DOE OSTI2025

Electrical and structural characterization of in situ MOCVD Al2O3/β-Ga2O3 and Al2O3/β-(AlxGa1−x)2O3 MOSCAPs

This study investigates the electrical and structural properties of metal–oxide–semiconductor capacitors (MOSCAPs) with in situ metal-organic chemical vapor deposition-grown Al2O3 dielectrics deposited at varying temperatures on (010) β-Ga2O3 and β-(AlxGa1−x)2O3 films with different Al compositions. The Al2O3/β-Ga2O3 MOSCAPs exhibited a strong dependence of electrical properties on Al2O3 deposition temperature. At 900 °C, reduced voltage hysteresis (∼0.3 V) with improved reverse breakdown voltage (74.5 V) was observed, corresponding to breakdown fields of 5.01 MV/cm in Al2O3 and 4.11 MV/cm in β-Ga2O3 under reverse bias. In contrast, 650 °C deposition temperature resulted in higher voltage hysteresis (∼3.44 V) and lower reverse breakdown voltage (38.8 V) with breakdown fields of 3.69 and 2.87 MV/cm in Al2O3 and β-Ga2O3, respectively, but exhibited impressive forward breakdown field, increasing from 5.62 MV/cm at 900 °C to 7.25 MV/cm at 650 °C. High-resolution scanning transmission electron microscopy (STEM) revealed improved crystallinity and sharper interfaces at 900 °C, contributing to enhanced reverse breakdown performance. For Al2O3/β-(AlxGa1−x)2O3 MOSCAPs, increasing Al composition (x) from 5.5% to 9.2% reduced net carrier concentration and improved reverse breakdown field contributions from 2.55 to 2.90 MV/cm in β-(AlxGa1−x)2O3 and 2.41 to 3.13 MV/cm in Al2O3. The electric field in Al2O3 dielectric under forward bias breakdown also improved from 5.0 to 5.4 MV/cm as Al composition increased from 5.5% to 9.2%. The STEM imaging confirmed the compositional homogeneity and excellent stoichiometry of both Al2O3 and β-(AlxGa1−x)2O3 layers. These findings demonstrate the robust electrical performance, high breakdown fields, and excellent structural quality of Al2O3/β-Ga2O3 and Al2O3/β-(AlxGa1−x)2O3 MOSCAPs, highlighting their potential for high-power electronic applications.

Bhuiyan, A. F. M. Anhar Uddin (ORCID:0000000334212↗
DOE OSTI2024

Impact of metal diffusion, lattice distortions, native defects, and ambient on dielectric breakdown in Ni–Ga 2 O 3 Schottky diodes

Ga 2 O 3 unipolar devices are of high interest due to their ~8 MV/cm predicted breakdown fields, which have not yet been achieved due to premature device failure. Pre- and post-failure defect analysis of Ni–Ga 2 O 3 Schottky diodes in ultrahigh vacuum (UHV) and air were performed using depth-resolved cathodoluminescence, high angle annular dark field scanning transmission electron microscopy, and energy dispersive x-ray analysis to understand the physical mechanisms that precede premature breakdown. The breakdown voltage in UHV was dramatically reduced by nearly 40% compared with the breakdown in air. This reduction in the breakdown voltage correlated with post-breakdown differences in Ni distribution, indicating that the coordination and bonding of Ni contribute strongly to electrical behavior in Ni–Ga 2 O 3 Schottky diodes. Breakdown studies in UHV revealed that Ni diffuses away more from the metal–semiconductor interface than with air breakdown, where Ni localizes more near the interface, indicative of the preferential formation of a Ni oxide under O-poor conditions. These measurements also identified the formation of divacancy-interstitial complexes and their characteristic luminescence signature ~150 nm from the interface, the densities of which correlated with breakdown fields. These findings show that electric-field-induced degradation occurs via the rearrangement of native point defects, which act as an additional precursor to device failure. Macroscopically, they show the impact of both vacuum conditions and metal reactivity on Ga 2 O 3 device fabrication.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Tunnel junction-enabled monolithically integrated GaN micro-light emitting transistor

GaN/InGaN microLEDs are a very promising technology for next-generation displays. Switching control transistors and their integration are key components in achieving high-performance, efficient displays. Monolithic integration of microLEDs with GaN switching devices provides an opportunity to control microLED output power with capacitive (voltage)-controlled rather than current-controlled schemes. This approach can greatly reduce system complexity for the driver circuit arrays while maintaining device opto-electronic performance. In this work, we demonstrate a 3-terminal GaN micro-light emitting transistor that combines a GaN/InGaN blue tunneling-based microLED with a GaN n-channel FET. Further, the integrated device exhibits excellent gate control, drain current control, and optical emission control. This work provides a promising pathway for future monolithic integration of GaN FETs with microLED to enable fast switching, high-efficiency microLED display and communication systems.

42 ENGINEERING↗
DOE OSTI2024

High temperature stability of regrown and alloyed Ohmic contacts to AlGaN/GaN heterostructure up to 500 °C

This Letter reports the stability of regrown and alloyed Ohmic contacts to AlGaN/GaN-on-Si high electron mobility transistors (HEMTs) for high temperature applications up to 500 °C. Transfer length method (TLM) measurements from 25 to 500 °C in air show that the regrown contacts appear to be stable up to 500 °C during short term (approximately 1 h) testing, while alloyed contacts appear to decrease in contact resistance from 300 to 500 °C though increases in the error bounds due to increase sheet resistance make it difficult to conclude definitely. Additionally, longer term testing shows both technologies remain stable at least up to 48 h at 500 °C, after which the large increase in sheet resistance makes the measurement uncertainty too large to conclude definitively. Advanced microscopy images indicate both the regrown and alloyed contact regions remain structurally intact after prolonged high temperature exposure with no visible degradation in crystallinity or metal composition.

Physics↗
DOE OSTI2024

Investigation of Interlayer Dielectric in BaTiO 3 /III–Nitride Transistors

In this paper, the impact of varying the thickness of the Al 2 O 3 interlayer dielectric on the electrical characteristics of BaTiO 3 /III-nitride transistors is investigated. In the findings, it is revealed that a minimum thickness of 8 nm for the Al 2 O 3 layer is crucial to maintain high device performance and protect against sputtering-induced damage during BaTiO 3 deposition. The fabricated BaTiO 3 /Al 2 O 3 /AlGaN/GaN high electron mobility transistors exhibit exceptional electrical properties, including a maximum current density of 700 mA mm –1 , an on-resistance of 5 Ω mm, an I ON /I OFF ratio of 10 7 , a subthreshold slope of 119 mV dec –1 , and significantly reduced gate leakage current. The devices with the optimal 8 nm Al 2 O 3 thickness demonstrates excellent agreement between theoretical and experimental values for effective mobility, achieving a value of 1188 cm 2 V –1 ·s at a 2D electron gas density of 10 13 cm –2 . Furthermore, in the study, it is confirmed that increasing the Al 2 O 3 thickness also improves the quality of interface charge density, as evidenced by the results obtained from capacitance–voltage measurements. In these findings, the critical role of controlling the Al 2 O 3 thickness in optimizing the electrical characteristics and overall performance of BaTiO 3 /III-nitride transistors are highlighted.

42 ENGINEERING↗
DOE OSTI2024

Al‐Rich AlGaN Transistors with Regrown p‐AlGaN Gate Layers and Ohmic Contacts

Abstract Epitaxial regrowth processes are presented for achieving Al‐rich aluminum gallium nitride (AlGaN) high electron mobility transistor (HEMTs) with p‐type gates with large, positive threshold voltage for enhancement mode operation and low resistance Ohmic contacts. Utilizing a deep gate recess etch into the channel and an epitaxial regrown p‐AlGaN gate structure, an Al 0.85 Ga 0.15 N barrier/Al 0.50 Ga 0.50 N channel HEMT with a large positive threshold voltage (V TH = +3.5 V) and negligible gate leakage is demonstrated. Epitaxial regrowth of AlGaN avoids the use of gate insulators which can suffer from charge trapping effects observed in typical dielectric layers deposited on AlGaN. Low resistance Ohmic contacts (minimum specific contact resistance = 4 × 10 −6 Ω cm 2 , average = 1.8 × 10 −4 Ω cm 2 ) are demonstrated in an Al 0.85 Ga 0.15 N barrier/Al 0.68 Ga 0.32 N channel HEMT by employing epitaxial regrowth of a heavily doped, n‐type, reverse compositionally graded epitaxial structure. The combination of low‐leakage, large positive threshold p‐gates and low resistance Ohmic contacts by the described regrowth processes provide a pathway to realizing high‐current, enhancement‐mode, Al‐rich AlGaN‐based ultra‐wide bandgap transistors.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Plasma-assisted deposition and characterization of Al 2 O 3 dielectric layers on (001) β -Ga 2 O 3

In this work, we have investigated plasma-assisted deposition of Al 2 O 3 on HVPE (001) β-Ga 2 O 3 and evaluated the dielectric quality from electrical measurements on fabricated metal-oxide-semiconductor (MOS) capacitors. The interface structure and crystallinity of the films were investigated as a function of the growth temperature. The dielectric/semiconductor interfaces were found to have reverse breakdown electric fields up to 5.3 MV/cm in the β-Ga 2 O 3 , with relatively low hysteresis in capacitance–voltage and low leakage current. We determined a negative fixed interface charge density at the interface from analysis of thickness-dependent capacitance voltage data. In conclusion, this study shows the advantage of using plasma-assisted deposition to achieve high breakdown strength Al 2 O 3 /β-Ga 2 O 3 MOS structures for device application purposes.

42 ENGINEERING↗
DOE OSTI2023

β -Ga 2 O 3 trench Schottky diodes by low-damage Ga-atomic beam etching

β-Ga 2 O 3 trench Schottky barrier diodes fabricated through a Gallium atomic beam etching technique with excellent field strength and power device figure of merit are demonstrated. Trench formation was accomplished by a low-damage Ga flux etch that enables near-ideal forward operating characteristics that are independent of fin orientation. The reverse breakdown field strength of greater than 5.10 MV/cm is demonstrated at a breakdown voltage of 1.45 kV. This result demonstrates the potential for Ga atomic beam etching and high-quality dielectric layers for improved performance in β-Ga 2 O 3 vertical power devices.

42 ENGINEERING↗
DOE OSTI2023

Wireless System Development for GaN-Based Transmitters for Advanced Nuclear Reactor Environments

The market for consumer electronics is dominated by Si-based electronics. Many Si-based complementary metal–oxide–semiconductor (CMOS) devices are reaching their limitations in terms of switching frequencies, voltages, currents, and temperatures. Furthermore, these devices are widely known to be susceptible to ionizing radiation and neutrons. Advanced nuclear reactors, especially microreactors and small modular reactors, require wireless electronics that can survive larger neutron and gamma doses than Si CMOS. Because of their size, electronics will need to be placed closer to the reactor cores, and cabling capabilities may be limited. However, GaN high-electron-mobility transistors (HEMTs) have been shown to switch faster with higher gains, and they can achieve current and voltage limits beyond traditional Si CMOS. However, they have less market maturity and have undergone less testing. These GaN HEMTs have been shown to survive ionizing radiation with little effects, but the effects of neutron radiation remain widely unknown. In this report, a wireless electronic system capable of supporting multiple radiation-hardened (rad-hard) sensors is presented. The proposed transmission scheme was designed to be simple to increase the likelihood of success in the immature GaN HEMT process and in high-radiation environments. The transmission system was tested using software-defined radios to emulate the transmission scheme before the transmitter circuitry in the GaN process was developed.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Demonstration of p-side down green light emitting diodes with high external quantum efficiencies

GaN/(In,Ga)N heterostructure based visible Light Emitting Diodes (LED) have enabled a wide range of solid-state lighting applications through excellent efficiency and power output in the shorter wavelengths (≤ 475nm) of violet/blue emission. However, the efficiency of emitters in the longer wavelength range (≥ 500nm) drops drastically due to the need to include higher Indium-content in the InGaN quantum wells. Large average polarization fields for high Indium-content quantum wells for conventional P-up structure, opposes the depletion field leading to large electrostatic barriers for both electrons and holes injection. LEDs fabricated along the N-polar direction with a p-up orientation or Ga-polar direction with p-down orientation lower such electrostatic barriers to carrier injection due to alignment of the polarization dipole field and depletion region field. This can therefore theoretically improve the electrical injection efficiency and reduce the forward voltage of operation. Such a Ga-polar p-down LED requires a bottom buried tunnel junction to avoid current spreading issues for a buried p-GaN layer. In this report, we demonstrate for the first time Ga-polar p-down green emitting LEDs using bottom tunnel junctions and having external quantum efficiencies comparable to those of equivalent p-up LEDs grown by Metal Organic Chemical Vapor Deposition (MOCVD).

36 MATERIALS SCIENCE↗
DOE OSTI2022

Simulation of GaN-based light emitting diodes incorporating composition fluctuation effects

III-Nitride light emitting diodes (LEDs) are widely used in a range of high efficiency lighting and display applications, which has enabled significant energy savings in the last decade. Despite the wide application of GaN LEDs, transport mechanisms across InGaN/GaN heterostructures in these devices are not well explained. Fixed polarization sheet charges at InGaN/GaN interfaces lead to large interface dipole charges, which create large potential barriers to overcome. One-dimensional models for transport across such heterostructures predict turn-on voltages that are significantly higher than that found in real devices. As a result, conventional models for transport cannot predict the performance of new designs such as for longer wavelength LEDs or for multi-quantum well LEDs. In this work, we show that incorporating low and high indium compositions within quantum wells at the submicrometer scale can provide an accurate prediction of the characteristics of GaN/InGaN light emitting diodes.

36 MATERIALS SCIENCE↗
DOE OSTI2022

β -Ga 2 O 3 Schottky barrier diodes with 4.1 MV/cm field strength by deep plasma etching field-termination Available

In this work, we demonstrate a deep mesa etch design for efficient edge field termination in β-Ga 2 O 3 Schottky barrier diodes (SBDs). The proposed design enabled parallel plate fields higher than 4.1 MV/cm with negligible change to the device ON characteristics. The effect of BCl 3 /Cl 2 -based dry etch on (100) and (010) etched vertical sidewalls is also analyzed. A remarkable anisotropy in depletion was observed for etch along (100) and (010) sidewalls. In conclusion, this work provides insight into the impact of etching on n-type Ga 2 O 3 and shows a promising method to realize efficient field termination for high breakdown field strength SBDs.

42 ENGINEERING↗
DOE OSTI2022

Selectively patterned Mg-doped GaN by SiN x -driven hydrogen injection

In this work, we demonstrate a method to achieve selectively patterned Mg-doped GaN layers using hydrogen drive-in through plasma-enhanced chemical vapor deposition (PECVD) silicon nitride (SiN x ) films. Activated Mg-doped GaN layers were selectively deactivated by patterned PECVD SiN x films with low-temperature annealing and showed high-resistive behavior. Spatially resolved photoluminescence measurements were used to optically verify the deactivation of Mg acceptors and showed distinct features corresponding to activated and deactivated Mg in GaN. The method suggested here provides a simple and effective method to achieve patterned Mg-doped GaN regions without thermal and plasma damage, which could cause degradation of device performance. The proposed method could provide a way to achieve future high-performance GaN lateral and vertical devices that rely on laterally patterned doping.

42 ENGINEERING↗
DOE OSTI2022

β -Ga 2 O 3 MESFETs with insulating Mg-doped buffer grown by plasma-assisted molecular beam epitaxy

In this work, we develop in situ Mg doping techniques in plasma-assisted molecular beam epitaxy (PAMBE) of β -Ga 2 O 3 to compensate Si dopants at the substrate epilayer growth interface and eliminate parasitic leakage paths. Both abrupt and uniform Mg doping profiles over a wide range of concentrations were achieved in β -Ga 2 O 3 epilayers grown by PAMBE. Capacitance–voltage characteristics of Si and Mg co-doped samples confirmed the compensating effect of the Mg dopants. Mg delta-doping was then integrated into a β -Ga 2 O 3 metal-semiconductor field effect transistor structure and shown to be effective in eliminating source leakage. In conclusion, the results presented here show that Mg doping is a promising way to engineer insulating buffer layers for β -Ga 2 O 3 lateral devices grown by PAMBE.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2022

Radiation-Hardened GaN HEMT and Cell Design, Modeling, and Fabrication for Nuclear Instrumentation Applications

Recent advances in nuclear power generation technologies show great promise for efficient, safe generation of carbon-free power in the near future. Consequently, many new generation reactor designs are being pursued by government and industry groups, including both fission- and fusion-based technologies. Radiation- and temperature-tolerant sensor technology continues to advance, yet development of the electronics/instrumentation technologies suitable for these environments have fallen behind. Industry has adequately addressed harsh environment electronics needs for low earth orbit satellites, but the much more extreme conditions associated with electronics placed near or in a reactor core remain unaddressed. This project investigates the use of gallium nitride (GaN) circuit technology to address the unique needs for sensor interface electronics and communications in reactor environments. This report provides a summary of the first year’s project activities related to developing and optimizing devices and circuits for this GaN high electronic mobility transistor (HEMT) process. Activities reported include multiple analog and digital circuit designs simulated using custom Verilog-A models generated from measured GaN devices fabricated in the target process. Digital circuit designs included fundamental logic circuits such as an inverter, NAND, NOR, AND and OR gates, as well as a 5-stage ring oscillator. Each design was simulated using an open-source SPICE simulator, and an integrated circuit layout was produced of each design for use in future fabrication. Analog circuit designs focused on the fundamental building blocks to be used to construct sensor interface and communications circuits. These included current mirrors, matched differential pairs, and a Gilbert cell mixer design, each with an associated integrated circuit layout. Layout tools used for these designs included two open-source packages—KLayout and Magic—which were customized for specific use with the OSU GaN process layers. Design rules and preliminary device extraction capabilities were built for the Magic tool to enable device extraction and subsequent netlist generation for SPICE simulation. Finally, future research directions for year two are summarized. When the year-two directions are implemented, the project will be in position to advance the state of the art in electronics for near- or in-reactor sensor interfacing and communications.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗