Radzanowski, Anne N. | Search NASA

DOE OSTI2024

Modulating the Contact Angle between Nonpolar Polymers and SiO 2 Nanoparticles

Polymer–nanoparticle interactions play an important role in determining the morphology and properties of polymer nanocomposites and controlling the polymeric reactions involving heterogeneous catalysts. Here, in this study, we modulate the interactions between nonpolar polymers and nanoparticles by modifying the nanoparticle surface chemistry and quantify the interaction strength through direct contact angle measurements. We investigate the interactions of three nonpolar polymers, polystyrene, polyethylene, and polycyclooctene, with silica nanoparticles whose surface chemistry has been modified by atomic layer deposition of titania and calcium carbonate and by alkyl silanization. Significant differences in polymer–nanoparticle interactions are observed, which can be attributed to differences in the polarizability of the polymers and oxide surface composition. Compared to fully hydrogenated polycyclooctene, polycyclooctene is shown to have stronger interactions with most metal oxides; however, this trend is reversed following alkyl silanization of the silica nanoparticles, which makes the surface of the particles less polar. These differences in interactions can be leveraged to make polymer nanocomposites with unique properties and enable the selective conversion of polymers without the need for separations.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Effects of the Hydrophobic Block Length Ratio of Poly(vinylbenzyl N -methylpiperidinium carbonate)- b -polyethylene- b -poly(vinylbenzyl N -methylpiperidinium carbonate) Block Copolymers for Anion Exchange Membrane Electrolysis

Electrolysis of water to produce hydrogen from renewable electricity is an extremely attractive strategy to reduce energy dependence on fossil fuels. Development of membrane and ionomer materials that maintain high performance with long lifetimes is needed. We developed and investigated the performance and durability of a series of polyethylene-based ABA triblock copolymer anion exchange ionomer and membrane (AEI, AEM) materials for anion exchange membrane water electrolysis. Poly(vinylbenzyl N-methylpiperidinium carbonate)-b-polyethylene-b-poly(vinylbenzyl N-methylpiperidinium carbonate) was synthesized with different hydrophobic/hydrophilic block ratios (1.02:1, 2.58:1, and 4.46:1) resulting in a range of ion exchange capacities (1.1–1.8 meq g –1 ) and water swelling (23–154%) characteristics. All AEMs showed full anionic dissociation, as evidenced by linear Arrhenius correlations, and excellent carbonate conductivity of 8–94 mS cm –1 at 50 °C. Hydrophilic phase separation may offer superior chemical durability by only wetting the ion-conducting region of the polymer and avoiding attack at the nonwetted backbone. We evaluated the performance and durability of these AEMs as a function of hydrophobic polyethylene (PE) content. The AEM containing the least amount of PE displayed the highest performance of 1 A cm –2 at 2.3 V but degraded at 40 mV h –1 before catastrophically failing after <3 h at 0.5 A cm –2 . With greater PE-containing AEMs, the degradation rate was reduced by 3 orders of magnitude with only a 0.2 V increase in voltage. Constant current electrolysis for 50 h resulted in a voltage change of 0.3 mV h –1 in a single-cell water electrolyzer and 1 M potassium carbonate. In a 600 h test, the voltage change in the final 200 h was impressively low for an experimental film, 58 μV h –1 . Postmortem analysis indicated that the membrane did not thin and that water becomes more tightly hydrogen-bound in the polymer after electrolysis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗