DOE OSTI2023

Enhanced laser-induced damage performance of all-glass metasurfaces for energetic pulsed laser applications

To fabricate optical components with surface layers compatible with high power laser applications that may operate as antireflective coatings, polarization rotators, or harness physical anisotropy for other uses, metasurfaces are becoming an appealing candidate. In this study, a large-beam (1.05 cm diameter) 351-nm laser-induced damage testing was done on an all-glass metasurface structure composed of cone-like features with a subwavelength spacing of adjacent features. These structures were fabricated on untreated fused silica glass and damage tested, as were structures that were fabricated on fused silica glass that experienced a preliminary etching process to remove the surface Beilby layer that is characteristic of polished fused silica. The laser-induced damage onset for structures on untreated fused silica glass was 19.3 J∙cm -2 , while the sample that saw an initial pretreatment etch exhibited an improved damage onset of 20.4 J∙cm -2 , only 6% short of the reference pretreated glass damage onset of 21.7 J∙cm -2 . For perspective, the National Ignition Facility (NIF) operational average fluence at this wavelength and pulse length is about 10 J/cm2. At a fluence of 25.5 J∙cm -2 , the reference (pretreated) fused silica initiated 5.2 damage sites per mm 2 , while the antireflective metasurface sample with a preliminary etching process treatment initiated 9.8 damage sites per mm 2 . In conclusion, these findings demonstrate that substrate-engraved metasurfaces are compatible with high energy and power laser applications, further broadening their application space.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Birefringent Glass‐Engraved Tilted Pillar Metasurfaces for High Power Laser Applications

Abstract Birefringent materials—which are highly needed in high power laser systems—may be limited in usage due to the laser‐induced damage threshold of traditional birefringent materials. This work reports here on all‐glass metasurfaces, fabricated by angled etching through sacrificial metal nanoparticle (NP) etching masks, for generation of effective birefringence in the formed layer. As a result, a fused silica metasurface, monolithic to the underlying substrate, is demonstrated to exhibit a birefringence of 6.57° under 375 nm illumination. Full‐wave analysis shows a good agreement with the measurement and presents potential paths forward to increasing the effective metasurface birefringence. This is the first demonstration, to the best of knowledge, of an etching technique to obtain the resulting tilted pillar‐like nanofeatures. The anisotropy of the metasurface nanoelements along the two window in‐plane major axes presents different effective paths for the two polarizations and thus generates birefringence in a nonbirefringent material. Additionally, the imparted anisotropy lends itself to manipulation of physical properties of the surface as well, with metasurface feature orientation suppressing water flow along one principal axis and giving rise to water flow steering capabilities.

36 MATERIALS SCIENCE↗

DOE OSTI2023

All-Glass Metasurfaces for Ultra-Broadband and Large Acceptance Angle Antireflectivity: from Ultraviolet to Mid-Infrared

For many optics technologies, such as display screens, solar cells, laser systems, and eyeglasses, antireflective (AR) coatings are well integrated; these applications frequently benefit from the ability to function as broadband AR. Here, in this work, all-glass metasurfaces are reported on, exhibiting a measured reflectance of 0.18% ± 0.23% per interface, averaged across wavelengths spanning from 350 nm (ultraviolet) to 2350 nm (mid-infrared); to the best of knowledge, this is the first-ever demonstration of an AR layer capable of this. Furthermore, acceptance angles up to 100° (angle of incidence = ±50°) results in % R < 0.6% per interface over the band 350–1300 nm for P-polarization and S-polarization, with wavelength averaged reflectance values 0.04% ± 0.05% and 0.11% ± 0.15%, respectively – another technological first. The process advancements presented here allow for reflectance suppression over a broad range of wavelengths, angles, and polarizations.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Modeling the hydrodynamic impact on the tool influence function during hemispherical subaperture optical polishing

To fabricate high-precision and accurate optics relative to the optical design surface, a high level of deterministic control of material removal (i.e., the tool influence function, TIF) during subaperture tool polishing is required. In this study, a detailed analysis of the pressure distribution, which is a key component of the TIF, has been performed using finite element analysis to couple together solid mechanics and fluid dynamics. Modeling experimental parameters of recently published work reveals that, when considering tool deformation, which in turn influences the fluid film thickness between the tool and workpiece, the effective pressure profile has a flat-top distribution. This flat-top pressure profile differs from the parabolic pressure distributions predicted by Hertzian mechanics. Furthermore, the shear contribution is shown here to be a key contributor to material removal, inducing the removal at the periphery of the contact edge and even outside the generally accepted contact area. Finally, the simulated fluid velocities provide evidence of mixed-mode contact polishing, supporting recent experimental findings that also suggest that onset of hydroplaning contributions lead to material removal drop-off.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Designer Metasurfaces for Antireflective Applications Enabled by Advanced Nanoparticle Technology

Optic processing advances have shifted system limitations, with current constraints consisting of antireflective (AR) coatings applied to optics and the inability to reduce size, weight, and price. Metasurfaces, and more broadly metaoptics, provide an avenue to overcome these limitations. The ability to generate substrate-engraved metasurfaces that can be tailored is demonstrated within a broad design space to satisfy large-area AR applications for bandpass or broadband needs, demonstrating an optically equivalent surface roughness standard deviation of only 5 Å. Using an advanced nanoparticle masking approach, two metasurfaces are fabricated: 1) vertical sidewall nanofeature metasurface (MS) for AR applications at 351 nm, and 2) sloped sidewall MS designed for broadband AR applications. For the 351 nm MS, the reflectance is measured to be 0.127%. In the case of the sloped sidewall MS, the reflectance is measured to be <0.25% over 400–700 nm and <1% over 400–1100 nm. To the best of the authors’ knowledge, this is the first demonstration of a broadband AR capable of this performance. The tunability of these structures, with a parameter space spanning even more remarkable designs such as broader bands and acceptance angles, coupled with high laser-induced damage durability and mechanical robustness, displays the strength of metasurfaces for AR applications.

36 MATERIALS SCIENCE↗

DOE OSTI2021

A semi-analytical model for laser induced densification in fused silica at elevated temperatures

A semi-analytical model for deterministic surface smoothing of fused silica below the evaporation temperature threshold is presented. Using this model, a method for calculating deterministic track depths for laser polishing fused silica is derived and validated with experiments. In this work, model predictions were in good agreement with experiment across varying laser preheating temperature and power. With the semi-analytical method presented here, deterministic laser smoothing can be achieved in the densification regime to close the process loop of laser polishing.

36 MATERIALS SCIENCE↗