Anion binding agent lithium salts for battery electrolytes

A method for synthesizing a purified lithium (Li)+ anion binding agent (ABA-F)− salt and the corresponding Li+(ABA-F)− are disclosed. The method includes dissolving a boron-based acid in a polar solvent to form a solution. The solution is refluxed to form an anion binding agent. A stoichiometric amount of a small fluorinated salt, such as LiF, is added to the anion binding agent to form a mixture. The mixture is subsequently crystallized to obtain a substantially pure Li+(ABA-F)− salt. Example purified Li+(ABA-F)− salts include Ox-Li+(ABA-F), m-Li+(ABA-F), and BF3—Li+(ABA-F)−. These purified Li+(ABA-F)− salts provide the benefits of increased battery thermal safety without loss of electrochemical performance.

Orendorff, Christopher↗
DOE OSTI2021

Durable and Highly Selective Ion Transport of a Sulfonated Diels Alder Poly(phenylene) for Vanadium Redox Flow Batteries

In order to improve the durability and ion selectivity of a hydrocarbon membrane for vanadium redox flow batteries (VRFBs) a polymer was rationally designed with an external hydrophobic shell and internal hydrophilic core. The polymer was designed to prevent hydrophilic polymer chain aggregation by functionalizing the external polymer shell with hydrophobic side chains and attaching acid moieties onto the polymer backbone. The hydrophobic shell is the result of pentafluorobenzoyl group functionalization on the pendent aryl rings in a Diels Alder poly(phenylene) backbone. The internal polymer chain contains sulfonic acid moieties to impart hydrophilic character. The physical and electrochemical characteristics of the membrane were systematically studied and compared with widely used Nafion-212. The synthesized membranes were found to be superior to Nafion-212 not only in terms of lower vanadium ion permeability (4.25 x 10 -8 vs. Nafion-212: 6.0 x 10 -6 cm 2 min -1 ) but also in higher VRFB performance (EE = 89% and vs. Nafion-212: 85.5% at 40 mA/cm 2 ). The membrane also showed over three times higher capacity retention than Nafion-212 (0.075 % vs. 0.25 % capacity loss per cycle respectively) and excellent ex situ and in situ chemical stability.

25 ENERGY STORAGE↗