Reece, C. E. | Search NASA

DOE OSTI2024

Oxide dissolution and oxygen diffusion scenarios in niobium and implications on the Bean–Livingston barrier in superconducting cavities

We generalize a native Nb 2 O 5 dissolution model [G. Ciovati, Appl. Phys. Lett. 89, 022507 (2006)] to sequential overlayer dissolutions, multilayer dissolution, and realistic temperature profiles, which may be applicable to other materials. The model is applied to secondary ion mass spectrometry depth profile measurements for varying temperature profiles and two-step oxide dissolution in Nb and found to agree well. In the context of the Meissner screening response due to impurity profiles on the length scale of the London penetration depth, the shallow diffusion of O impurities results in a substantial decrease in the peak supercurrent density near the surface. In this framework, oxide dissolution and oxygen diffusion can account for a rise in peak supportable magnetic field in SRF cavities with baking time and a suppression after the optimal baking time is reached, in good agreement with peak-field baking temperatures and times as well as recent quench field measurements.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2022

SIMS Investigation of Furnace-Baked Nb

Results recently published by Ito et al. showed that "furnace baking" Nb SRF cavities after electropolishing yields high quality factors and anti-Q-slopes resembling that of N doped cavities. Small Nb samples were prepared following the recipe outlined by Ito. These samples were measured by SIMS to examine impurity contributions to the RF penetration layer. These diffusion profiles are modeled, and their consequences on RF properties discussed.

Lechner, E. M.↗

DOE OSTI2022

Status of the LCLS-II-HE Project at Jefferson Lab

The Linac Coherent Light Source II High Energy (LCLS-II-HE) upgrade at the SLAC National Accelerator Laboratory is being constructed in partnership with the Thomas Jefferson National Accelerator Facility (JLab) and the Fermi National Accelerator Laboratory (FNAL). The cryomodule production scope consists of the design, procurement, construction, and acceptance testing of 24 eight-cavity, 1.3 GHz cryomodules, as well as R&D activities necessary to develop the required technology. To achieve this, JLab and FNAL are also contributing to SLAC’s effort to develop the cavity recipe and production processes necessary to meet the LCLS-II-HE goal of 20.8 MV/m and average Q₀ of 2.7·10¹⁰. This paper details the JLab scope, focusing on the project initiation phase, in particular technology development and prototyping, project development and planning, and implementation of lessons learned from LCLS-II.

Wilson, K. M.↗

DOE OSTI2022

Nb3Sn Coating of Twin Axis Cavity for SRF Applications

The twin axis cavity with two identical accelerating beams has been proposed for Energy recovery linac (ERL) applications. Nb3Sn is a superconducting material with a higher critical temperature and a higher critical field as compared to Nb, which promises a lower operating cost due to higher quality factors. Two niobium twin axis cavities fabricated at JLab and were proposed to be coated with Nb3Sn. Due to their more complex geometry, the typical coating process used for basic elliptical cavities needs to be improved to coat these cavities. This devel-opment advances the current coating system at JLab for coating complex cavities. Two twin axis cavities were coated recently for the first time. This contribution dis-cusses initial results from coating of twin axis cavities, RF testing and witness sample analysis with an overview of the current challenges towards high performance Nb3Sn coated twin axis cavities.

Tiskumara, J.↗

DOE OSTI2022

Nb$_3$Sn Superconducting Radiofrequency Cavities: a Maturing Technology for Particle Accelerators and Detectors

Nb3Sn superconducting radiofrequency (SRF) cavities have substantial potential for enabling new performance capabilities for particle accelerators for high energy physics (HEP), as well as for RF cavity-based detectors for dark matter, gravitational waves, and other quantum sensing applications. Outside of HEP, Nb3Sn SRF cavities can also benefit accelerators for nuclear physics, basic energy sciences, and the industry. In this contribution to Snowmass 2021, we overview the potential, status, and outlook of Nb3Sn SRF cavities.

43 PARTICLE ACCELERATORS↗

DOE OSTI2022

New Improved Horizontal Electropolishing System for SRF Cavities

The best performance of niobium SRF accelerating cavities is obtained with surfaces smoothed with electropolishing chemical finishing. Jefferson Lab has recently specified, procured, installed, and commissioned a new versatile production electropolishing (EP) tool. Experience with EP research and operations at JLab as well as vendor interactions and experience guided development of the system specification. Detailed design and fabrication was awarded by contract to Semiconductor Process Equipment Corporation (SPEC). The delivered system was integrated into the JLab chemroom infrastructure and commissioned in 2020. The new EP tool provides much improved heat exchange from the circulating H₂SO₄/HF electrolyte and also the cavity via variable temperature external cooling water flow, resulting in quite uniform cavity wall temperature control and thus improved removal uniformity. With the JLab infrastructure, stabilized process temperature as low as 5 C is available. We describe the system and illustrate operational modes in this contribution.

Reece, C. E.↗

DOE OSTI2022

Managing Sn-Supply to Tune Surface Characteristics of Vapor-Diffusion Coating of Nb₃Sn

Nb₃Sn promises better RF performance (Q and E_{acc}) than niobium at any given temperature because of superior superconducting properties. Nb₃Sn-coated SRF cavities are now produced routinely by growing a few microns thick Nb₃Sn films inside Nb cavities via the tin vapor diffusion technique. Sn evaporation and consumption during the growth process notably affect the quality of the coating. Aiming at favorable surface characteristics that could enhance the RF performance, many coatings were produced by varying Sn sources and temperature profiles. Coupon samples were examined using different material characterization techniques, and a selected few sets of coating parameters were used to coat 1.3 GHz single-cell cavities for RF testing. The Sn supply’s careful tuning is essential to manage the microstructure, roughness, and overall surface characteristics of the coating. We summarize the material analysis of witness samples and discuss the performance of several Nb₃Sn-coated single-cell cavities linked to Sn-source characteristics and observed Sn consumption during the film growth process.

Pudasaini, U.↗

DOE OSTI2021

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

Recently, Nb superconducting radio frequency cavities vacuum heat treated between 300 and 400°C for a few hours have exhibited very high quality factors (~5 × 10 10 at 2.0 K). Secondary ion mass spectrometry measurements of O, N, and C show that this enhancement in RF surface conductivity is primarily associated with interstitial O alloying via dissolution and diffusion of the native oxide. We use a theory of oxide decomposition and O diffusion to quantify previously unknown parameters crucial in modeling this process. RF measurements of a vacuum heat-treated Nb superconducting radio frequency cavity confirm the minimized surface resistance (higher Q 0 ) previously expected only from 800 °C diffusive alloying with N.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2021

Managing Sn-supply to tune surface characteristics of vapor-diffusion coating of Nb3Sn

Nb₃Sn promises better RF performance (Q and E_{acc}) than niobium at any given temperature because of superior superconducting properties. Nb₃Sn-coated SRF cavities are now produced routinely by growing a few microns thick Nb₃Sn films inside Nb cavities via the tin vapor diffusion technique. Sn evaporation and consumption during the growth process notably affect the quality of the coating. Aiming at favorable surface characteristics that could enhance the RF performance, many coatings were produced by varying Sn sources and temperature profiles. Coupon samples were examined using different material characterization techniques, and a selected few sets of coating parameters were used to coat 1.3 GHz single-cell cavities for RF testing. The Sn supply’s careful tuning is essential to manage the microstructure, roughness, and overall surface characteristics of the coating. We summarize the material analysis of witness samples and discuss the performance of several Nb₃Sn-coated single-cell cavities linked to Sn-source characteristics and observed Sn consumption during the film growth process.

Pudasaini, U.↗

DOE OSTI2021

SIMS Investigation of Furnace-Baked Nb

Results recently published by Ito et al. showed that "furnace baking" Nb SRF cavities after electropolishing yields high quality factors and anti-Q-slopes resembling that of N doped cavities. Small Nb samples were prepared following the recipe outlined by Ito. These samples were measured by SIMS to examine impurity contributions to the RF penetration layer. These diffusion profiles are modeled, and their consequences on RF properties discussed.

Lechner, E. M.↗