Ratcliffe, James

Publications and source records attributed to Ratcliffe, James.

9 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS2020

Quasi-static and Fatigue Delamination at Tape/Fabric Interfaces

The relationship between quasi-static and fatigue delamination of a fabric/tape interface is examined experimentally and numerically.Mixed-mode bending tests were conducted using specimens in which a mid-plane delamination is bound between a ply of 0-degree unidirectional tape and a 0-degree fabric ply of the same material system. The experimental results indicate that delaminations tend to migrate towards the constraining ply that is on the compressive side of the laminate in bending, and that the fracture toughness for a fabric-constrained delamination is almost twice that of a tape-constrained delamination. A cohesive model based on superposition of bilinear laws was used to account for these differences in measured properties. Fatigue analyses were conducted with a cohesive damage model that uses an idealization of stress-life diagrams used in engineering design. The fatigue model is shown to be capable of predicting the steady-state rate of delamination propagation described by the Paris law, as well as the initial transients that depend on the quasi-static R-curve effects. The analysis results help quantify the effects of fracture toughness and R-curves on the rates of delamination propagation in fatigue.

Davila, Carlos G.↗
NASA NTRS2017

Guidelines for VCCT-Based Interlaminar Fatigue and Progressive Failure Finite Element Analysis

This document is intended to detail the theoretical basis, equations, references and data that are necessary to enhance the functionality of commercially available Finite Element codes, with the objective of having functionality better suited for the aerospace industry in the area of composite structural analysis. The specific area of focus will be improvements to composite interlaminar fatigue and progressive interlaminar failure. Suggestions are biased towards codes that perform interlaminar Linear Elastic Fracture Mechanics (LEFM) using Virtual Crack Closure Technique (VCCT)-based algorithms [1,2]. All aspects of the science associated with composite interlaminar crack growth are not fully developed and the codes developed to predict this mode of failure must be programmed with sufficient flexibility to accommodate new functional relationships as the science matures.

Deobald, Lyle R.↗
NASA NTRS2014

A Numerical and Experimental Study of Damage Growth in a Composite Laminate

The present study has three goals: (1) perform an experiment where a simple laminate damage process can be characterized in high detail; (2) evaluate the performance of existing commercially available laminate damage simulation tools by modeling the experiment; (3) observe and understand the underlying physics of damage in a composite honeycomb sandwich structure subjected to low-velocity impact. A quasi-static indentation experiment has been devised to provide detailed information about a simple mixed-mode damage growth process. The test specimens consist of an aluminum honeycomb core with a cross-ply laminate facesheet supported on a stiff uniform surface. When the sample is subjected to an indentation load, the honeycomb core provides support to the facesheet resulting in a gradual and stable damage growth process in the skin. This enables real time observation as a matrix crack forms, propagates through a ply, and then causes a delamination. Finite element analyses were conducted in ABAQUS/Explicit(TradeMark) 6.13 that used continuum and cohesive modeling techniques to simulate facesheet damage and a geometric and material nonlinear model to simulate core crushing. The high fidelity of the experimental data allows a detailed investigation and discussion of the accuracy of each numerical modeling approach.

McElroy, Mark↗
NASA NTRS2013

Analysis of an Aircraft Honeycomb Sandwich Panel with Circular Face Sheet/Core Disbond Subjected to Ground-Air Pressurization

The ground-air pressurization of lightweight honeycomb sandwich structures caused by alternating pressure differences between the enclosed air within the honeycomb core and the ambient environment is a well-known and controllable loading condition of aerospace structures. However, initial face sheet/core disbonds intensify the face sheet peeling effect of the internal pressure load significantly and can decrease the reliability of the sandwich structure drastically. Within this paper, a numerical parameter study was carried out to investigate the criticality of initial disbonds in honeycomb sandwich structures under ground-air pressurization. A fracture mechanics approach was used to evaluate the loading at the disbond front. In this case, the strain energy release rate was computed via the Virtual Crack Closure Technique. Special attention was paid to the pressure-deformation coupling which can decrease the pressure load within the disbonded sandwich section significantly when the structure is highly deformed.

Rinker, Martin↗
NASA NTRS2012

Comparison of Intralaminar and Interlaminar Mode-I Fracture Toughness of Unidirectional IM7/8552 Graphite/Epoxy Composite

The intralaminar and interlaminar mode-I fracture-toughness of a unidirectional IM7/8552 graphite/epoxy composite were measured using compact tension (CT) and double cantilever beam (DCB) test specimens, respectively. Two starter crack geometries were considered for both the CT and DCB specimen configurations. In the first case, starter cracks were produced by 12.5 micron thick, Teflon film inserts. In the second case, considerably sharper starter cracks were produced by fatigue precracking. For each specimen configuration, use of the Teflon film starter cracks resulted in initially unstable crack growth and artificially high initiation fracture-toughness values. Conversely, specimens with fatigue precracks exhibited stable growth onset and lower initiation fracture toughness. For CT and DCB specimens with fatigue precracks, the intralaminar and interlaminar initiation fracture toughnesses were approximately equal. However, during propagation, the CT specimens exhibited more extensive fiber bridging, and rapidly increasing R-curve behavior as compared to the DCB specimens. Observations of initiation and propagation of intralaminar and interlaminar fracture, and the measurements of fracture toughness, were supported by fractographic analysis using scanning electron microscopy.

Czabaj, Michael W.↗
NASA NTRS2007

Analysis of Composite Panel-Stiffener Debonding Using a Shell/3D Modeling Technique

Interlaminar fracture mechanics has proven useful for characterizing the onset of delaminations in composites and has been used successfully primarily to investigate onset in fracture toughness specimens and laboratory size coupon type specimens. Future acceptance of the methodology by industry and certification authorities, however, requires the successful demonstration of the methodology on the structural level. For this purpose, a panel was selected that is reinforced with stiffeners. Shear loading causes the panel to buckle, and the resulting out-of-plane deformations initiate skin/stiffener separation at the location of an embedded defect. A small section of the stiffener foot, web and noodle as well as the panel skin in the vicinity of the delamination front were modeled with a local 3D solid model. Across the width of the stiffener foot, the mixedmode strain energy release rates were calculated using the virtual crack closure technique. A failure index was calculated by correlating the results with a mixed-mode failure criterion of the graphite/epoxy material. Computed failure indices were compared to corresponding results where the entire web was modeled with shell elements and only a small section of the stiffener foot and panel were modeled locally with solid elements. Including the stiffener web in the local 3D solid model increased the computed failure index. Further including the noodle and transition radius in the local 3D solid model changed the local distribution across the width. The magnitude of the failure index decreased with increasing transition radius and noodle area. For the transition radii modeled, the material properties used for the noodle area had a negligible effect on the results. The results of this study are intended to be used as a guide for conducting finite element and fracture mechanics analyses of delamination and debonding in complex structures such as integrally stiffened panels.

Krueger, Ronald↗
NASA NTRS1990

Predicting The Compression Strength Of Impact-Damaged Sandwich Panels

The objective of this work was to develop a technique for predicting the residual compression strength of sandwich panels containing impact damage in one facesheet. The technique was tailored to predict the strength of specimens that exhibit a failure mode involving the formation of kink bands at locations of peak strain in the region of impact damage. Under continued compression loading, the kink bands propagate in a stable manner perpendicular to the applied load. When a critical kink-band length is reached, growth becomes unstable corresponding to panel failure. The analysis follows in two sections. The first section calculates the far-field stress required for stable kink-band growth and the second calculates that required for unstable growth. The residual strength prediction is made when the stress for stable growth becomes equal to that for unstable kink-band growth. Initial comparisons between analysis and experiment show good agreement.

Ratcliffe, James↗