Pudasaini, U. — Page 2

DOE OSTI2022

Lower Temperature Annealing of Vapor Diffused Nb₃Sn for Accelerator Cavities

Nb₃Sn is a next-generation superconducting material for the accelerator cavities with higher critical temperature and superheating field, both twice compared to Nb. It promises superior performance and higher operating temperature than Nb, resulting in significant cost reduction. So far, the Sn vapor diffusion method is the most preferred and successful technique to coat niobium cavities with Nb₃Sn. Although several post-coating techniques (chemical, electrochemical, mechanical) have been explored to improve the surface quality of the coated surface, an effective process has yet to be found. Since there are only a few studies on the post-coating heat treatment at lower temperatures, we annealed Nb₃Sn-coated samples at 800 C - 1000 C to study the effect of heat treatments on surface properties, primarily aimed at removing surface Sn residues. This paper discusses the systematic surface analysis of coated samples after annealing at temperatures between 850 C and 950 C.

43 PARTICLE ACCELERATORS↗

DOE OSTI2022

Nb3Sn Coating of Twin Axis Cavity for SRF Applications

The twin axis cavity with two identical accelerating beams has been proposed for Energy recovery linac (ERL) applications. Nb3Sn is a superconducting material with a higher critical temperature and a higher critical field as compared to Nb, which promises a lower operating cost due to higher quality factors. Two niobium twin axis cavities fabricated at JLab and were proposed to be coated with Nb3Sn. Due to their more complex geometry, the typical coating process used for basic elliptical cavities needs to be improved to coat these cavities. This devel-opment advances the current coating system at JLab for coating complex cavities. Two twin axis cavities were coated recently for the first time. This contribution dis-cusses initial results from coating of twin axis cavities, RF testing and witness sample analysis with an overview of the current challenges towards high performance Nb3Sn coated twin axis cavities.

Tiskumara, J.↗

DOE OSTI2022

Nb$_3$Sn Superconducting Radiofrequency Cavities: a Maturing Technology for Particle Accelerators and Detectors

Nb3Sn superconducting radiofrequency (SRF) cavities have substantial potential for enabling new performance capabilities for particle accelerators for high energy physics (HEP), as well as for RF cavity-based detectors for dark matter, gravitational waves, and other quantum sensing applications. Outside of HEP, Nb3Sn SRF cavities can also benefit accelerators for nuclear physics, basic energy sciences, and the industry. In this contribution to Snowmass 2021, we overview the potential, status, and outlook of Nb3Sn SRF cavities.

43 PARTICLE ACCELERATORS↗

DOE OSTI2022

Managing Sn-Supply to Tune Surface Characteristics of Vapor-Diffusion Coating of Nb₃Sn

Nb₃Sn promises better RF performance (Q and E_{acc}) than niobium at any given temperature because of superior superconducting properties. Nb₃Sn-coated SRF cavities are now produced routinely by growing a few microns thick Nb₃Sn films inside Nb cavities via the tin vapor diffusion technique. Sn evaporation and consumption during the growth process notably affect the quality of the coating. Aiming at favorable surface characteristics that could enhance the RF performance, many coatings were produced by varying Sn sources and temperature profiles. Coupon samples were examined using different material characterization techniques, and a selected few sets of coating parameters were used to coat 1.3 GHz single-cell cavities for RF testing. The Sn supply’s careful tuning is essential to manage the microstructure, roughness, and overall surface characteristics of the coating. We summarize the material analysis of witness samples and discuss the performance of several Nb₃Sn-coated single-cell cavities linked to Sn-source characteristics and observed Sn consumption during the film growth process.

Pudasaini, U.↗

DOE OSTI2021

Managing Sn-supply to tune surface characteristics of vapor-diffusion coating of Nb3Sn

Nb₃Sn promises better RF performance (Q and E_{acc}) than niobium at any given temperature because of superior superconducting properties. Nb₃Sn-coated SRF cavities are now produced routinely by growing a few microns thick Nb₃Sn films inside Nb cavities via the tin vapor diffusion technique. Sn evaporation and consumption during the growth process notably affect the quality of the coating. Aiming at favorable surface characteristics that could enhance the RF performance, many coatings were produced by varying Sn sources and temperature profiles. Coupon samples were examined using different material characterization techniques, and a selected few sets of coating parameters were used to coat 1.3 GHz single-cell cavities for RF testing. The Sn supply’s careful tuning is essential to manage the microstructure, roughness, and overall surface characteristics of the coating. We summarize the material analysis of witness samples and discuss the performance of several Nb₃Sn-coated single-cell cavities linked to Sn-source characteristics and observed Sn consumption during the film growth process.

Pudasaini, U.↗

DOE OSTI2020

Nb 3 Sn multicell cavity coating system at Jefferson Lab

Superconducting radio frequency niobium cavities are the building blocks of modern accelerators for scientific applications. Lower surface resistance, higher fields, and high operating temperatures advance the reach of the future accelerators for scientific discovery as well as potentially enabling cost-effective industrial solutions. We describe the design and performance of an Nb 3 Sn coating system that converts the inner surface of niobium cavities to an Nb 3 Sn film. The niobium surface, heated by radiation from the niobium retort, is exposed to Sn and SnCl 2 vapor during the heat cycle, which results in about 2 μm Nb 3 Sn film on the niobium surface. Film composition and structure as well as radio frequency properties with 1-cell R&D cavities and 5-cell practical accelerator cavities are presented.

47 OTHER INSTRUMENTATION↗

DOE OSTI2020

Effect of layer thickness on structural, morphological and superconducting properties of Nb 3 Sn films fabricated by multilayer sequential sputtering

Superconducting Nb3Sn films can be synthesized by controlling atomic concentration of Sn. Multilayer sequential sputtering of Nb and Sn thin films followed by high temperature annealing is considered as a method to fabricate Nb3Sn films where Sn composition of deposited films can be controlled by controlling the thickness of alternating Nb and Sn layers. We report on the structural, morphological and superconducting properties of Nb3Sn films fabricated by multilayer sequential sputtering of Nb and Sn films on sapphire substrates with ex-situ annealing at 950 °C for 3 h. We have investigated the effect of Nb and Sn layer thickness on the properties of Nb3Sn films. The thicknesses of Nb and Sn layers were varied in two ways: (1) varied Nb:Sn thickness ratio (1:1, 2:1, 3:1, 4:1), and (2) varied layer thickness of both Nb and Sn layers, while keeping constant Nb:Sn thickness ratio of 2:1. The crystal structure, surface morphology, topography, and film composition were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and energy dispersive X-ray spectroscopy (EDS) respectively. The results showed Sn loss from the surface due to evaporation during annealing. Superconducting Nb3Sn films of critical temperature up to 17.93 K have been achieved.

Sayeed, M. N.↗