Ray, Chandra S.

Publications and source records attributed to Ray, Chandra S..

At least 19 records

Method of Estimating Continuous Cooling Transformation Curves of Glasses

A method is proposed for estimating the critical cooling rate and continuous cooling transformation (CCT) curve from isothermal TTT data of glasses. The critical cooling rates and CCT curves for a group of lithium disilicate glasses containing different amounts of Pt as nucleating agent estimated through this method are compared with the experimentally measured values. By analysis of the experimental and calculated data of the lithium disilicate glasses, a simple relationship between the crystallized amount in the glasses during continuous cooling, X, and the temperature of undercooling, (Delta)T, was found to be X = AR(sup-4)exp(B (Delta)T), where (Delta)T is the temperature difference between the theoretical melting point of the glass composition and the temperature in discussion, R is the cooling rate, and A and B are constants. The relation between the amount of crystallisation during continuous cooling and isothermal hold can be expressed as (X(sub cT)/X(sub iT) = (4/B)(sup 4) (Delta)T(sup -4), where X(sub cT) stands for the crystallised amount in a glass during continuous cooling for a time t when the temperature comes to T, and X(sub iT) is the crystallised amount during isothermal hold at temperature T for a time t.

Zhu, Dongmei↗

Computer Modeling of Thermal Convection in Melts to Explain Glass Formation in Low Gravity and on Earth

Experiments conducted up to this time on glass forming melts in the low gravity environment of space show that glasses prepared in low-g are more chemically homogeneous and more resistant to crystallization than the comparable glasses prepared at 1-g on Earth. This result is somewhat surprising and opposite to the accepted concept on glass formation for a melt. A hypothesis based on "shear thinning" of a melt, a decrease in viscosity with increasing shear stress, is proposed as an explanation for the observed low-gravity results. This paper describes detailed simulation procedures to test the role of thermal convection in introducing shear stress in glass forming melts, using a lithium disilcate melt as a model. The simulation system in its idealized version consists of a cylinder that is heated at one end and cooled at the other with gravity acting in a transverse direction to the thermal gradient. The side wall of the cylinder is assumed to be insulating. The governing equations of motion and energy are solved using variable properties for viscosity (Arrehenius and non-Arrehenius behaviors) and density (constant and temperature dependent). Other parametric variables in the calculations include gravity level and gravity vector orientation. The shear stress in the system are then computed as a function of gravity from the calculated values of maximum melt velocity, and its effect on melt viscosity (shear thinning) is predicted. Also included and discussed are the modeling efforts related to other potential convective processes in glass forming melts and their possible effects on melt viscosity.

Ray, Chandra S.↗

Processing of Lunar Soil Simulant for Space Exploration Applications

NASA's long-term vision for space exploration includes developing human habitats and conducting scientific investigations on planetary bodies, especially on Moon and Mars. To reduce the level of up-mass processing and utilization of planetary in-situ resources is recognized as an important element of this vision. Within this scope and context, we have undertaken a general effort aimed primarily at extracting and refining metals, developing glass, glass-ceramic, or traditional ceramic type materials using lunar soil simulants. In this paper we will present preliminary results on our effort on carbothermal reduction of oxides for elemental extraction and zone refining for obtaining high purity metals. In additions we will demonstrate the possibility of developing glasses from lunar soil simulant for fixing nuclear waste from potential nuclear power generators on planetary bodies. Compositional analysis, x-ray diffraction patterns and differential thermal analysis of processed samples will be presented.

Sen, Subhayu↗

Deformation, Stress Relaxation, and Crystallization of Lithium Silicate Glass Fibers Below the Glass Transition Temperature

The deformation and crystallization of Li(sub 2)O (center dot) 2SiO2 and Li(sub 2)O (center dot) 1.6SiO2 glass fibers subjected to a bending stress were measured as a function of time over the temperature range -50 to -150 C below the glass transition temperature (Tg). The glass fibers can be permanently deformed at temperatures about 100 C below T (sub)g, and they crystallize significantly at temperatures close to, but below T,, about 150 C lower than the onset temperature for crystallization for these glasses in the no-stress condition. The crystallization was found to occur only on the surface of the glass fibers with no detectable difference in the extent of crystallization in tensile and compressive stress regions. The relaxation mechanism for fiber deformation can be best described by a stretched exponential (Kohlrausch-Williams-Watt (KWW) approximation), rather than a single exponential model.The activation energy for stress relaxation, Es, for the glass fibers ranges between 175 and 195 kJ/mol, which is considerably smaller than the activation energy for viscous flow, E, (about 400 kJ/mol) near T, for these glasses at normal, stress-free condition. It is suspected that a viscosity relaxation mechanism could be responsible for permanent deformation and crystallization of the glass fibers below T,

Ray, Chandra S.↗

Containerless Processing of a Lithium Disilicate Glass

Glasses of Li2O.2SiO2 (LS2), and LS2 doped with 0.001wt% platinum (LS2 + 0.001 wt% Pt) compositions were melted, cooled and reheated at controlled rates while levitated (containerless) inside an Electrostatic Levitator (ESL) furnace at the NASA Marshall Space Flight Center, Huntsville, AL. The experiments were conducted in vacuum (approximately 10(exp -5) Pa) using spherical, 2.5 to 3 millimeter diameter, glass samples. The measured critical cooling rate for glass formation, R(sub c), for the LS2 and LS2+0.001 wt% Pt glasses processed at ESL were 14 plus or minus 2 Celsius per minute and 130 plus or minus 5 Celsius per minute, respectively. The values of R(sub c), for the same LS2 and LS2 + 0.001 wt% Pt glasses processed in a container were 62 plus or minus 3 Celsius per minute and 162 plus or minus 5 Celsius per minute, respectively. The effective activation energy for crystallization, E, for this LS2 glass processed without a container at ESL, 392 plus or minus 15 kiloJoules per mole, was higher than that, 270 plus or minus 15 kiloJoules per mole, for an identical glass processed in a container. These results suggest that the glass formation tendency for a containerless LS2 melt is significantly increased compared to an identical melt in contact with a container. The absence of heterogeneous nucleation sites that are inherently present in all melts held in containers, and or a change in the surface composition due to evaporation of Li2O during processing at ESL are likely reasons for the increased glass forming tendency of this containerless LS2 melt.

Ranasinghe, Kisa↗

A New DTA Method for Measuring Critical Cooling Rate for Glass Formation

A new differential thermal analysis (DTA) experimental method has been developed to determine the critical cooling rate for glass formation, R(sub c). The method, which is found especially suitable for melts that, upon cooling, have a small heat of crystallization or a very slow crystallization rate, has been verified using a 38Na2O-62SiO2 (mol%) melt with a known R(sub c) (-approx. 19 C/min), then used to determine R(sub c) for two complex lithium silicate glass forming melts. The new method is rapid, easy to conduct and yields values for R(sub c) that are in excellent agreement with the R(sub c)-values measured by standard DTA techniques.

Ray, Chandra S.↗

Nucleation and Crystallization as Induced by Bending Stress in Lithium Silicate Glass Fibers

Glass Fibers of Li2O.2SiO2 (LS2) and Li2O.1.6SiO2 (LS1.6) compositions were heated near, but below, the glass transition temperature for different times while subjected to a constant bending stress of about 1.2 GPa. The nucleation density and the crystallization tendency estimated by differential thermal analysis (DTA) of a glass sample in the vicinity of the maximum of the bending stress increased relative to that of stress-free glass fibers. LS2 glass fibers were found more resistant to nucleation and crystallization than the Ls1.6 glass fibers. These results are discussed in regards to shear thinning effects on glass stability.

Reis, Signo T.↗

Kinetics of Nucleation and Crystal Growth in Glass Forming Melts in Microgravity

This flight definition project has the specific objective of investigating the kinetics of nucleation and crystal growth in high temperature inorganic oxide, glass forming melts in microgravity. It is related to one1 of our previous NASA projects that was concerned with glass formation for high temperature containerless melts in microgravity. The previous work culminated in two experiments which were conducted aboard the space shuttle in 1983 and 1985 and which consisted of melting (at 1500 C) and cooling levitated 6 to 8 mm diameter spherical samples in a Single Axis Acoustic Levitator (SAAL) furnace. Compared to other types of materials, there have been relatively few experiments, 6 to 8, conducted on inorganic glasses in space. These experiments have been concerned with mass transport (alkali diffusion), containerless melting, critical cooling rate for glass formation, chemical homogeneity, fiber pulling, and crystallization of glass forming melts. One of the most important and consistent findings in all of these experiments has been that the glasses prepared in microgravity are more resistant to crystallization (better glass former) and more chemically homogeneous than equivalent glasses made on earth (1g). The chemical composition of the melt appears relatively unimportant since the same general results have been reported for oxide, fluoride and chalcogenide melts. These results for space-processed glasses have important implications, since glasses with a higher resistance to crystallization or higher chemical homogeneity than those attainable on earth can significantly advance applications in areas such as fiber optics communications, high power laser glasses, and other photonic devices where glasses are the key functional materials. The classical theories for nucleation and crystal growth for a glass or melt do not contain any parameter that is directly dependent upon the g-value, so it is not readily apparent why glasses prepared in microgravity should be more resistant to crystallization than equivalent glasses prepared on earth. Similarly, the gravity-driven convection in a fluid melt is believed to be the primary force field that is responsible for melt homogenization on earth. Thus, it is not obvious why a glass prepared in space, where gravity-driven convection is ideally absent, would be more chemically homogeneous than a glass identically prepared on earth. The primary objective of the present research is to obtain experimental data for the nucleation rate and crystal growth rate for a well characterized silicate melt (lithium disilicate) processed entirely in space (low gravity) and compare these rates with the nucleation and crystal growth rates for a similar glass prepared identically on earth (1g).

Day, Delbert E.↗

Kinetics of Nucleation and Crystal Growth in Glass Forming Melts in Microgravity

This flight definition project has the specific objective of investigating the kinetics of nucleation and crystal growth in high temperature inorganic oxide, glass forming melts in microgravity. It is related to one of our previous NASA projects that was concerned with glass formation for high temperature containerless melts in microgravity. The previous work culminated in two experiments which were conducted aboard the space shuttle in 1983 and 1985 and which consisted of melting (at 1500 C) and cooling levitated 6 to 8 mm diameter spherical samples in a Single Axis Acoustic Levitator (SAAL) furnace. Compared to other types of materials, there have been relatively few experiments, 6 to 8, conducted on inorganic glasses in space. These experiments have been concerned with mass transport (alkali diffusion), containerless melting, critical cooling rate for glass formation, chemical homogeneity, fiber pulling, and crystallization of glass forming melts. One of the most important and consistent findings in all of these experiments has been that the glasses prepared in microgravity are more resistant to crystallization (better glass former) and more chemically homogeneous than equivalent glasses made on Earth (1 g). The chemical composition of the melt appears relatively unimportant since the same general results have been reported for oxide, fluoride and chalcogenide melts. These results for space-processed glasses have important implications, since glasses with a higher resistance to crystallization or higher chemical homogeneity than those attainable on Earth can significantly advance applications in areas such as fiber optics communications, high power laser glasses, and other photonic devices where glasses are the key functional materials.

Day, Delbert E.↗

Kinetics of Nucleation and Crystal Growth in Glass Forming Melts in Microgravity

The following list summarizes the most important results that have been consistently reported for glass forming melts in microgravity: (1) Glass formation is enhanced for melts prepared in space; (2) Glasses prepared in microgravity are more chemically homogeneous and contain fewer and smaller chemically heterogeneous regions than identical glasses prepared on earth; (3) Heterogeneities that are deliberately introduced such as Pt particles are more uniformly distributed in a glass melted in space than in a glass melted on earth; (4) Glasses prepared in microgravity are more resistant to crystallization and have a higher mechanical strength and threshold energy for radiation damage; and (5) Glasses crystallized in space have a different microstructure, finer grains more uniformly distributed, than equivalent samples crystallized on earth. The preceding results are not only scientifically interesting, but they have considerable practical implications. These results suggest that the microgravity environment is advantageous for developing new and improved glasses and glass-ceramics that are difficult to prepare on earth. However, there is no suitable explanation at this time for why a glass melted in microgravity will be more chemically homogeneous and more resistant to crystallization than a glass melted on earth. A fundamental investigation of melt homogenization, nucleation, and crystal growth processes in glass forming melts in microgravity is important to understanding these consistently observed, but yet unexplained results. This is the objective of the present research. A lithium disilicate (Li2O.2SiO2) glass will be used for this investigation, since it is a well studied system, and the relevant thermodynamic and kinetic parameters for nucleation and crystal growth at 1-g are available. The results from this research are expected to improve our present understanding of the fundamental mechanism of nucleation and crystal growth in melts and liquids, and to lead improvements in glass processing technology on earth, with the potential for creating new high performance glasses and glass-ceramics.

Day, Delbert E.↗

Kinetics of phase transformations in glass forming systems

A nucleation rate like curve for a glass can be determined from the functional dependence of the maximum height of its DTA crystallization peak, (delta T)(sub p), on the nucleation temperature, T(sub n). This nucleation rate curve provides information for the temperature range where nucleation for the glass can occur and the temperature where the nucleation rate is a maximum. However, this curve does not provide information for the nucleation rate, I, for the glass at different temperatures. A method for estimating I at different temperatures from (delta T)(sub p) was developed using a Li2O.2SiO2 (LS2) glass. Also, the dielectric constant (epsilon) and the loss factor (tan delta) of a glass-ceramic depend, in part, upon the amount of crystallinity which, in turn, depends upon the nucleation density in the starting glass. It is therefore expected that epsilon and tan delta should have a relationship with nucleation density and hence on the nucleation rate.

Ray, Chandra S.↗

Kinetics of phase transformation in glass forming systems

The objectives of this research were to (1) develop computer models for realistic simulations of nucleation and crystal growth in glasses, which would also have the flexibility to accomodate the different variables related to sample characteristics and experimental conditions, and (2) design and perform nucleation and crystallization experiments using calorimetric measurements, such as differential scanning calorimetry (DSC) and differential thermal analysis (DTA) to verify these models. The variables related to sample characteristics mentioned in (1) above include size of the glass particles, nucleating agents, and the relative concentration of the surface and internal nuclei. A change in any of these variables changes the mode of the transformation (crystallization) kinetics. A variation in experimental conditions includes isothermal and nonisothermal DSC/DTA measurements. This research would lead to develop improved, more realistic methods for analysis of the DSC/DTA peak profiles to determine the kinetic parameters for nucleation and crystal growth as well as to assess the relative merits and demerits of the thermoanalytical models presently used to study the phase transformation in glasses.

Ray, Chandra S.↗

Kinetics of phase transformations in glass forming systems

In crystallization measurements of nonisothermal nucleation for Li2O.2SiO2 (LS2) glass, using DTA, the glass sample is scanned at different constant heating rates until it is crystallized. This means that the temperature range where nucleation can occur for the glass is scanned also at different rates which allows the glass to be nucleated for different time prior to crystallization. Consequently, the concentration of nuclei developed in the glass may be different for different heating rates and the DTA peak height which has shown to be sensitive to the number of nuclei present in the sample, is expected to change with heating rate. DTA peak height depends strongly on the overlap between the nucleation rate and growth rate curves, assuming the peak height is directly proportional to the total number of nuclei present in the glass sample under investigation, which, in turn, should be proportional to the volume or weight of the sample. To verify this assumption, DTA measurements were made using a LS2 glass to determine the peak height as a function of the sample weight. Using the DTA peak height technique, a nucleation rate like curve was determined for the BaO.2SiO2 (BS2) glass which showed that the temperature for nucleation ranged from 650 to 750 C for this glass and the temperature for maximum nucleation was approximately 705 C. These values are in excellent agreement with those determined by the conventional technique. There was international collaboration with Japan and Germany on this project.

Ray, Chandra S.↗

Use of microgravity to improve the efficiency and power output of Nd-doped laser glasses

The objectives of this research are to: (1) obtain further evidence and understand the science for the reported improvement in chemical homogeneity in glasses prepared in microgravity; and (2) study the feasibility of improving the optical and fluorescence properties, particularly, the limit for Nd(+3) concentration quenching and threshold energy for laser action for laser glasses prepared in microgravity. Attention was directed to ground based investigation whose primary purpose was to determine the suitability and conditions for processing these laser glasses in space. This report describes that the scientific and technical information required for planning flight experiments for these glasses have been obtained, and the preparation for handling and analyzing post flight samples have also been taken. Instruments required for measuring the fluorescence properties of interest have been constructed. The optical and fluorescence properties for the glasses have been measured and made available for comparative property analysis.

Ray, Chandra S.↗

Nucleation and crystallization of Na2O-2CaO-3SiO2 glass by differential thermal analysis

DTA is presently used to characterize the nucleation and crystallization processes of the Na2O-2CaO-3SiO2 glass. A nucleation rate-temperaturelike curve is obtained by plotting either the reciprocal of the temperature corresponding to the crystallization peak maximum, or the height of the crystallization peak, as a function of nucleation temperature. The nucleation-temperature range for this glass composition, 550-650 C, and the maximum nucleation temperature of 600 + or - 5 C, are found to be in excellent agreement with those associated with the classical nucleation technique, followed by isothermal crystallization. It is noted that when most of the nucleation occurs during the DTA measurements, a modified Kissinger equation must be used to calculate the crystallization energy.

Xu, Xiaojie J.↗

Crystallization kinetics of a lithia-silica glass - Effect of sample characteristics and thermal analysis measurement techniques

DTA and both isothermal and nonisothermal DSC techniques are presently used to investigate the crystallization kinetics of a 40 (mol) percent Li2O-60 percent SiO2 glass as a function of glass powder particle size, the use of either alumina or Pt as the crucible material, the use of N, O, or Ar atmospheres, and surface pretreatments of the glass powder with deionized water, HCl, or HF. Neither the furnace atmosphere nor the crucible material had a significant effect on activation energy, frequency factor, or Avrami exponent. Washings of the glass with the three different fluids decreased the crystallization temperature by 25 to 30 C.

Ray, Chandra S.↗

Glass formation and properties in the system calcia-gallia-silica

The glass-forming region in the calcia-gallia-silica system is studied and found to be fairly large, with a density of 3-4 g/cu cm, a refractive index of 1.6-1.73, an Abbe number of 35-58, a thermal expansion coefficient of 6.5-11.5 x 10 to the -7th/deg C, and a Vickers microhardness of 5.2-7.3 GPa. Crystalline phases are identified at the boundary of the glass-forming region. The structural groups in the glass-forming compositions are analyzed by infrared absorption spectroscopy.

Angel, Paul W.↗

Determining the nucleation rate curve for lithium disilicate glass by differential thermal analysis

The crystallization of lithium disilicate (Li2O+2SiO2) glass nucleated at various temperatures was studied by differential thermal analysis (DTA). A plot of the DTA crystallization peak height versus nucleation temperature closely resembles the classical nucleation rate curve for lithium disilicate glass whose maximum is at 453 C. The glass becomes saturated with internal nuclei when heated at 453 C for 10 h. The activation energy for crystallization and the heat of crystallization are independent of the concentration of nuclei and are 249 + or - 10 and 67 + or - 3 kJ/mol, respectively. The Avrami exponent, n, depends strongly on the concentration of nuclei in the glass.

Ray, Chandra S.↗