Shelf-life of ball-milled catalyst inks for the fabrication of fuel cell electrodes
A major factor driving fuel cell costs is the quantity of precious metal required. Therefore, it is important to understand a timeframe where inks can be reused. Here, in this work, we explore differences between a freshly prepared catalyst ink and one that has been stored for over a year – comparing ink properties, cathode catalyst layer microstructure, and their respective fuel cell performance. Ink studies revealed smaller agglomerate sizes and a decrease in shear viscosity for the aged ink. Longer storage time also results in fewer cracks and a more uniform ionomer distribution, as evidenced by microscopy characterization of rod-coated electrodes. Lastly, polarization curves show improved performance at higher current densities for the electrode prepared from the aged ink. We rationalize such effect in terms of enhanced ionomer adsorption onto the catalyst over time.
Characterization of Porous Transport Layers Towards the Development of Efficient Proton Exchange Membrane Water Electrolysis
The current goals for implementing the hydrogen economy have highlighted a need to further optimize water-splitting technologies for clean hydrogen production. Proton exchange membrane water electrolysis (PEMWE) is a leading technology, but further optimizations of anode materials including the porous transport layer (PTL) and the adjacent catalyst layer (CL) are required to increase overall cell performance and reduce cost. This literature review describes advances in PTL development and characterization, highlighting early PTL characterization work and most common methods including capillary flow porometry and mercury intrusion porometry, optical imaging, neutron and x-ray radiography, and x-ray computed tomography. The article also discusses PTL protective coatings and their characterizations, focusing on platinum group metal (PGM)-based coatings, alternative non-PGM-based coatings, post-treated PTLs, and investigations into thin PGM-based coatings. Furthermore, it highlights the integration of the PTL and the adjacent CL along with associated characterization challenges. Lastly, this review discusses future developments in the characterization needed to improve PEMWE's performance and long-term durability are discussed.
X-ray Photoelectron Spectroscopy Analysis of Nafion-Containing Samples: Pitfalls, Protocols, and Perceptions of Physicochemical Properties
X-ray photoelectron spectroscopy (XPS) is one of the most common techniques used to analyze the surface composition of catalysts and support materials used in polymer electrolyte membrane (PEM) fuel cells and electrolyzers, providing important insights for further improvement of their properties. Characterization of catalyst layers (CLs) is more challenging, which can be at least partially attributed to the instability of ionomer materials such as Nafion during measurements. This work explores the stability of Nafion during XPS measurements, illuminating and addressing Nafion degradation concerns. The extent of Nafion damage as a function of XPS instrumentation, measurement conditions, and sample properties was evaluated across multiple instruments. Results revealed that significant Nafion damage to the ion-conducting sulfonic acid species (>50% loss in sulfur signal) may occur in a relatively short time frame (tens of minutes) depending on the exact nature of the sample and XPS instrument. This motivated the development and validation of a multipoint XPS data acquisition protocol that minimizes Nafion damage, resulting in reliable data acquisition by avoiding significant artifacts from Nafion instability. The developed protocol was then used to analyze both thin film ionomer samples and Pt/C-based CLs. Comparison of PEM fuel cell CLs to Nafion thin films revealed several changes in Nafion spectral features attributed to charge transfer due to interaction with conductive catalyst and support species. This study provides a method to reliably characterize ionomer-containing samples, facilitating fundamental studies of the catalyst-ionomer interface and more applied investigations of structure-processing-performance correlations in PEM fuel cell and electrolyzer CLs.
The effect of ink ball milling time on interparticle interactions and ink microstructure and their influence on crack formation in rod-coated catalyst layers
This work investigates the influence of ballmilling (sometimes also referred to as jar roller milling) time on cathode catalyst layer (CL) inks and electrode properties using formulations and coating methods relevant for industrial manufacturing. Four CL inks with the same composition were milled for 24, 48, 72, or 96 h. Rheological investigation of these inks showed a reduction of elastic moduli and steady-shear viscosity with continuous ink milling, which is correlated to a decrease in particle-particle interactions as well as formation of smaller agglomerates. Optical microscopy (OM) analysis of the fabricated electrodes revealed a trend in surface crack formation; formulations milled for 24 h contained the lowest average surface crack area percentages of 0.370% at heavy-duty loadings of ~0.300 mg Pt cm -2 , compared to 2.418% for the ink milled for 96 h. Further characterization of the CL through transmission electron microscopy (TEM) imaging showed a decrease in the mean agglomerate and pore size with milling time. Furthermore, these smaller electrode features were consistent with reduced fracture resistance and, hence, development of larger stresses during drying. Our results highlight the need to consider ink processing as an important component in defect-free CL manufacturing.
Aging gracefully? Investigating iridium oxide ink's impact on microstructure, catalyst/ionomer interface, and PEMWE performance
Here, in this study, we conducted a thorough investigation of the impact of aging iridium oxide (IrO 2 ) perfluorosulfonic acid ionomer ink for up to 14 days on the properties of the ink and the resulting catalyst layers. We examined ink properties, such as zeta potential, dynamic light scattering (DLS), density, surface tension, and rheology, as functions of ink aging time. To evaluate the microstructure and catalyst/ionomer interface, we employed transmission electron microscopy (TEM), X-ray scattering, and X-ray photoelectron spectroscopy (XPS) techniques. Furthermore, we assessed the effect of ink aging on the performance of proton exchange membrane water electrolyzers (PEMWEs). Our findings reveal that most ink properties remain stable for 14 days. The variations in PEMWE cell performance are minimal, and no clear trend is observed in relation to ink aging time. This study demonstrates that the effects of aging the inks for 14 days on ink properties, catalyst layer structure, catalyst/ionomer interface, and PEMWE performance are negligible, indicating a substantial time window after ink preparation without any significant changes in its properties. These insights provide crucial guidance for the commercial production and coating processes of ink, which is necessary for scaling up PEM technologies to meet future demand.
Revealing in-plane movement of platinum in polymer electrolyte fuel cells after heavy-duty vehicle lifetime
Fuel cell heavy-duty vehicles (HDVs) require increased durability of oxygen-reduction-reaction electrocatalysts, making knowledge of realistic degradation mechanisms critical. Here identical-location micro-X-ray fluorescence spectroscopy was performed on membrane electrode assemblies. The results exposed heavy in-plane movement of electrocatalyst after HDV lifetime, suggesting that electrochemical Ostwald ripening may not be a local effect. Development of local loading hotspots and preferential movement of electrocatalyst away from cathode catalyst layer cracks was observed. The heterogeneous degradation exhibited by a modified cathode gas diffusion layer membrane electrode assembly after HDV lifetime was successfully quantified by the identical-location approach. Further synchrotron micro-X-ray diffraction and micro-X-ray fluorescence experiments were performed to obtain the currently unknown correlation between electrocatalyst nanoparticle size increase and loading change. A direct correlation was discovered which developed only after HDV lifetime. Finally, the work provides a route to engineer immediate system-level mitigation strategies and to develop structured cathode catalyst layers with durable electrocatalysts.
Degradation Effects at the Porous Transport Layer/Catalyst Layer Interface in Polymer Electrolyte Membrane Water Electrolyzer
The porous transport layer (PTL)/catalyst layer (CL) interface plays a crucial role in the achievement of high performance and efficiency in polymer electrolyte membrane water electrolyzers (PEMWEs). This study investigated the effects of the PTL/CL interface on the degradation of membrane electrode assemblies (MEAs) during a 4000 h test, comparing the MEAs assembled with uncoated and Ir-coated Ti PTLs. Our results show that compared to an uncoated PTL/CL interface, an optimized interface formed when using a platinum group metal (PGM) coating, i.e., an iridium layer at the PTL/CL interface, and reduced the degradation of the MEA. The agglomeration and formation of voids and cracks could be found for both MEAs after the long-term test, but the incorporation of an Ir coating on the PTL did not affect the morphology change or oxidation of IrO x in the catalyst layer. In addition, our studies suggest that the ionomer loss and restructuring of the anodic MEA can also be reduced by Ir coating of the PTL/CL interface. Optimization of the PTL/CL interface improves the performance and durability of a PEMWE.
Multi-technique characterization of spray coated and roll-to-roll coated gas diffusion fuel cell electrodes
Here this work reports the characterization of catalyst layer (CL) structure and composition for a set of gas-diffusion electrodes (GDEs) fabricated by different coating methods with the goal of developing a better understanding of CL processing-structure-property-performance relationships. The CL coating techniques used in this study were ultrasonic spray coating, and two roll-to-roll (R2R) methods - gravure and slot die. Scanning transmission electron microscopy (STEM) coupled with X-ray energy dispersive spectroscopy (EDS) analysis of GDE cross-sections provided bulk information, while scanning electron microscopy (SEM) with EDS and X-ray photoelectron spectroscopy (XPS) were used to investigate the near surface and surface composition of the CLs that will be in direct contact with the membrane once the membrane electrode assembly (MEA) is constructed. This study demonstrates that common quantification parameters, namely the F:Pt ratio extracted from cross-sectional STEM-EDS maps and top-down CL measurements with SEM and XPS, along with roughness parameters quantified from SEM micrographs are useful parameters in explaining and potentially predicting performance trends. Additionally, it highlights the importance of understanding key CL surface properties for advancing the manufacturability of high-performance components for polymer electrolyte membrane (PEM) technologies.
Thermal Decomposition of Magnesium Borohydride: New Insights from Synchrotron X-ray Scattering
Not Available
Low-Temperature Dehydrogenation of Vapor-Deposited Magnesium Borohydrides Imaged Using Identical Location Microscopy
Not Available
Optimization of Extended-Surface PtNi Nanowire Oxygen Reduction Electrocatalysts Produced via Atomic Layer Deposition
Polymer electrolyte membrane fuel cells (PEMFCs) produce electricity with only heat and water as byproducts, but sluggish kinetics of the oxygen reduction reaction (ORR) at the cathode and durability limitations restrict widespread commercialization, motivating the development of advanced catalysts. In this research, extended-surface platinum nickel (PtNi) nanowires (NWs) synthesized using the scalable atomic layer deposition (ALD) technique are investigated with the goal of exploring the durability benefits of high-aspect-ratio electrocatalysts and the tunability of beneficial kinetic properties. The surface and bulk composition and the structure of the PtNi NWs were investigated as a function of a series of postsynthesis modifications. The results from a combination of electron microscopy and X-ray spectroscopy characterization techniques were correlated to electrochemical performance to gain a comprehensive understanding of the structure-property-performance relationships. The robust structure of the ALD-derived NWs enabled additional postsynthesis optimization steps, which were not possible with previous-generation materials synthesized via spontaneous galvanic displacement, resulting in a catalyst with beneficial properties for catalyst kinetics as well as improved durability. Our study demonstrates potential pathways toward further improving the performance of this class of materials through optimization of bulk and surface properties of the catalyst.
(Invited) Linking Ionomer/Electrocatalyst Interactions to Membrane Electrode Assembly Performance and Durability in Proton Exchange Membrane Fuel Cells
Explore the source record for details and available documents.
Influence of Ink Formulation and Drying Conditions on Ionomer Distribution in High-Performance Roll-to-Roll-Coated Gas-Diffusion Electrodes
To enable mass production of fuel cell membrane electrode assemblies (MEAs) catalyst layers production will require continuous roll-to-roll (R2R) coating processes. Gas diffusion electrodes (GDEs) are advantageous for mass production because the catalyst layer can be directely coated on the microporous layer of the gas diffusion media without the need for a decal-transfer process. It is known that the water-to-alcohol ratio in the catalyst ink influences the interactions of the ionomer with the catalyst leading to different distributions of ionomer in spray-coated catalyst layers. It is also known that during drying of colloidal mixtures, like fuel cell inks, factors such as drying rate, particle size, and agglomeration influence how the materials distribute themselves throughout the thickness of the dired film. Thus far there have only been limited studies to understand how process conditions such as ink formulation and drying temperature influence the distribution of ionomer and catalyst coated using scalable methods. This understanding is especially important for GDEs since it is known that having a sufficient amount of ionomer at the catalyst layer-membrane interface is critical for high performance. In this study we have focused on determining how the ratio of water to 1-propanol in the catalyst ink ink and drying temperature influence the distribution of ionomer throughout the thickness of the catalyst layer. Using a combination of Kelvin probe and x-ray photoelectron spectroscopy we show that an ionomer-rich surface is promoted by a higher drying rate and a water-rich catalyst ink. In contrast, a 1-propanol catalyst ink leads to a lower concentration of ionomer on the top surface. Using x-ray computed tomography, we are able to characterize the ionomer distribution throughout the thickness of the layer. We find that, in addition to promoting an ionomer-rich top surface, water-rich inks lead to a more homogenous distribution of ionomer, whereas a 1-propanol-rich ink leads to a more irregular distribution. It is found that MEA performance is improved by selecting conditions and ink formulations that promote ionomer enrichment at the top surface to facilitate a good interface with the membrane. MEAs prepared with a 75 wt% water catalyst ink with a 0.9 I/C have equivalent performance to spray-coated GDEs. Critically, these R2R-coated GDEs do not need an additional ionomer overlayer like the spray-coated GDEs do, reducing the number of processing steps in a manufacturing setting. This work shows that with the appropriate selection of materials, ink formulation, and processing conditions gas-diffusion electrodes are a viable pathway for fuel cell manufacturing.
Development of high-performance roll-to-roll-coated gas-diffusion-electrode-based fuel cells
This study focuses on determining fabrication conditions to create high-performance roll-to-roll-coated (R2R-coated) gas-diffusion electrodes (GDEs) for proton-exchange-membrane fuel cells (PEMFCs). Here, we examine how process conditions influence the distribution of ionomer in the electrode, which is shown to be critical for high performance. Using a combination of Kelvin probe, X-ray photoelectron spectroscopy, and nano-scale X-ray computed tomography we show that formation of an ionomer-rich surface is promoted by using a higher drying rate. We show that R2R-coated GDEs have higher surface ionomer concentration than spray-coated GDEs, which enables these R2R-coated GDEs to not need an additional ionomer overlayer, as is typically the case for spray-coated GDEs. This will reduce the number of processing steps and lower material costs in a manufacturing setting. This work shows that with the appropriate selection of materials, ink formulation, and processing conditions, direct-coated GDEs are a viable pathway for fuel cell manufacturing.
Toward Optimizing Electrospun Nanofiber Fuel Cell Catalyst Layers: Microstructure and Pt Accessibility
This work investigates how local ionomer/platinum (Pt) interactions and ionomer distribution in electrospun Pt/Vulcan nanofiber electrodes impact ionomer coverage, proton accessibility, and oxygen reduction reaction (ORR) performance in proton-exchange membrane fuel cells. Insights from various in situ electrochemical diagnostics were utilized in conjunction with ex situ microscopic characterization to understand how the electrode microstructure—both at the aggregate level and near the ionomer/platinum interface—is affected by electrospinning in comparison to ultrasonic spraying. The effect of the carrier polymer poly(acrylic acid) (PAA) concentration from 5–20 wt % (with respect to total ink solids) on the resulting nanofiber morphology is discussed. Electron microscopy observations and CO displacement measurements indicated that Pt/Vulcan nanofibers prepared with a higher PAA concentration (15 wt %) were conformally coated with a film of ionomer on the exterior of the fiber, which resulted in an overall lower ionomer coverage on both Pt and carbon throughout the fiber diameter. In contrast, 10 wt % PAA leads to a uniform intrafiber distribution of the ionomer within the fibers, increasing the overall ionomer coverage and proton accessibility under both wet and dry conditions. These differences in the local ionomer coverage on Pt between 10 and 15 wt % PAA were also attributed to differences in the adsorption/interaction affinities between PAA and the ionomer onto the catalyst surface in the ink using zeta potential measurements. Additional fuel cell electrochemical tests on the electrospun electrodes show improvements in ORR kinetics and high-current-density H 2 /air performance compared to the ultrasonically sprayed electrodes.
Visualization, understanding, and mitigation of process-induced-membrane irregularities in gas diffusion electrode-based polymer electrolyte membrane fuel cells
Polymer electrolyte membrane fuel cells (PEMFC) show substantial promise for their application in electric vehicles. For large-scale manufacturing of PEMFCs, roll-to-roll coated gas-diffusion-electrodes (GDE) offer certain advantages over other production pathways. Procedures including hot pressing and coating an ionomer overlayer may be necessary for this manufacturing pathway to enable a suitable catalyst layer/membrane interface. The same procedures may potentially introduce membrane irregularities, especially when thin membranes are used. Limited understanding exists regarding if and to what extent such irregularities impact PEMFC performance and lifetime, and therefore be considered defects. In this study, NREL's customized fuel cell hardware that enables quasi in-situ infrared (IR) thermography studies was utilized to visualize spatial hydrogen crossover and identify membrane irregularities that originated from the GDE-based MEA fabrication process. The structure of these membrane irregularities was investigated by scanning electron microscopy (SEM) and its impact on initial H2/air performance was determined. Accelerated stress testing (AST) revealed that these irregularities develop into failure point locations. These results were validated across many MEAs with identified process-induced membrane irregularities. By selecting specific gas diffusion media properties and by fine tuning the MEA hot pressing parameters, the formation of such membrane irregularities was mitigated.