On plasticity-enhanced interfacial toughness in bonded joints
Here, the performance and reliability of many structures and components depend on the integrity of interfaces between dissimilar materials. Interfacial toughness Γ is the key material parameter that characterizes resistance to interfacial crack growth, and Γ is known to depend on many factors including temperature. For example, previous work showed that the toughness of an epoxy/aluminum interface decreased 40 % as the test temperature was increased from -60 °C to room temperature (RT). Interfacial integrity at elevated temperatures is of considerable practical importance. Recent measurements show that instead of continuing to decrease with increasing temperature, Γ increases when test temperature is above RT. Cohesive zone finite element calculations of an adhesively bonded, asymmetric double cantilever beam specimen of the type used to measure Γ suggest that this increase in toughness may be a result of R-curve behavior generated by plasticity-enhanced toughening during stable subcritical crack growth with interfacial toughness defined as the critical steady-state limit value. In these calculations, which used an elastic-perfectly plastic epoxy model with a temperature-dependent yield strength, the plasticity-enhanced increase in Γ above its intrinsic value Γ o depended on the ratio of interfacial strength σ* to the yield strength σyb of the bond material. There is a nonlinear relationship between Γ/Γ o and σ*/σ yb with the value Γ/Γ o increasing rapidly above a threshold value of σ*/σ yb . The predicted increase in toughness can be significant. For example, there is nearly a factor of two predicted increase in Γ/Γ o during micrometer-scale crack-growth when σ*/σ yb = 2 (a reasonable choice for σ*/σ yb ). Furthermore, contrary to other reported results, plasticity-enhanced toughening can occur prior to crack advance as the cohesive zone forms and the peak stress at the tip of the original crack tip translates to the tip of the fully formed cohesive zone. These results suggest that plasticity-enhanced toughening should be considered when modeling interfaces at elevated temperatures.