Impact of carrier wafer on etch rate, selectivity, morphology, and passivation during GaN plasma etching
The choice of carrier wafer was found to significantly influence etch rates, selectivity, and morphology in GaN micropillar etching in a Cl 2 -Ar high-density inductively coupled plasma. 7 × 7 mm 2 GaN on sapphire chips with a plasma-enhanced chemical vapor deposition SiO 2 hard mask was etched on top of 4-in. fused silica, silicon carbide, silicon, sapphire, aluminum nitride, and high purity aluminum carriers. Silicon and silicon carbide carriers reduced GaN:SiO 2 selectivity because incidental SiCl x and CCl x etch products from the carriers attack the SiO 2 mask. Aluminum nitride and high-purity aluminum carriers yielded the highest GaN:SiO 2 selectivities due to the deposition of Al-based etched by-products, while the highest GaN etch rate was achieved using the sapphire carrier since it was the most inert carrier and did not sink any Cl 2 . Overall, results indicate that SiO 2 and Al may be used as passivation materials during GaN etching, as vertical profiles were achieved when SiO 2 or Al is redeposited from the fused silica and aluminum carriers, respectively. Floor pitting, trenching, sidewall roughness, and faceting were all influenced by carrier wafer type and will be discussed.