MnFe{sub 2}O{sub 4} as a gas sensor towards SO{sub 2} and NO{sub 2} gases
The chemical co-precipitation method was used to synthesize MnFe{sub 2}O{sub 4} nanoparticles. Single cubic phase formation of nanoparticles was confirmed by X-ray diffraction technique. The average particle size of MnFe{sub 2}O{sub 4} nanoparticles was found to be 10.7 nm using Scherrer formula. The ultrafine powder of MnFe{sub 2}O{sub 4} nanoparticles was pressed to design pellet of 10 mm diameter and 1mm thickness. Copper electrodes have been deposited on the surface of pellet using silver paste in the form of capacitor. Fabricated gas sensing device of MnFe{sub 2}O{sub 4} nanoparticles was tested towards SO{sub 2} and NO{sub 2} gases. Cole-Cole plot of MnFe{sub 2}O{sub 4} was investigated with the help of electrochemical workstation. The performance of the sensors including sensitivity, response and recovery time was also determined. It was observed that the MnFe{sub 2}O{sub 4} nanoparticles are more sensible for NO{sub 2} gas as compared to SO{sub 2} gas.