Engineering topics
Publications and source records attributed to Reale Batista, Mariana Desireé.
An infrared transparent foam made from inexpensive salts was developed enabling sub-ambient cooling of underlying surfaces for a full 24 hour cycle. This work showcases how non-convetional materials may be used for passive day-time radiative cooling.
Supercapacitors exhibit fast charging/discharging ability and have attracted considerable attention within the automotive, aerospace, and telecommunication industries. Porous carbons, prized for their high electrical conductivity and high surface area, have been attractive candidates for supercapacitor electrodes. Moving to thick electrodes is one strategy to further increase energy density due to a higher volume fraction of active material. However, thick electrodes suffer from sluggish charged species transport, which is why thin electrodes are currently favored. In this work, we investigate the use of computational optimization and additive manufacturing to design and fabricate thick porous electrodes with improved performance. Electrode performance was maximized by designing their morphologies via topology optimization and printing by projection micro stereolithography (PμSL) using commercial resin (PR48). The PR48 resin was then pyrolyzed (PR48-P) to create the final conductive electrode. The optimized PR48-P electrodes exhibited 99% improvement in capacitance compared to control electrodes printed with cubic lattice morphologies. To further improve performance, we formulated a resin combining graphene oxide (GO) and trimethylolpropane triacrylate (TMPTA). Electrodes printed with 3 wt% GO in TMPTA exhibited improved capacitance retention after pyrolysis compared to the PR48-P electrodes. Finally, this work demonstrates the benefits of using topology optimization to design electrodes and material development to improve functional properties of 3D printable electrodes.
Bamboo fibers (BFs) have high mechanical properties and are candidate reinforcement for epoxy matrix composites. However, to improve performance, good fiber-matrix interaction is required. In this work, unidirectional long BF reinforced epoxy composites at fiber volume content of 22%, 40%, and 50% were made by compression molding. The 40 v% untreated BF reinforced composites exhibited 107% and 439% increase for flexural strength and modulus, respectively, compared to neat epoxy. Sodium hydroxide (NaOH) treatment was used to modify the surface of the BFs, and then the NaOH modified BFs were coated with graphene oxide (GO). The 40 v% NaOH modified BF composites showed an improvement from 259.9 to 327.5 MPa for flexural strength and from 16.7 to 21.5 GPa for flexural modulus, compared to 40 v% untreated BF composites. Slight improvement in properties up to 334.6 MPa for flexural strength and up to 23.8 GPa for flexural modulus was achieved for composites made of 40 v% NaOH/GO modified BF. Surface modification of BF after the NaOH and NaOH/GO treatment was confirmed by X-ray photoelectron spectroscopy and by scanning electron microscopy, which showed differences on the fiber surface morphology and on the composite fracture surface. This BF surface modification approach with GO has potential to impart other properties beyond mechanical to produce multifunctional composite and lead to the use of sustainable plant fibers as alternatives to synthetic fibers.