Direct Feed High-Level Waste APPS Model Glass Testing (DFHLW APPS) Matrix

This report summarizes the data collected during the batching and melting of the Direct Feed High-Level Waste APPS Model Glass Matrix (DFHLW APPS) to serve as a quality-assured validation of the Aspen Process Performance Simulation (APPS) formulation method. Of 15 glasses tested, 12 satisfied all target property constraints. Two glasses, APPS-05 and -06, formed nepheline on canister centerline cooling heat-treatment and failed the Product Consistency Test response limits. Glass APPS-07-2 formed unacceptably high concentrations of crystals (primarily Na3Nd(PO4)2) when heat treated at 950 °C. All other glasses were found to be satisfactory. The measured property values were compared to predicted values from a set of current models. In many cases the current models were found to be inadequate for design of DFHLW glasses. These models are being adjusted to correct for mispredictions. Other models, e.g., density, toxicity characteristic leaching procedure, and sulfur solubility, are adequate for formulation of DFHLW glasses.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2023

Enhanced Hanford Low-Activity Waste Glass Property Data Development: Phase 5 and Phase 6

This report summarizes the data collected on two test matrices of low-activity waste (LAW) glass compositions intended to expand the composition-property database: Low-Activity Waste (LAW) Phase 5: Expansion of LAW Glass Composition Boundaries and LAW Phase 6: High PCT and VHT Response Glass Matrix. Both matrix glass compositions were statistically designed to expand the LAW glass composition region. The analyses performed on these glasses include chemical composition (for target compositional verification), density, viscosity, electrical conductivity, crystal fraction, container centerline cooling with crystal identification, the product consistency test (PCT) response, the vapor hydration test (VHT) response, and sulfur solubility. Because of the slightly different scope of the two matrices, not all methods were applied to both matrices. Specifically, the following measurements were taken only on the LAW Phase 5: Expansion of LAW Glass Composition Boundaries glasses: crystal fraction as a function of temperature, density (ρ), viscosity (η), and electrical conductivity (EC, e). Combined, these data contribute a significant amount, 51 glasses, to the database for high LAW loaded enhanced waste glasses. Most of these data are focused near the boundaries of acceptable PCT and VHT responses, where prediction uncertainties are most impactful.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗