Predicted High-Pressure Hot Superconductivity in Li 2 CaH 16 and Li 2 CaH 17 Phases that Resemble the Type-II Clathrate Structure
High-temperature high-pressure superconducting hydrides are typically characterized by cage-like hydrogenic lattices filled with electropositive metal atoms. Here, density functional theory based evolutionary crystal structure searches find two phases that possess these geometric features and are related to the Type-II clathrate structure. In these Fd$\overline{3}$m Li 2 CaH 16 and R$\overline{3}$m Li 2 CaH 17 phases the calcium atom occupies the larger cage and the lithium atom the smaller one. The highest superconducting critical temperatures predicted within the isotropic Eliashberg formalism, 330 K at 350 GPa for Fd$\overline{3}$m Li 2 CaH 16 and 370 K at 300 GPa for R$\overline{3}$m Li 2 CaH 17 , suggest these structures are another example of hot superconducting hydrides. As pressure is lowered the cage-like lattices distort with the emergence of quasimolecular hydrogenic motifs; nonetheless Li 2 CaH 17 is predicted to be superconducting down to 160 GPa at 205 K.