Effects of elevated temperature exposure on the residual stress state and microstructure of PVD Cr coatings on SiC investigated via in situ X-ray diffraction and transmission electron microscopy
Pure Cr coatings are being considered as corrosion-resistant layers for SiC-SiC f composite fuel cladding in light water reactors. The residual stress state and interdiffusion behavior of Cr coatings deposited on SiC substrates using bipolar high-power impulse magnetron sputtering (B-HiPIMS) and direct current impulse magnetron sputtering (DCMS) were studied using in situ X-ray diffraction experiments at 300 °C, 700 °C, and 1200 °C. After elevated temperature exposure, evolution of the coating microstructure and coating/substrate interdiffusion was characterized by transmission electron microscopy. The compressive residual stress of the dense B-HiPIMS coating at room temperature was gradually relieved at 300 °C, while the stress transitioned to a tensile state at 700 °C. Grain growth of the Cr coating and a Cr–SiC interdiffusion layer consisting of newly formed Cr–C and Cr–Si phases were observed in the B-HiPIMS coating after exposure at 700 °C. The phases in the interdiffusion layer were identified to be Cr 7 C 3 , Cr 3 Si, and Cr 5 Si 3 C x experimentally and by thermodynamic predictions. For the DCMS coating, however, changes in residual stress and microstructure at the elevated temperatures were limited by the inherent porosity and inhomogeneous structure of the as-deposited coating. At 1200 °C, both coating types interacted rapidly with the underlying SiC substrate in the early stages of the experiment. The results from this study suggest that the characteristics of the Cr coatings do not significantly change at the reactor operating temperature of 300 °C, while changes in microstructure and stress state are expected in off-normal conditions of 700 °C and 1200 °C. Finally the results from this study suggest the B-HiPIMS coating is best-suited as a protective coating for SiC fuel cladding.
36 MATERIALS SCIENCE↗
Microstructural and nanomechanical studies of PVD Cr coatings on SiC for LWR fuel cladding applications
The microstructure and nanomechanical properties of pure Cr coatings deposited on SiC with various physical vapor deposition (PVD) methods have been investigated for the mitigation of hydrothermal corrosion of SiC-SiC f (SiC fiber-reinforced SiC matrix) composite fuel cladding in light water reactors (LWR). Cr coatings (4–7 μm thick) were deposited on unbiased SiC substrates using six variants of magnetron sputtering processes: (i) standard (S-DCMS), (ii) pulsed (P-DCMS), (iii) ion-assisted (I-DCMS), and (iv) pulsed ion-assisted direct current magnetron sputtering (PI-DCMS), (v) high-power impulse magnetron sputtering (HiPIMS), and (vi) bipolar HiPIMS (B-HiPIMS). Microstructural characterization and nanoindentation testing were used to evaluate effects of deposition technique on coating microstructure and nanomechanical properties. The application of positive reverse pulses to the sputter target induced coarsening of the columnar grain structure, while ion bombardment of substrates during deposition promoted densification of the coating microstructure. Both effects are exemplified in B-HiPIMS deposition, resulting in a high-density microstructure with compressive residual stress. Material pile-up around nano-indents and plastic work during nanoindentation were analyzed to understand deformation behavior of the coatings. Finally, the results suggest the B-HiPIMS process to be among the promising methods for the deposition of Cr coatings on SiC-SiC f for LWR cladding application.
36 MATERIALS SCIENCE↗
Experimental evaluation of direct current magnetron sputtered and high-power impulse magnetron sputtered Cr coatings on SiC for light water reactor applications
Two types of physical vapor deposition Cr coatings were deposited on chemical vapor deposited SiC coupons using conventional direct current magnetron sputtering (DCMS) and high-power impulse magnetron sputtering (HiPIMS) to mitigate the corrosion of SiC, an advanced fuel and structural material in light water nuclear reactor cores. Coating microstructure was characterized using scanning electron microscopy and scanning transmission election microscopy. X-ray diffraction analysis was conducted for phase identification and qualitative analysis of residual stresses. The mechanical integrity of the coatings was evaluated using scratch testing, micro-indentation, and nano-indentation tests. Additionally, the microstructure of the DCMS coating consisted of fine columnar grains with nanoscale intercolumnar channels, while the HiPIMS microstructure was denser and free of any columnar defects. The DCMS coating showed a small tensile residual stress, while the HiPIMS coating was under compressive stress. Both types of coatings showed good mechanical integrity in terms of ductility and adhesion to the substrate. Corrosion performance of the coatings was assessed with a 30-day high temperature water autoclave test. Both types of coatings formed a protective Cr 2 O 3 surface layer 20-30 nm thick during the autoclave test. In the DCMS coating, the columnar defects provided permeation pathways for water penetration resulting in oxide formation in the intercolumnar regions in the interior of the coating. Overall, both types of Cr coatings offer promise for the mitigation of hydrothermal corrosion of SiC in light water reactor operating environments.
36 MATERIALS SCIENCE↗