DOE OSTI2024

Understanding the influence of boron in additively manufactured GammaPrint®-700 CoNi-based superalloy

Boron is commonly added to superalloys in small amounts to enhance creep resistance, but can lead to cracking at high concentrations, especially during the additive manufacturing process. Two variants of CoNi-based GammaPrint®-700 superalloy with different B contents (0.08 at% vs 0.16 at%) were printed via laser powder bed fusion (LPBF) with the same printing parameters, with only the high B alloy exhibiting solidification cracking. Atom probe tomography (APT) revealed stronger segregation behaviors in the high B alloy compared to the low B alloy at both the inter-dendritic regions and grain boundaries (GBs). The segregation behavior at inter-dendritic regions was well captured with Scheil simulation and can correlate with the existing cracking susceptibility index (CSI) on cracking tendencies, although high angle GBs are where cracking occurs according to electron backscatter diffraction (EBSD) measurements. Additionally, the extent of GB segregation was compared between the high B and low B alloy. Higher B additions led to significantly more GB B segregation in the high B alloy compared to the low B alloy. Further, for the high B alloy, the cracked region of one GB exhibited higher levels of B compared to the uncracked region of the same GB. However, much higher B contents were also found in two other uncracked GBs in the high B alloy, which demonstrates that higher GB B concentrations are not fully responsible for the cracking. A much larger variance in GB B segregation content was found in the high B alloy compared to the low B alloy. These phenomena were explained with a solidification model with the GB segregation content expressed explicitly by a modified Langmuir-McLean equation. This model linked the GB segregation content with solidification undercooling, which can be used as quantitative cracking criteria for future builds.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Minor Elements and Solidification Cracking During Laser Powder-Bed Fusion of a High $\gamma ^{\prime }$ CoNi-Base Superalloy

Here, the cracking behavior of a high γ' volume fraction CoNi-base superalloy fabricated via laser powder bed fusion (LPBF) is studied in relation to the content of carbon and boron. Severe cracking occurred with the increase in boron content from 0.08 to 0.16 at. pct (0.015 to 0.029 wt pct), while compositions with 0.1 to 0.36 at. pct C (0.02 to 0.076 wt pct) and 0.08 at. pct B exhibited minimal cracking. Assessment of cracks in the high-boron composition shows a variation in crack density with printing parameters, and alignment of the cracks with the build direction. Scanning electron microscopy (SEM) of the crack surfaces shows evidence of a solidification cracking mode. Differential thermal analysis (DTA) reveals a decreased incipient melting temperature for the high-boron composition, and atom probe tomography (APT) is used to measure the enrichment at grain boundaries, revealing distinct boron segregation. Scheil-Gulliver solidification simulations for the different C and B levels are consistent with the incipient melting behavior observed with DTA. Evaluation of the solidification cracking susceptibility from the simulations allow for comparison of the CoNi alloy behavior to Ni-base superalloys studied for LPBF fabrication and displays how such metrics may aid in the design of new precipitation-strengthened superalloys for additive manufacturing (AM).

36 MATERIALS SCIENCE↗

DOE OSTI2022

Boundary characterization using 3D mapping of geometrically necessary dislocations in AM Ta microstructure

Additive manufacturing (AM) of high strength metallic materials produces microstructures and defects that deviate substantially from those created through conventional manufacturing methods. It has recently been demonstrated that with application of extreme energy densities, a high-temperature refractory metal, tantalum (Ta), can be printed to a fully dense state with exceptionally low porosity. Here we employ a combination of three-dimensional electron backscattered diffraction (EBSD) TriBeam technology and crystallographic geometrically necessary dislocation (GND) theory to characterize the microstructure and defect boundaries of this unusual AM product. Two-dimensional (2D) EBSD and these three-dimensional (3D) measurements indicate that the microstructure of AM Ta is highly oriented <111> along the build direction, yet at the same time contains large crystallographic orientation gradients that span mm’s across the build. Crystallographic GND density analysis of the 3D microstructure reveals that highly misoriented subboundaries exist within this strongly textured microstructure that have large dislocation densities of 1×10 16 m –2 , just as large as those comprising the high-angle grain boundaries (HAGBs) in the same material. The 3D crystallographic GND density mapping reveals these subboundaries are part of a complex, finely spaced network that extends throughout the entire microstructure. Here, the orientation of these boundaries can be related to the scan strategy used during printing. TEM measurements corroborate an extremely high dislocation density at the microscale and indicate a cell-like dislocation network structure existing in the AM Ta at the sub-μm scale.

36 MATERIALS SCIENCE↗

DOE OSTI2020

A defect-resistant Co–Ni superalloy for 3D printing

Abstract Additive manufacturing promises a major transformation of the production of high economic value metallic materials, enabling innovative, geometrically complex designs with minimal material waste. The overarching challenge is to design alloys that are compatible with the unique additive processing conditions while maintaining material properties sufficient for the challenging environments encountered in energy, space, and nuclear applications. Here we describe a class of high strength, defect-resistant 3D printable superalloys containing approximately equal parts of Co and Ni along with Al, Cr, Ta and W that possess strengths in excess of 1.1 GPa in as-printed and post-processed forms and tensile ductilities of greater than 13% at room temperature. These alloys are amenable to crack-free 3D printing via electron beam melting (EBM) with preheat as well as selective laser melting (SLM) with limited preheat. Alloy design principles are described along with the structure and properties of EBM and SLM CoNi-base materials.

36 MATERIALS SCIENCE↗