Engineering topics

Reeder, James R.

Publications and source records attributed to Reeder, James R..

At least 19 records

NASA NTRS2014

The Inclusion of Arbitrary Load Histories in the Strength Decay Model for Stress Rupture

Stress rupture is a failure mechanism where failures can occur after a period of time, even though the material has seen no increase in load. Carbon/epoxy composite materials have demonstrated the stress rupture failure mechanism. In a previous work, a model was proposed for stress rupture of composite overwrap pressure vessels (COPVs) and similar composite structures based on strength degradation. However, the original model was limited to constant load periods (holds) at constant load. The model was expanded in this paper to address arbitrary loading histories and specifically the inclusions of ramp loadings up to holds and back down. The broadening of the model allows for failures on loading to be treated as any other failure that may occur during testing instead of having to be treated as a special case. The inclusion of ramps can also influence the length of the "safe period" following proof loading that was previously predicted by the model. No stress rupture failures are predicted in a safe period because time is required for strength to decay from above the proof level to the lower level of loading. Although the model can predict failures during the ramp periods, no closed-form solution for the failure times could be derived. Therefore, two suggested solution techniques were proposed. Finally, the model was used to design an experiment that could detect the difference between the strength decay model and a commonly used model for stress rupture. Although these types of models are necessary to help guide experiments for stress rupture, only experimental evidence will determine how well the model may predict actual material response. If the model can be shown to be accurate, current proof loading requirements may result in predicted safe periods as long as 10(13) years. COPVs design requirements for stress rupture may then be relaxed, allowing more efficient designs, while still maintaining an acceptable level of safety.

Reeder, James R.↗

NASA NTRS2012

Composite Stress Rupture: A New Reliability Model Based on Strength Decay

A model is proposed to estimate reliability for stress rupture of composite overwrap pressure vessels (COPVs) and similar composite structures. This new reliability model is generated by assuming a strength degradation (or decay) over time. The model suggests that most of the strength decay occurs late in life. The strength decay model will be shown to predict a response similar to that predicted by a traditional reliability model for stress rupture based on tests at a single stress level. In addition, the model predicts that even though there is strength decay due to proof loading, a significant overall increase in reliability is gained by eliminating any weak vessels, which would fail early. The model predicts that there should be significant periods of safe life following proof loading, because time is required for the strength to decay from the proof stress level to the subsequent loading level. Suggestions for testing the strength decay reliability model have been made. If the strength decay reliability model predictions are shown through testing to be accurate, COPVs may be designed to carry a higher level of stress than is currently allowed, which will enable the production of lighter structures

Reeder, James R.↗

NASA NTRS2010

A Critique of a Phenomenological Fiber Breakage Model for Stress Rupture of Composite Materials

Stress rupture is not a critical failure mode for most composite structures, but there are a few applications where it can be critical. One application where stress rupture can be a critical design issue is in Composite Overwrapped Pressure Vessels (COPV's), where the composite material is highly and uniformly loaded for long periods of time and where very high reliability is required. COPV's are normally required to be proof loaded before being put into service to insure strength, but it is feared that the proof load may cause damage that reduces the stress rupture reliability. Recently, a fiber breakage model was proposed specifically to estimate a reduced reliability due to proof loading. The fiber breakage model attempts to model physics believed to occur at the microscopic scale, but validation of the model has not occurred. In this paper, the fiber breakage model is re-derived while highlighting assumptions that were made during the derivation. Some of the assumptions are examined to assess their effect on the final predicted reliability.

Reeder, James R.↗

NASA NTRS2006

User-Defined Material Model for Progressive Failure Analysis

An overview of different types of composite material system architectures and a brief review of progressive failure material modeling methods used for structural analysis including failure initiation and material degradation are presented. Different failure initiation criteria and material degradation models are described that define progressive failure formulations. These progressive failure formulations are implemented in a user-defined material model (or UMAT) for use with the ABAQUS/Standard1 nonlinear finite element analysis tool. The failure initiation criteria include the maximum stress criteria, maximum strain criteria, the Tsai-Wu failure polynomial, and the Hashin criteria. The material degradation model is based on the ply-discounting approach where the local material constitutive coefficients are degraded. Applications and extensions of the progressive failure analysis material model address two-dimensional plate and shell finite elements and three-dimensional solid finite elements. Implementation details and use of the UMAT subroutine are described in the present paper. Parametric studies for composite structures are discussed to illustrate the features of the progressive failure modeling methods that have been implemented.

Knight, Norman F. Jr.↗

NASA NTRS2006

3-D Mixed Mode Delamination Fracture Criteria - An Experimentalist's Perspective

Many delamination failure criteria based on fracture toughness have been suggested over the past few decades, but most only covered the region containing mode I and mode II components of loading because that is where toughness data existed. With new analysis tools, more 3D analyses are being conducted that capture a mode III component of loading. This has increased the need for a fracture criterion that incorporates mode III loading. The introduction of a pure mode III fracture toughness test has also produced data on which to base a full 3D fracture criterion. In this paper, a new framework for visualizing 3D fracture criteria is introduced. The common 2D power law fracture criterion was evaluated to produce unexpected predictions with the introduction of mode III and did not perform well in the critical high mode I region. Another 2D criterion that has been shown to model a wide range of materials well was used as the basis for a new 3D criterion. The new criterion is based on assumptions that the relationship between mode I and mode III toughness is similar to the relation between mode I and mode II and that a linear interpolation can be used between mode II and mode III. Until mixed-mode data exists with a mode III component of loading, 3D fracture criteria cannot be properly evaluated, but these assumptions seem reasonable.

Reeder, James R.↗

NASA NTRS2005

Fractographic Examination of the Vertical Stabilizer and Rudder from American Airlines Flight 587

The first major structural component failure of a composite part on a commercial airplane occurred during the crash of American Airlines Flight 587. The fractured composite lugs that attached the vertical stabilizer to the aircraft tail and the fractured composite honeycomb rudder were examined as part of the National Transportation Safety Board investigation of the accident. In this paper the composite fractures are described and the resulting clues to the failure events are discussed.

Fox, Matthew R.↗

NASA NTRS2005

Materials Examination of the Vertical Stabilizer from American Airlines Flight 587

The first in-flight failure of a primary structural component made from composite material on a commercial airplane led to the crash of American Airlines Flight 587. As part of the National Transportation Safety Board investigation of the accident, the composite materials of the vertical stabilizer were tested, microstructure was analyzed, and fractured composite lugs that attached the vertical stabilizer to the aircraft tail were examined. In this paper the materials testing and analysis is presented, composite fractures are described, and the resulting clues to the failure events are discussed.

Fox, Matthew R.↗

NASA NTRS2002

Prediction of Long-Term Strength of Thermoplastic Composites Using Time-Temperature Superposition

Accelerated tests for composite failure were investigated. Constant ramp transverse strength tests on thermoplastic composite specimens were conducted at four temperatures from 300 F to 450 F and five duration times from 0.5 sec to 24 hrs. Up to 400 F, the time-temperature-superposition method produces a master curve allowing strength at longer times to be estimated from strength tests conducted over shorter times but at higher temperatures. The shift factors derived from compliance tests applied well to the strength data. To explain why strength behaved similar to compliance, a viscoelastic fracture model was investigated based on the hypothesis that the work of fracture for crack initiation at some critical flaw remains constant with time and temperature. The model, which used compliance as input, was found to fit the strength data only if the critical fracture energy was allowed to vary with stress rate. Fracture tests using double cantilever beam specimens were conducted from 300 F to 450 F over time scales similar to the strength study. The toughness data showed a significant change with loading rate, less variation with temperature, did not form a master curve, and could not be correlated with the fracture model. Since the fracture model did not fit the fracture data, an alternative explanation based on the dilatational strain energy density was proposed. However the usefulness of this model is severely limited because it relies on a critical parameter which varies with loading rate.

Reeder, James R.↗

NASA NTRS2002

A Criterion to Control Nonlinear Error in the Mixed-Mode Bending Test

The mixed-mode bending test ha: been widely used to measure delamination toughness and was recently standardized by ASTM as Standard Test Method D6671-01. This simple test is a combination of the standard Mode I (opening) test and a Mode II (sliding) test. This test uses a unidirectional composite test specimen with an artificial delamination subjected to bending loads to characterize when a delamination will extend. When the displacements become large, the linear theory used to analyze the results of the test yields errors in the calcu1ated toughness values. The current standard places no limit on the specimen loading and therefore test data can be created using the standard that are significantly in error. A method of limiting the error that can be incurred in the calculated toughness values is needed. In this paper, nonlinear models of the MMB test are refined. One of the nonlinear models is then used to develop a simple criterion for prescribing conditions where thc nonlinear error will remain below 5%.

Reeder, James R.↗

NASA NTRS2002

Postbuckling and Growth of Delaminations in Composite Plates Subjected to Axial Compression

The postbuckling response and growth of circular delaminations in flat and curved plates are investigated as part of a study to identify the criticality of delamination locations through the laminate thickness. The experimental results from tests on delaminated plates are compared with finite element analysis results generated using shell models. The analytical prediction of delamination growth is obtained by assessing the strain energy release rate results from the finite element model and comparing them to a mixed-mode fracture toughness failure criterion. The analytical results for onset of delamination growth compare well with experimental results generated using a 3-dimensional displacement visualization system. The record of delamination progression measured in this study has resulted in a fully 3-dimensional test case with which progressive failure models can be validated.

Reeder, James R.↗

NASA NTRS2002

The Use of Doublers in Delamination Toughness Testing

In this paper, the data reduction equations for common delamination toughness tests are rederived for use with specimens which have bonded doublers. The common toughness tests considered here are the double cantilever beam (DCB) for mode I toughness; the end notch flexure (3ENF) and 4 point ENF (4ENF) for mode II toughness; and the mixed mode bending (MMB) test for testing under combined mode I and mode II loading. Because the addition of the doublers changes the bending stiffness of the specimens, these data reduction equations may need to be corrected. Doublers were added to the delamination test specimens to solve a premature failure problem. Delamination toughness is normally tested using a beam with an imbedded insert so that one end of the specimen is split into two arms. If the specimen is too thin, or if the toughness of the material is too high, an arm of the specimen may fail in bending before the delamination grows. When this occurs, the toughness of the material cannot be determined. To delay the bending failure so that delamination growth occurs, doubler plates were bonded to both top and bottom surfaces of the specimen. A doubler parameter, beta, which describes how much the use of doubler plates changed the ratio of full thickness to delaminated bending stiffnesses, was defined. When changes to the data reduction equations were required, the changes were minor when written in terms of the beta parameter. The doubler plate technique was demonstrated by measuring the mixed-mode fracture toughness of a carbon-carbon composite using test specimens which would otherwise have failed before delamination growth occurred. The doubler plate technique may solve several problems that can be encountered when testing delamination fracture toughness.

Reeder, James R.↗

NASA NTRS2001

Crack Turning Mechanics of Composite Wing Skin Panels

The safety of future composite wing skin integral stiffener panels requires a full understanding of failure mechanisms of these damage tolerance critical structures under both in-plane and bending loads. Of primary interest is to derive mathematical models using fracture mechanics in anisotropic cracked plate structures, to assess the crack turning mechanisms, and thereby to enhance the residual strength in the integral stiffener composite structures. The use of fracture mechanics to assess the failure behavior in a cracked structure requires the identification of critical fracture parameters which govern the severity of stress and deformation field ahead of the flaw, and which can be evaluated using information obtained from the flaw tip. In the three-year grant, the crack-tip fields under plane deformation, crack-tip fields for anisotropic plates and anisotropic shells have been obtained. In addition, methods for determining the stress intensity factors, energy release rate, and the T-stresses have been proposed and verified. The research accomplishments can be summarized as follows: (1) Under plane deformation in anisotropic solids, the asymptotic crack-tip fields have been obtained using Stroh formalism; (2) The T-stress and the coefficient of the second term for sigma(sub y), g(sub 32), have been obtained using path-independent integral, the J-integral and Betti's reciprocal theorem together with auxiliary fields; (3) With experimental data performed by NASA, analyses indicated that the mode-I critical stress intensity factor K(sub Q) provides a satisfactory characterization of fracture initiation for a given laminate thickness, provided the failure is fiber-dominated and crack extends in a self-similar manner; (4) The high constraint specimens, especially for CT specimens, due to large T-stress and large magnitude of negative g(sub 32) term may be expected to inhibit the crack extension in the same plane and promote crack turning; (5) Crack turning out of crack plane in generally anisotropic solids under plane deformation has been studied; (6) The role of T-stress and the higher-order term of sigma(sub y) on the crack turning and stability of the kinked crack has been quantified; (7) Asymptotic crack-tip fields including the effect of transverse shear deformation (Reissner plate theory) in an anisotropic plate under bending, twisting moments, and transverse shear loads has been presented; (8) The expression of the path-independent J-integral in terms of the generalized stress and strain has been derived; (9) Asymptotic crack-tip fields including the effect of transverse shear deformation (Reissner shallow shell theory) in a general anisotropic shell has been developed; (10) The Stroh formalism was used to characterize the crack tip fields in shells up to the second term and the energy release rate was expressed in a very compact form.

Yuan, F. G.↗

NASA NTRS2001

Development and Evaluation of Stitched Sandwich Panels

This study explored the feasibility and potential benefits provided by the addition of through-the-thickness reinforcement to sandwich structures. Through-the-thickness stitching is proposed to increase the interlaminar strength and damage tolerance of composite sandwich structures. A low-cost, out-of-autoclave processing method was developed to produce composite sandwich panels with carbon fiber face sheets, a closed-cell foam core, and through-the-thickness Kevlar stitching. The sandwich panels were stitched in a dry preform state, vacuum bagged, and infiltrated using Vacuum Assisted Resin Transfer Molding (VARTM) processing. For comparison purposes, unstitched sandwich panels were produced using the same materials and manufacturing methodology. Test panels were produced initially at the University of Utah and later at NASA Langley Research Center. Four types of mechanical tests were performed: flexural testing, flatwise tensile testing, core shear testing, and edgewise compression testing. Drop-weight impact testing followed by specimen sectioning was performed to characterize the damage resistance of stitched sandwich panels. Compression after impact (CAI) testing was performed to evaluate the damage tolerance of the sandwich panels. Results show significant increases in the flexural stiffness and strength, out-of-plane tensile strength, core shear strength, edgewise compression strength, and compression-after-impact strength of stitched sandwich structures.

Stanley, Larry E.↗

NASA NTRS2001

Fracture Behavior of a Stitched Warp-Knit Carbon Fabric Composite

Tests were conducted on several types of fracture specimens made from a carbon/epoxy composite. The composite material was stitched prior to introducing epoxy resin. Boeing, used this material to develop a composite wing box for a transport aircraft in the NASA Advanced Composites Transport Program. The specimens included compact, extended compact, and center notched tension specimens. The specimens were cut from panels with three orientations in order to explore the effects of anisotropy. The panels were made with various thicknesses to represent a wing, skin from tip to root. All fractures were not self-similar depending on specimen type and orientation. Unnotched tension specimens were also tested to measure elastic constants and strengths. The normal and shear strains were calculated on fracture planes using a series representation of strain fields for plane anisotropic crack problems. The fracture parameters were determined using a finite element method. Characteristic distances for critical tension and shear strains were calculated for each specimen and a failure criterion based on the interaction of tension and shear strains was proposed.

Poe, Clarence C., Jr.↗

NASA NTRS2000

Refinements to the Mixed-Mode Bending Test for Delamination Toughness

The mixed-mode bending (MMB) test for delamination toughness was first introduced in 1988. This simple test is a combination of the standard Mode I (opening) test and a Mode II (sliding) test. This MMB test has become widely used in the United States and around the world for mixed-mode toughness measurements. Because of the widespread use of this test method, it is being considered for standardization by ASTM Committee D30. This paper discusses several improvements to the original test method. The improvements to the MMB test procedure include an improved method for calculating toughness from the measured test quantities, a more accurate way of setting the mixed-mode ratio to be tested, and the inclusion of a new alignment criterion for improved consistency in measured values.

Reeder, James R.↗

NASA NTRS1995

Comparison of the Compressive Strengths for Stitched and Toughened Composite Systems

The compression strength of a stitched and a toughened matrix graphite/epoxy composite was determined and compared to a baseline unstitched untoughened composite. Two different layups with a variety of test lengths were tested under both ambient and hot/wet conditions. No significant difference in strength was seen for the different materials when the gage lengths of the specimens were long enough to lead to a buckling failure. For shorter specimens, a 30% reduction in strength from the baseline was seen due to stitching for both a 48-ply quasi-isotropic and a (0/45/0/-45/90/-45/0/45/0)s laminate. Analysis of the results suggested that the decrease in strength was due to increased fiber misalignment due to the stitches. An observed increasing strength with decreasing gage length, which was seen for all materials, was explained with a size effect model. The model assumed a random distribution of flaws (misaligned fibers). The toughened material showed a small increase in strength over the baseline material for both laminates presumably due to the compensating effects of a more compliant matrix and straighter fibers in the toughened material. The hot/wet strength of the stitched and baseline material fell 30% below their ambient strengths for shorter, non-buckling specimen, while the strength of the toughened matrix material only fell 20%. Video images of the failing specimen were recorded and showed local failures prior to global collapse of the specimen. These images support the theory of a random distribution of flaws controlling composite failure. Failed specimen appearance however, seems to be a misleading indication of the cause of failure.

Reeder, James R.↗

NASA NTRS1994

Comparison of the compressive strengths for stitched and toughened composite systems

The compression strength of a stitched and a toughened matrix graphite/epoxy composite was determined and compared to a baseline unstitched untoughened composite. Two different layups with a variety of test lengths were tested under both ambient and hot/wet conditions. No significant difference in strength was seen for the different materials when the gage lengths of the specimens were long enough to lead to a buckling failure. For shorter specimens, a 30 percent reduction in strength from the baseline was seen due to stitching for both a 48-ply quasi-isotropic and a (0/45/0/-45/90/-45/0/45/0)s laminate. Analysis of the results suggested that the decrease in strength was due to increased fiber misalignment due to the stitches. An observed increasing strength with decreasing gage length, which was seen for all materials, was explained with a size effect model. The model assumed a random distribution of flaws (misaligned fibers). The toughened materials showed a small increase in strength over the baseline material for both laminates presumably due to the compensating effects of a more compliant matrix and straighter fibers in the toughened material. The hot/wet strength of the stitched and baseline material fell 30 percent below their ambient strengths for shorter, nonbuckling specimen, while the strength of the toughened matrix material only fell 20 percent. Video images of the failing specimen were recorded and showed local failures prior to global collapse of the specimen. These images support the theory of a random distribution of flaws controlling composite failure. Failed specimen appearance, however, seems to be a misleading indication of the cause of failure.

Reeder, James R.↗

NASA NTRS1993

A bilinear failure criterion for mixed-mode delamination

Many different failure criteria have been suggested for mixed-mode delamination toughness, but few sets of mixed-mode data exist that are consistent over the full range of Mode 1 opening load to Mode 2 shear load range. The mixed-mode bending (MMB) test was used to measure the delamination toughness of a brittle epoxy composite, a state-of-the-art toughened epoxy composite, and a tough thermoplastic composite over the full mixed-mode range. To gain insight into the different failure responses of the different materials, the delamination fracture surfaces were also examined. An evaluation of several failure criteria that have been reported in the literature was performed, and the range of responses modeled by each criterion was analyzed. A bilinear failure criterion was introduced based on a change in the failure mechanism observed from the delamination surfaces. The different criteria were compared to the failure response of the three materials tested. The responses of the two epoxies were best modeled with the new bilinear failure criterion. The failure response of the tough thermoplastic composite could be modeled well with the bilinear criterion but could also be modeled with the more simple linear failure criterion. Since the materials differed in their mixed-mode failure response, mixed-mode delamination testing will be needed to characterize a composite material. This paper presents consistent sets of mixed-mode data, provides a critical evaluation of the mixed-mode failure criteria, and should provide general guidance for selecting an appropriate criterion for other materials.

Reeder, James R.↗