NASA NTRS1995

Evaluation of the impact response of textile composites

An evaluation of the impact damage resistance and impact damage tolerance of stitched and unstitched uniweaves, 2-D braids, and 3-D weaves was conducted. Uniweave laminates were tested at four thicknesses to determine the sensitivity of the tests to this parameter. Several braid and weave parameters were also varied to establish their velocity (large mass) impacts and then loaded in tension or compression to measure residual strength. Experimental results indicate that stitching significantly improves the uniweaves' damage resistance. The 2-D braids and 3-D weaves offered less damage resistance than the stitched materials. Stitching also improved the compression after impact (CAI) and tension after impact (TAI) strengths of the uniweave materials.

Portanova, M. A.↗

NASA NTRS1995

Standard Methods for Unnotched Tension Testing of Textile Composites

An investigation was conducted by researchers at the Boeing Defense & Space Group to investigate the effects of specimen sizing on several braided textile materials. Test results from this and other test programs were compared in an effort to determine what effect, if any, specimen size has on elastic property measurements of unnotched tension test. In general, the unnotched tensile strength of 2-D braids was found to be insensitive to specimen width, length, or thickness effects. The results from this study suggest that standard testing methods used for tape materials may be sufficient for tension testing of textile composite materials. Specifically, the straight sided specimen geometry described in ASTM 3034, and used by Boeing, should provide acceptable results. Further experiments performed at Boeing and by other investigators on other textile architectures suggest similar results. Although specimen size studies were not conducted, failing stresses varied on the same order as those obtained with the 2-D materials. This suggests that the accuracy of the results were consistent with those obtained with the 2-D materials.

Portanova, M. A.↗

NASA NTRS1995

Standard methods for open hole tension testing of textile composites

Sizing effects have been investigated by comparing the open hole failure strengths of each of the four different braided architectures as a function of specimen thickness, hole diameter, and the ratio of specimen width to hole diameter. The data used to make these comparisons was primarily generated by Boeing. Direct comparisons of Boeing's results were made with experiments conducted at West Virginia University whenever possible. Indirect comparisons were made with test results for other 2-D braids and 3-D weaves tested by Boeing and Lockheed. In general, failure strength was found to decrease with increasing plate thickness, increase with decreasing hole size, and decreasing with decreasing width to diameter ratio. The interpretation of the sensitive to each of these geometrical parameters was complicated by scatter in the test data. For open hole tension testing of textile composites, the use of standard testing practices employed by industry, such as ASTM D5766 - Standard Test Method for Open Hole Tensile Strength of Polymer Matrix Composite Laminates should provide adequate results for material comparisons studies.

Portanova, M. A.↗

NASA NTRS1995

Standard methods for filled hole tension testing of textile composites

The effects of two test specimen geometry parameters, the specimen width and W/D ratio, on filled-hole tensile strength were determined for textile composite materials. Test data generated by Boeing and Lockheed on 2-D and 3-D braids, and 3-D weaves were used to make these evaluations. The investigation indicated that filled-hole tensile-strength showed little sensitivity to either parameter. Test specimen configurations used in open-hole tension tests, such as those suggested by ASTM D5766 - Standard Test Method for Open Hole Tensile Strength of Polymer Matrix Composite Laminates or those proposed by MIL-HDBK-17-lD should provide adequate results for material comparisons studies. Comparisons of the materials' open-hole and filled-hole tensile strengths indicated that the latter were generally lower than the former. The 3-D braids were the exception; their filled-hole strengths were unexpected larger than their open-hole strengths. However, these increases were small compared to the scatter in the data. Thus, filled hole tension may be a critical design consideration for textile composite materials.

Portanova, M. A.↗

NASA NTRS1995

Standard Methods for Bolt-Bearing Testing of Textile Composites

The response of three 2-D braided materials to bolt bearing loading was evaluated using data generated by Boeing Defense and Space Group in Philadelphia, PA. Three test methods, stabilized single shear, unstabilized single shear, and double shear, were compared. In general, these textile composites were found to be sensitive to bolt bearing test methods. The stabilized single shear method yielded higher strengths than the unstabilized single shear method in all cases. The double shear test method always produced the highest strengths but these results may be somewhat misleading. It is therefore recommended that standard material comparisons be made using the stabilized single shear test method. The effects of two geometric parameters, W/D and e/D, were also studied. An evaluation of the effect of the specimen width (W) to hole diameter (D) ratio concluded that bolt bearing responses were consistent with open hole tension results. A W/D ratio of 6 or greater should be maintained. The proximity of the hole to the specimen edge significantly affected strength. In all cases, strength was improved by increasing the ratio of the distance from the hole center to the specimen edge (e) to the hole diameter (D) above 2. An e/D ratio of 3 or greater is recommended.

Portanova, M. A.↗

NASA NTRS1992

Tension and compression fatigue response of unnotched 3D braided composites

The unnotched compression and tension fatigue response of a 3-D braided composite was measured. Both gross compressive stress and tensile stress were plotted against cycles to failure to evaluate the fatigue life of these materials. Damage initiation and growth was monitored visually and by tracking compliance change during cycle loading. The intent was to establish by what means the strength of a 3-D architecture will start to degrade, at what point will it degrade beyond an acceptable level, and how this material will typically fail.

Portanova, M. A.↗

NASA NTRS1991

Comparison of impact results for several polymeric composites over a wide range of low impact velocities

Static indentation, falling weight, and ballistic impact tests were conducted in clamped plates made of AS4/3501-6 and IM7/8551-7 prepreg tape. The transversely isotropic plates were nominally 7-mm thick. Pendulum and ballistic tests were also conducted on simply supported plates braided with Celion 12000 fibers and 3501-6 epoxy. The 20 degree braided plates were about 5-mm thick. The impactors had spherical or hemispherical shapes with a 12.7 mm diameter. Residual compression strength and damage size were measured. For a given kinetic energy, damage size was least for IM7/8551-7 and greatest for the braided material. Strengths varied inversely with damage size. For a given damage size, strength loss as a fraction of original strength was least for the braided material and greatest for AS4/3501-6 and IM7/8551-7. Strength loss for IM7/8551-7 and AS4/3501-6 was nearly equal. No significant differences were noticed between damage sizes and residual compression strengths for the static indentation, falling weight, and ballistic tests of AS4/3501-6 and IM7/8551-7. For the braided material, sizes of damage were significantly less and compression strengths were significantly more for the falling weight tests than for the ballistic tests.

Poe, C. C., Jr.↗

NASA NTRS1990

Open hole and post-impact compression fatigue of stitched and unstitched carbon/epoxy composites

The performance is studied of a stitched uniweave fabric composite and that of a toughened tape composite. The effects of stitching on compression fatigue life are addressed. Post impact compression fatigue and open hole fatigue tests were run on an AS4/3501-6 uniweave with stitching and a toughened IM7/8551-7 tape without stitching. Stitching was found to increase the thickness and consequently the weight of the composite material. The two materials were compared on an equal carbon content basis as well as on an equal weight basis. The excess thickness in the stitched uniweave composite was responsible for the lower fatigue life, on an equal carbon basis, compared to the toughened resin tape composite. Comparison of fatigue lives on an equal carbon content basis indicated that puncture or crimp type damage from stitching has very little effect on compression failure. Post impact fatigue test showed that although the damage area in the stitched uniweave composite was twice that of the toughened tape composite, the fatigue lives of the stitched composite were significantly longer than those of the toughened composite. Thus, it appears that the increase in thickness from stitching is much more of a penalty than crimped fibers or puncture type damage from stitching.

Portanova, M. A.↗

NASA NTRS1989

Strengths of balloon films with flaws and repairs

The effects of manufacture flaws and repairs in high altitude scientific balloons was examined. A right circular cylinder was used to induce a biaxial tension-tension stress field in the polyethlene film used to manufacture these balloons. A preliminary investigation of the effect that cylinder geometry has on stress rate as a function of inflation rate was conducted. The ultimate goal was to rank, by order of degrading effects, the flaws and repairs commonly found in current high altitude balloons.

Portanova, M. A.↗