Aluminum bonded SmCo5 magnets with enhanced mechanical strength

Despite their versatility and easy manufacturability, polymer-bonded magnets find limited application due to their limited mechanical properties and temperature resistance. In this study, we developed mechanically robust, aluminum-bonded SmCo5 magnets by utilizing a low-temperature, shear-assisted friction consolidation technique. Bonded magnets with varying magnetic phase content were fabricated at processing temperature of 500°C, and their microstructures, magnetic, mechanical, and electrical properties were systematically investigated. The resulting bonded-magnets showed effective consolidation with nanocrystalline microstructures. Magnetic properties were found to be tunable through variations in binder phase content, with coercivity reaching values up to 15.3 kOe (1217.5 kA/m) and maximum magnetic energy product up to 3.6 MGOe (28.7 kJ/m3), which are comparable to other bonded magnets. Electrical resistivities were lower than the polymer-bonded magnets, but comparable to the sintered ones. We observed an average flexural strength of 223 MPa for 60 vol.% SmCo5/Al sample, which is nearly two times higher than the reported values for sintered and bonded Sm-Co magnets. Our research demonstrated an effective approach to fabricate metal-bonded permanent magnets with superior magnetic and mechanical properties potentially applicable for high temperature applications.

Poudel Chhetri, Tej Bahadur↗

DOE OSTI2024

Crafting Multifunctional Materials with Tailored Mechanical and Magnetic Properties by Solid-State Non-equilibrium Processing

Aluminum matrix composites hold promise for creating lightweight structural components with multifunctional properties. Nonetheless, achieving desired magnetic or electrical characteristics without compromising their fundamental mechanical properties presents a significant challenge. Here, in this study, we explore mechanical stir-based extrusion as a solid-state metalworking technique to develop fine-grained microstructures and highly refined metallic composites. Our study focuses on creating a SmCo 5 -reinforced aluminum matrix composite using solid stir extrusion (SSE) and assessing its microstructure, mechanical, and magnetic properties through a comprehensive suite of characterization tools, including x-ray diffraction, electron microscopy, and magnetometry. Our findings reveal that incorporating a small amount (3.76 wt.%) of SmCo 5 phase in a non-heat-treatable, non-magnetic aluminum alloy via SSE yields a composite that exhibits good hard magnetic characteristics with a large coercivity (H ci = 13.5 kOe) and improved mechanical properties. This study underscores non-equilibrium processing via solid-state high-speed stirring as a compelling method for crafting multifunctional materials with tailored mechanical and magnetic properties.

36 MATERIALS SCIENCE↗