Abstract One key barrier to using lithium‐metal anode batteries is that metal dendrites can penetrate solid electrolytes, causing short‐circuits and battery failures. It is established that this failure is likely caused by crack propagation due to electrodeposition‐induced stresses from lithium metal. This study explores ways to harness these electrochemical‐mechanical couplings to control dendrite growth and improve battery reliability using a phase‐field model and targeted fracture experiments. The results show that dendrite growth can be effectively mitigated by applying mechanical stresses or tailoring the material's fracture toughness. This study also outlines the requirements for compressive stress to halt or deflect dendrites as a function of the overpotential and discusses the role of microstructure in this process.

Monismith, Scott↗

NASA NTRS1999

Ultrasonic Nondestructive Characterization of Adhesive Bonds

Adhesives and adhesive joints are widely used in various industrial applications to reduce weight and costs, and to increase reliability. For example, advances in aerospace technology have been made possible, in part, through the use of lightweight materials and weight-saving structural designs. Joints, in particular, have been and continue to be areas in which weight can be trimmed from an airframe through the use of novel attachment techniques. In order to save weight over traditional riveted designs, to avoid the introduction of stress concentrations associated with rivet holes, and to take full advantage of advanced composite materials, engineers and designers have been specifying an ever-increasing number of adhesively bonded joints for use on airframes. Nondestructive characterization for quality control and remaining life prediction has been a key enabling technology for the effective use of adhesive joints. Conventional linear ultrasonic techniques generally can only detect flaws (delamination, cracks, voids, etc) in the joint assembly. However, more important to structural reliability is the bond strength. Although strength, in principle, cannot be measured nondestructively, a slight change in material nonlinearity may indicate the onset of failure. Furthermore, microstructural variations due to aging or under-curing may also cause changes in the third order elastic constants, which are related to the ultrasonic nonlinear parameter of the polymer adhesive. It is therefore reasonable to anticipate a correlation between changes in the ultrasonic nonlinear acoustic parameter and the remaining bond strength. It has been observed that higher harmonics of the fundamental frequency are generated when an ultrasonic wave passes through a nonlinear material. It seems that such nonlinearity can be effectively used to characterize bond strength. Several theories have been developed to model this nonlinear effect. Based on a microscopic description of the nonlinear interface binding force, a quantitative method was presented. Recently, a comparison between the experimental and simulated results based on a similar theoretical model was presented. A through-transmission setup for water immersion mode-converted shear waves was used to analyze the ultrasonic nonlinear parameter of an adhesive bond. In addition, ultrasonic guided waves have been used to analyze adhesive or diffusion bonded joints. In this paper, the ultrasonic nonlinear parameter is used to characterize the curing state of a polymer/aluminum adhesive joint. Ultrasonic through-transmission tests were conducted on samples cured under various conditions. The magnitude of the second order harmonic was measured and the corresponding ultrasonic nonlinear parameter was evaluated. A fairly good correlation between the curing condition and the nonlinear parameter is observed. The results show that the nonlinear parameter might be used as a good indicator of the cure state for adhesive joints.

Qu, Jianmin↗

NASA NTRS1997

Ultrasonic Nondestructive Characterization of Adhesive Bonds

Qualitative measurements of adhesion or binding forces can be accomplished, for example, by using the reflection coefficient of an ultrasound or by using thermal waves (Light and Kwun, 1989, Achenbach and Parikh, 1991, and Bostrom and wickham, 1991). However, a quantitative determination of binding forces is rather difficult. It has been observed that higher harmonics of the fundamental frequency are generated when an ultrasound passes through a nonlinear material. It seems that such non-linearity can be effectively used to characterize the bond strength. Several theories have been developed to model this nonlinear effect (Adler and Nagy, 1991; Achenbach and Parikh, 1991; Parikh and Achenbach, 1992; and Hirose and Kitahara, 1992; Anastasi and Roberts, 1992). Based on a microscopic description of the nonlinear interface binding force, a quantitative method was presented by Pangraz and Arnold (1994). Recently, Tang, Cheng and Achenbach (1997) made a comparison between the experimental and simulated results based on this theoretical model. A water immersion mode-converted shear wave through-transmission setup was used by Berndt and Green (1997) to analyze the nonlinear acoustic behavior of the adhesive bond. In this project, the nonlinear responses of an adhesive joint was investigated through transmission tests of ultrasonic wave and analyzed by the finite element simulations. The higher order harmonics were obtained in the tests. It is found that the amplitude of higher harmonics increases as the aging increases, especially the 3dorder harmonics. Results from the numerical simulation show that the material nonlinearity does indeed generate higher order harmonics. In particular, the elastic-perfect plastic behavior generates significant 3rd and 5th order harmonics.

Qu, Jianmin↗

NASA NTRS1989

Reciprocal relations for transmission coefficients - Theory and application

The authors present a rigorous proof of certain intuitively plausible reciprocal relations for time harmonic plane-wave transmission and reflection at the interface between a fluid and an anisotropic elastic solid. Precise forms of the reciprocity relations for the transmission coefficients and for the transmitted energy fluxes are derived, based on the reciprocity theorem of elastodynamics. It is shown that the reciprocity relations can be used in conjunction with measured values of peak amplitudes for transmission through a slab of the solid (water-solid-water) to obtain the water-solid coefficients. Experiments were performed for a slab of a unidirectional fiber-reinforced composite. Good agreement of the experimentally measured transmission coefficients with theoretical values was obtained.