Magnetocaloric properties of Eu{sub 1−x}La{sub x}TiO{sub 3} (0.01 ≤ x ≤ 0.2) for cryogenic magnetic cooling
We report magnetic and magnetocaloric (MCE) properties of polycrystalline Eu{sub 1−x}La{sub x}TiO{sub 3} samples over a wide composition range (0.01 ≤ x ≤ 0.20). It is found that the ground state changes from antiferromagnetic for x = 0.01 (T{sub N} = 5.2 K) to ferromagnetic for x ≥ 0.03 and the ferromagnetic Curie temperature increases from T{sub C} = 5.7 K for x = 0.03 to T{sub C} = 7.9 K for x = 0.20. The x = 0.01 sample shows a large reversible isothermal magnetic entropy change of −ΔS{sub m} = 23 (41.5) J/kg K and adiabatic temperature change of ΔT{sub ad} = 9 (17.2) K around 6.7 K for a field change of μ{sub 0}ΔH = 2 (5) Tesla. Although the peak value of −ΔS{sub m} decreases as La content increases, it is impressive in x = 0.2(−ΔS{sub m} = 31.41 J/kg K at T = 7.5 K for μ{sub 0}ΔH = 5 T). The large value of MCE arises from suppression of the spin entropy associated with the localized moment (J = 7/2) of Eu{sup 2+}:4f{sup 7} ions. This large MCE over a wide compositional range suggests that the Eu{sub 1−x}La{sub x}TiO{sub 3} series could be useful for magnetic cooling below 40 K.
Magnetocaloric effect in amorphous and partially crystallized Fe{sub 40}Ni{sub 38}Mo{sub 4}B{sub 18} alloys
A study of magnetocaloric effect in amorphous and partially crystallized Fe{sub 40}Ni{sub 38}Mo{sub 4}B{sub 18} alloys is reported. Amorphous Fe{sub 40}Ni{sub 38}Mo{sub 4}B{sub 18}, near its magnetic ordering temperature (600 K) showed a magnetic entropy change ΔS{sub M} of 1.1 J/KgK and a relative cooling power of 36 J/Kg in a field change of 10 kOe. Amorphous samples were partially crystallized by annealing at 700 K at different time intervals. Partially crystallized samples showed two distinct magnetic ordering temperature, one corresponding to the precipitated FeNi nanocrystals and the other one corresponding to the boron rich amorphous matrix. Magnetic ordering temperature of the residual amorphous matrix got shifted to the lower temperatures on increasing the annealing duration. Partially crystallised samples showed a magnetic entropy change of about 0.27 J/kgK near the magnetic ordering temperature of the amorphous matrix (540 K) in a field change of 10 kOe. The decrease in ΔS{sub M} on partial crystallisation is attributed to the biphasic magnetic nature of the sample.