slow-diffusing elements, specifically Zr, has been previously reported which is attributed to Zr segregation at the Al/Al 3 Ni interface. In this study, we explore the influence of microalloying Al-Ni alloys with Zr, Ti, V, and Fe on microstructural evolution, hardness, and electrical and thermal conductivity across a range of heat-treatment temperatures from 300 to 450 °C. The distribution of microalloying elements and precipitates after heat treatment is characterized using atom probe tomography (APT). Our investigation confirms Zr segregation to the Al/Al 3 Ni interface, while similar interfacial segregation is absent with the addition of Ti, V, and Fe. Additionally, our analysis of the Al 3 Ni microfiber morphology reveals that their coarsening and spheroidization rates are similar with and without interfacial segregation; thus, retaining the fiber reinforcement through interfacial segregation of slow diffusing elements may not be an effective strategy. Precipitation of L1 2 nanoparticles was found to be the dominant mechanism affecting enhanced hardness and electrical conductivity in Al-Ni-Zr alloys, attributed to precipitation strengthening and solute depletion, respectively. Similar precipitation was not observed for additions of Ti, V, and Fe following heat treatment. We provide a thermodynamic explanation for this limitation. Furthermore, the findings of this study suggest that an effective approach for designing Al-Ni alloys should involve prioritizing microalloying elements to maximize L1 2 precipitation and minimize solute content in the FCC-Al matrix post heat treatment, rather than focusing on Al/Al3Ni interfacial segregation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Enhancing Mechanical Properties of Carbon–Silicon Steel through Two–Stage Quenching and Partitioning with Bainitic Transformation: Ultimate Tensile Strength of 1875 MPa and Total Elongation of 8.03%

To achieve the desired microstructural properties, the ongoing development and innovation in new structural steels require novel thermal processing. This study aims to improve the mechanical properties of a commercial spring carbon–silicon steel by tailoring its microstructure through a process involving quenching and partitioning (Q&P) followed by bainitic transformation. A two–stage Q&P process is proposed to generate a nanoscale dispersion of stable retained austenite and carbides within the tempered martensite and bainite microstructure. The resulting tensile properties demonstrate a yield strength of 1280 MPa, an ultimate tensile strength of 1875 MPa, and a total elongation of 8.03%. These values surpass those of conventional spring 9254 steel, highlighting the effectiveness of the thermal treatment design. Microstructure analysis reveals the presence of tempered martensite, bainite sheaves, nanoscale carbides, and aggregates of retained austenite. Moreover, the resulting body–centered cubic matrix exhibits minimal lattice tetragonality of ≈1.0051, coupled with stable retained austenite featuring a carbon concentration of ≈3.42 ± 0.5 wt%, resulting in outstanding strength–ductility properties. In conclusion, these findings indicate that the proposed two–stage Q&P process, followed by bainitic transformation, significantly enhances the mechanical properties of carbon–silicon steels, making it a promising candidate for high–performance spring applications.

36 MATERIALS SCIENCE↗