Impact of impurity-based phonon resonant scattering on thermal conductivity of single crystalline GaN
The impact of impurities on the thermal conductivity of halide vapor phase epitaxy gallium nitride (GaN) was studied. Phonon resonances with impurities, modeled as Lorentz oscillators, were used to explain the much lower thermal conductivity than predicted by the Debye–Callaway model. The resonance energies for the oscillators were determined by Raman spectroscopy for Mn and by mass difference approximation for C and Fe. Employing the obtained resonance energies and proportionality factors extracted as fitting parameters, the modified model showed a good agreement with the experimental data. While the doping decreased thermal conductivity for all temperatures, the room temperature values started decreasing significantly once the doping levels approached ~10 19 cm -3 . Consequently, required doping levels to achieve certain GaN-based devices may reduce the thermal conductivity of GaN by as much as 1/3.
Chemical treatment effects on Schottky contacts to metalorganic chemical vapor deposited n-type N-polar GaN
In this article, we investigate the effect of different chemical treatments, such as solvents, bases, and acids, on the surface properties and electrical behavior of Schottky diodes fabricated on metalorganic chemical vapor deposition-grown, n-type, N-polar GaN. The I–V and C–V barrier heights of the as-grown Schottky diodes are found to be 0.40 eV and 0.60 eV, respectively, with an ideality factor n = 1.07. It is found that the solvent treatments neither change the surface nor the electrical performance of the Schottky diodes, as expected. However, the treatments by the alkaline photolithography developer and acid—the latter of which is often used to clean the surface of Ga-polar GaN films prior to metal contact deposition—degrade the performance of N-polar GaN. These base and acid treatments severely roughen the surface by creating triangular/hexagonal crystallographic facets. The I–V and C–V barrier heights of these base- and acid-treated diodes are increased to 0.63 eV and 1.00 eV, respectively, with ideality factor values n < 1.2. X-ray photoelectron spectroscopy studies indicate that base- and acid-treated surfaces have lower oxygen content as compared to the as-grown sample surface. It is understood that the increment in the barrier height for base- and acid-treated diodes could be due to the change in polarity, from N-polar to semi-polar/non-polar, on these crystallographic features. All these results demonstrate that, unlike for Ga-polar GaN, the N-polar GaN surface is highly reactive to bases and acids.