Electrochemical Li intercalation in b-As y P 1–y alloys: In-situ Raman spectroscopy study

Structural evolution of b-As y P 1-y alloys with varying As concentration, y was studied during Li-intercalation using in-situ Raman spectroscopy. A monotonic redshift of all the vibrational modes corresponding to P-P bonds (A 1 g , A 2 g , B 2g ), As-As bonds (A 1 g , A 2 g , B 2g ), and As-P bonds of all the samples was observed during the initial stages of the intercalation process due to the softening of each mode caused by the intercalation driven donor-type charge-transfer from Li to b-As y P 1-y . The emergence of a new peak identified as the E g mode of gray As, above an intercalation threshold, is indicative of the presence of an intercalation-driven structural phase segregation process. Further, the A 1g mode of gray As emerging after this intercalation threshold lies in close proximity of the A 2 g Raman mode of b-As y P 1-y . All the peaks beyond the intercalation threshold show an upshift due to the co-existence of gray As with b-As y P 1-y alloys causing strain and thus hardening of the phonon modes. In the sample with the highest As concentration phase segregation takes place during the synthesis process. Computational modeling reveals the co-existence of gray As in the b-As y P 1-y alloys with high As concentrations. It also confirms the existence of a local structural segregation taking place at a critical Li concentration during the intercalation process. Furthermore, this work shows the significance of intercalation on structural changes in the search for new phases of b-As y P 1-y alloys.

2D Materials↗
DOE OSTI2021

Vapor-Phase Intercalation of Cesium into Black Phosphorous

Cesium vapors were charged into black phosphorous (BP) flakes at varied times and at a temperature gradient of 150 °C. The X-ray diffraction (XRD) measurements of these samples suggest a reduction in the strength of van der Waal interactions between BP layers leading to the loss of coherence of out-of-plane peaks. At the same time, the three main Raman modes of BP (A g 1 , B 2 g , and A g 2 ) steadily redshifted as exposure times were increased, with modes B 2 g and A g 2 shifting faster than A g 1 . After initial rapid downshifts of active BP phonon modes, this intercalation strategy showed its limits following prolonged exposure times. Saturation of BP flakes by Cs vapors ensued and the kinetics was fitted with an exponential decay function. Furthermore, the thermoelectric power (TEP) of cesiated BP exhibited an inversion in sign from positive to negative around 400 K, lending credence to the transformation of as-prepared BP which is a p-type semiconductor to an n-type equivalent due to Cs atom intercalation driven shifting of the Fermi level toward the conduction band of BP and the donation of electrons from Cs. Furthermore, density functional theory (DFT) calculations were used to delve deeper into understanding Cs intercalation on the structural evolution of BP.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Visualization of Solid-State Synthesis for Chalcogenide Na Superionic Conductors by in-situ Neutron Diffraction

Chalcogenide superionic sodium (Na) conductors are great potential as solid electrolytes (SEs) in all-solid-state Na batteries with advantages of high energy density and safety, and cost effectiveness. For solid Na-ion conductors, their crystal structures and ionically conductive properties are strongly influenced by the synthetic approaches and processing parameters. Thus, understanding the synthesis process is essential to control the structures and phases and thereby yields to Na-ion conductors with desirable properties. Thanks to the high-flux and deep-penetrating time-of-flight neutron diffraction (ND), we employed in situ experiments to track real-time structural changes of two chalcogenide SEs (Na 3 SbS 4 and Na 3 SbS 3.5 Se 0.5 ) during the solid-state synthesis. For these two conductors, the ND results reveal a fast one-step reaction for the synthesis and the molten process when heating up, and the recrystallization as well as the cubic-to-tetragonal phase transition up on cooling. Moreover, Se-doping is found to influence the reaction temperatures, lattice parameter and structure stability based on neutron experimental observations and theoretical simulation. This work presents a detailed structural study using in situ neutron diffraction technology for the solid synthesis process of chalcogenide Na-ion conductors, beneficial for the design and synthesis of new solid-state conductors.

25 ENERGY STORAGE↗
DOE OSTI2021

Vibrational Properties of Pristine and Lithium-Intercalated Black Phosphorous under High-Pressure

Structural evolution of Li-intercalated and pristine black phosphorous (BP) under high-pressure (up to ≈8 GPa) is studied using in situ Raman spectroscopy. Even though both materials show a monotonic blueshift of the out-of-plane vibrational mode (A 1 g ) with pressure, Li-intercalated BP do not show a blueshift until a threshold pressure (2.4 GPa) is reached to compensate the structural expansion caused by intercalation. However, the in-plane modes (B 2g and A 2 g) in each sample respond differently. In the mid-pressure region, they both show redshifts which in Li-intercalated BP is also followed by abrupt blueshifts. Such behavior indicates pressure-induced structural reorganizations inside the material. Computational modeling reveals the existence of a process of P-P bond breaking and reforming in the system due to the redistribution of intercalated Li atoms under pressure. This work shows the significance of combined effect of pressure and intercalation on structural changes in the search for new phases of BP and other two-dimensional (2D) materials.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Intercalation as a versatile tool for fabrication, property tuning, and phase transitions in 2D materials

Recent advances in two-dimensional (2D) materials have led to the renewed interest in intercalation as a powerful fabrication and processing tool. Intercalation is an effective method of modifying the interlayer interactions, doping 2D materials, modifying their electronic structure or even converting them into starkly different new structures or phases. Herein, we discuss different methods of intercalation and provide a comprehensive review of various roles and applications of intercalation in next-generation energy storage, optoelectronics, thermoelectrics, catalysis, etc. The recent progress in intercalation effects on crystal structure and structural phase transitions, including the emergence of quantum phases are also reviewed.

2D materials↗
DOE OSTI2021

Li interaction-induced phase transition from black to blue phosphorene

A comprehensive first-principle calculation has been carried out and revealed that at sufficiently high Li concentration and certain well-defined configurations a phase transition from black to blue phosphorene can take place. Blue phosphorene, a newly predicted allotrope of phosphorus, possesses unique crystalline and electronic structure and is a promising candidate, not only for fundamental research but also for electronic and optoelectronic applications. Methods to growth high quality blue phosphorene layers are highly desirable but challenging. Here, a novel kinetic pathway to grow blue phosphorene layers from black phosphorene layers via Li intercalation is proposed based on first principle study. This study pointed out that Li atoms intercalated in black phosphorene could act as ‘catalyst’ in the ‘reactive region’ of the lone pair of P atoms, leading to a P-P bond breaking and subsequently, a local structural transformation from orthorhombic lattice to an assembly of parallel narrow nanoribbons with rhombohedra-like symmetry. During Li deintercalation, these nanoribbons are self-mended and form blue phosphorene layers. The interlayer distance was found 4.60 Å for double layer with AA stacking and 4.13 Å for multilayer with ABC stacking, respectively, indicating a monolayer blue phosphorene can be mechanically exfoliated. Furthermore, this study also points out the possibility of new phases in other systems, where intercalation can lead to an unexpected structural phase transition and even a discovery of novel materials.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Structural and Thermoelectric Properties of Black Arsenic–Phosphorus

Here, we report the structural and temperature dependent transport properties of As x P 1-x (x = 0, 0.2, 0.5, 0.83, 1) alloys. It is observed that black phosphorous (BP)-related phonon modes in the alloy samples are red-shifted with increasing arsenic concentration, while black arsenic-related modes in these samples are blue-shifted with increasing phosphorus concertation. As the arsenic concentration, x increases from 0 to 1, the 4-probe resistance of the As x P 1-x alloys is found to decrease by more than 3 orders of magnitude. The transport studies reveal that samples with the highest arsenic concentration (x = 1 and 0.83) show metallic behavior in the temperature dependence of resistance with a small thermopower at room temperature with an anomalous temperature dependence. In contrast, the samples with high phosphorus concentration (x = 0, 0.2, and 0.5) show very large thermopower values at room temperature reaching a value as high as 803 μV/k for x = 0.2. The temperature dependence of the thermopower of these samples can be well described by the variable range hopping (VRH) mechanism in two-dimensions (2-d), S ~ T 1/3 . Similarly, their 4-probe resistance (R) values can be fitted with 2-d VRH mechanism, R ~ exp(T -1/3 ).

36 MATERIALS SCIENCE↗
DOE OSTI2020

Electrochemical Li Intercalation in Black Phosphorus: In Situ and Ex Situ Studies

A systematic study on electrochemical charge transfer in Li-doped black phosphorous (BP) was carried out by both in-situ and ex-situ Raman scattering. Galvanostatic discharge of dedicated in-situ electrochemical cell for Raman spectroscopy was used to study time evolution of vibrational modes under lithiation. In addition to the peak broadening which is a result of structural expansion, peaks corresponding to all three atomic vibrational modes A 1 g , B 2 g and A 2 g were found to red-shift as a result of lithiation. Peaks B 2 g and A 2 g were shifted about 1.6 times more towards lower wavenumbers in comparison to A 1 g . Further characterizations using optical and electron microscopy showed that the intercalation of BP is highly anisotropic, where channels along the zigzag direction were found to be the easy direction for intercalation. X-ray diffraction on intercalated samples confirmed a reduction of thickness as lithiation weakens interlayer bonding, thus resulting in a partial exfoliation of BP flakes. Here, first principle studies using density function theory (DFT) were used to develop a theoretical model for the intercalation mechanism. The discrepancy between the experimental and the theoretical results was also addressed.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Gas adsorption and light interaction mechanism in phosphorene-based field-effect transistors

Phosphorene-based field effect transistor (FET) structures were fabricated to study the gas- and photo-detection properties of phosphorene. The interplay between device performance and environmental conditions was probed and analyzed using in situ transport measurements. The device structures were exposed to different chemical and light environments to understand how they perform under different external stimuli. For the gas/molecule detection studies, inert (Ar), as well as, oxidizing (N 2 O), and reducing (H 2 and also N 2 H 4 ) agents were selected. The FET structure was exposed to these different gases, and the effect of each gas on the device resistance was measured. The study showed varying response towards different molecules. Specifically, no significant resistance change was observed upon exposure to Ar, while H 2 and N 2 H 4 were found to decrease the resistance and N 2 O had the opposite effect resulting in an increase in resistance. This work is the first demonstration for the detection of N 2 H 2 and N 2 O using a phosphorene-based system. These phosphorene-based FET structures were also found to be sensitive to light exposure. When such structure was irradiated with light, the current modulation was lost. The observed resistance changes can be explained as a result of the modulation of the Schottky barrier at the phosphorene-electrical contact interface due to the adsorbed molecules and charge transfer, and/or photo-induced carrier generation. Furthermore, the results were consistent with the transfer characteristics of V ds v s . V g .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗