DOE OSTI2024

Experimental determination of the electrochemical properties of bismuth chloride in eutectic LiCl–KCl and LiCl–KCl–CaCl 2 molten salts

Bismuth has been investigated as a potential liquid electrode for molten salt electrorefining, but the electrochemical behavior of Bi 3+ /Bi redox couple has received scant attention in LiCl–KCl and LiCl–KCl–CaCl 2 eutectics. Electroanalytical techniques were used to determine properties of Bi 3+ /Bi. Diffusivities of 6.71 and 8.93 × 10 –6 cm 2 s –1 and standard apparent potentials of 0.1166 and 0.1187 V versus Ag/AgCl (4.75 mol%) were recommended for BiCl 3 in LiCl–KCl and LiCl–KCl–CaCl 2 eutectics, respectively, at 680 ± 3.1 K. The ICP-MS analysis of BiCl 3 content limited the accuracy of the results. Furthermore, the reliability of the results improved with a more thorough drying procedure for CaCl 2 .

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Determination of a surrogate for plutonium electrorefining

Conducting research experiments on plutonium electrorefining is difficult due to the significant hazards and regulations associated with nuclear materials. Finding a surrogate for plutonium electrorefining studies would enable more fundamental research to be conducted. Potential surrogates were first identified by determining the physical properties required to conduct electrorefining at the same conditions commonly used in plutonium electrorefining, a molten metal and molten CaCl 2 at 1123 K. Ce-CeCl 3 , In-InCl 3 , and Pb-PbCl 2 were the only potential surrogates identified using these constraints. Sn-SnCl 2 was also tested at these same conditions. More potential surrogates were identified by changing the matrix salt and operating temperature. This expanded the potential surrogate list to also include Zn-ZnCl 2 , Sn-SnCl 2 , and Bi-BiCl 3 . Zn-ZnCl 2 was used with the LiCl-CaCl 2 (65:35 mol%) eutectic at 773 K. Sn-SnCl2 and Bi-BiCl 3 were used with the LiCl-KCl-CaCl 2 (50.5:44.2:5.3 mol%) eutectic at 673–773 K. Ce electrorefining in molten CaCl 2 resulted in a difficult to separate colloid mixture of Ce, Ca and Cl. Electrorefining rates for In in molten CaCl 2 were too slow due to InCl 3 volatilizing out of the molten salt. Only trace amounts of SnCl 2 was retained in the CaCl 2 at 1123 K resulting in impractical electrorefining rates. Zn metal product was successfully collected in the LiCl-CaCl 2 eutectic molten salt, but the metal obtained did not coalesce into one piece. Sn and Bi were successfully electrorefined in the LiCl-KCl-CaCl 2 eutectic molten salt and coalesced into product rings with high yields and coulombic efficiencies. Finally, while a surrogate could not be identified using the same conditions as plutonium electrorefining, two possible surrogates, Sn-SnCl 2 and Bi-BiCl 3 , were found that could imitate the physical configuration (i.e., molten salt on top of molten metal) of plutonium electrorefining at a reduced temperature using the eutectic LiCl-KCl-CaCl 2 salt at 673–773 K in place of CaCl 2 at 1123 K.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Development of In-Situ Chlorine Generator for Metal Purification (End of Contract Report)

It has been demonstrated that rare-earth and actinide metals can be purified via conversion to chlorides and heating to volatilize impurities. To this end, BYU has been working towards designing, building, and testing a system that incorporates the chlorine gas generation method into the chloride volatility process. The efforts made towards the project tasks listed in the Statement of Work are addressed in the following sections. Finally, a report on information related to this project that has been published or presented is addressed. By the end of the contract period, small-scale tests using LaCl 3 -CaCl 2 to generate Cl 2 had been conducted, the produced Cl 2 was successfully reacted with Ce foil to create CeCl 3 , initial designs for the large-scale apparatus were completed, and manufacturing for the large-scale apparatus had begun.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Electroanalytical Measurements of Oxide Ions in Molten CaCl 2 on W electrode

The electrochemical interaction of oxide ions with tungsten electrodes in molten calcium chloride (CaCl 2 ) was analyzed by combining electroanalytical techniques with X-ray photoelectron spectroscopy. During a cyclic voltammetry (CV) scan, the oxide ions appear to interact with the tungsten working electrode via a multi-step oxidation and reduction process. The overall redox peaks behave reversibly up to 750 mV s -1 . This electrochemical process enables the oxide ion concentration to be correlated to CV oxidation peaks. Lastly, the resulting correlation agrees well (8.8% difference) with back titration measurements and can be used to monitor oxide content in the salt in real-time during CaCl 2 based pryoprocesses.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Development of small-scale plutonium electrorefining in molten CaCl 2

Molten salt extraction and electrorefining of plutonium were successfully conducted with only a 200-g initial charge. Due to this small scale, the electrorefining cell components were redesigned relative to conventional, multi-kg standards. The efficiency and yield of this small-scale process are comparable to those of larger-scale exemplars. Chemical analysis of the plutonium product and the anode heel is presented. Here, the product was 99.8% pure. The anode heel was able to be depleted beyond the expected freezing point without significant impurity carryover.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

Development of metallic nuclear material purification process via simultaneous chlorination and volatilization

Here, a purification process involving simultaneous chlorination and volatilization is reported using aluminum, iron, gallium, and uranium separation from cerium metal as the demonstration system. Anhydrous Cl 2 gas was reacted with the metal after it had been converted to small particles of hydride at temperatures ranging from 523 to 973 K. Each of the impurities should form chlorides with relatively high saturated vapor pressures. The objective of the process was to volatilize these chlorides after first achieving near-complete conversion of the metals to hydride and then chlorides. Complete conversion of hydrides to chlorides could not be achieved using relatively low-grade (99.5%) Cl 2 . High decontamination factors for all of the metal impurities required near complete conversion to chloride. It was concluded that oxygen contamination of the feed gas stream likely limits the conversion to chlorides by forming oxides instead, which then limits the volatilization of contaminants. Uranium was particularly challenging to remove in experiments suspected of having high oxygen contamination in the feed gas stream. After switching to ultra-high purity (99.999%) Cl 2 , complete conversion to chlorides within the measurement error was possible for the entire temperature range studied. Decontamination factors for aluminum, iron, gallium, and uranium were found to have average values of 1.9, 9.8, 14, and 5, respectively, at 973 K. While the process was most extensively studied using a once-through gas flow, recycling unreacted Cl 2 gas succeeded at minimizing waste while still maintaining complete conversion and similar decontamination factors.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Gas-solid reaction pathway for chlorination of rare earth and actinide metals using hydrogen and chlorine gas

Hydriding and chlorination of buttons of metallic cerium have been tested as a head-end step to separating metal impurities from actinides. The objective here was to achieve complete conversion to chlorides while maintaining high surface area via small particles and open porosity. Hydriding by reaction with 100% H 2 gas at 573 K was successful at reducing cm-scale metal buttons into small particles/fragments. This step was followed by reaction with flowing 99.5% anhydrous Cl 2 gas at temperatures ranging from 423 to 573 K for 60 min. In experiments reported here, up to 92% conversion to cerium chloride was achieved from reacting with the anhydrous chlorine gas. The final chloride product has high porosity coupled with small particle sizes (microns to 1600 μm), which makes it suitable for subsequent purification processes. Higher chlorine concentrations in the gas favor higher conversion to chloride. The optimal temperature to achieve high chlorination is 523 K. Oxygen is a minor impurity in the chlorine gas which appears to prevent complete chlorination from being achieved.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗