Progress toward the development of dual junction GaAs/Ge solar cells
Large area GaAs/Ge cells offer substantial promise for increasing the power output from existing silicon solar array designs and for providing an enabled technology for missions hitherto impossible using silicon. Single junction GaAs/Ge cells offer substantial advantages in both size, weight, and cost compared to GaAs cells but the efficiency is limited to approximately 19.2 to 20 percent AMO. The thermal absorptance of GaAs/Ge cells is also worse than GaAs/GaAs cells (0.88 vs 0.81 typ.) due to the absorption in the Ge substrate. On the other hand dual junction GaAs/Ge cells offer efficiencies up to ultimately 24 percent AMO in sizes up to 8 x 8 cm but there are still technological issues remaining to achieve current matching in the GaAs and Ge cells. This can be achieved through tuned antireflection (AR) coatings, improved quality of the GaAs growth, improved quality Ge wafers and the use of a Back Surface Field (BSF)/Back Surface Reflector (BSR) in the Ge cell. Although the temperature coefficients of efficiency and voltage are higher for dual junction GaAs/Ge cells, it has been shown elsewhere that for typical 28 C cell efficiencies of 22 percent (dual junction) vs 18.5 percent (single junction) there is a positive power tradeoff up to temperatures as high as 120 C. Due to the potential ease of fabrication of GaAs/Ge dual junction cells there is likely to be only a small cost differential compared to single junction cells.