Reisert, Michael

Publications and source records attributed to Reisert, Michael.

7 records

DOE OSTI2022

Assessment of Protective Coatings for Metal-Supported Solid Oxide Electrolysis Cells

Green hydrogen is essential to achieving carbon neutrality, and solid oxide electrolysis cells can produce hydrogen using renewable power and waste heat. Insufficient long-term durability of solid oxide electrolysis cells has impeded their commercialization. Here, coatings in the porous stainless steel support of metal-supported solid oxide electrolysis cells (MS-SOECs) are used to dramatically improve their performance and durability. The long-term degradation rate of uncoated MS-SOECs is highly dependent on the current density, with the fastest degradation occurring at the highest current density tested, 0.5 A cm -2 . At this current density, coatings are quite effective. Three protective coatings, Co 3 O 4 deposited by atomic layer deposition (ALD), Co 3 O 4 deposited by electroplating deposition (ED), and CuMn 1.8 O 4 (CMO) deposited by electrophoretic deposition (EPD), are explored to enhance the performance of MS-SOECs with La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3 -Sm 0.2 Ce 0.8 O 3 (LSCF-SDC) as the oxygen catalyst and SDC-Ni as the fuel catalyst. The initial average current density at 1.4 V is increased with coatings. It is 0.83 mA cm -2 for the ALD cells, 1.05 mA cm -2 for the ED cells, and 1.13 mA cm -2 for the EPD cells, compared to 0.65 mA cm -2 for the bare cells at 700 °C with 50% H 2 -50% H 2 O. The degradation rate over 1000 h of continuous operation is reduced from 36% to 26%, 27%, and 19% kh -1 with the three coatings, respectively. Furthermore, these improvements are ascribed to reduced Cr poisoning on the oxygen catalyst, which is one of the primary degradation modes for this type of MS-SOEC.

25 ENERGY STORAGE↗

DOE OSTI2022

Performance of stainless steel interconnects with (Mn,Co) 3 O 4 -Based coating for solid oxide electrolysis

Mixed transition-metal oxide coatings are commonly applied to stainless steel interconnects for solid oxide cell stacks. Such coatings reduce oxidation and Cr evaporation rates, leading to improved degradation rate and stack lifetime. Here, the ChromLok™ MCO-based composition (Mn,Co) 3 O 4 is applied to Crofer 22 APU stainless steel and evaluated specifically for application in solid oxide electrolyzer stacks operating around 800 °C and utilizing oxygen-ion-conducting solid oxide cells. The MCO coating is found to decrease the stainless steel oxidation rate by about one order of magnitude, and decrease the Cr evaporation rate by fourfold. Furthermore, the coating also dramatically lowers the rate of area-specific resistance increase for stainless steel coupons oxidized for 500 h with constant current applied, from 33 mΩ*cm 2 kh -1 for an uncoated coupon to less than 4 mΩ*cm2 kh -1 for coated coupons. The coating is demonstrated on full-scale interconnects for single-cells, where the coating dramatically reduces degradation rate, and for a stack, which displays stable operation for 700 h.

08 HYDROGEN↗

DOE OSTI2021

Hydroxide melt induced corrosion of Ni at elevated temperatures under steam electrolysis conditions

Molten alkali electrolyte based high temperature water electrolysis (HTWE) process offers an efficient pathway to integrate renewable energy resources for large scale and economic hydrogen production. Long term and stable operation of these systems require an in-depth understanding of materials stability under anodic and cathodic exposure conditions of the cell and cell stacks. In the present study, we report our findings on the corrosion of Ni in the presence and absence of (LieNa) hydroxide melt at 600 °C under oxidizing and reducing conditions representative of HTWE. While the Ni electrode was found to remain thermodynamically stable in metallic form under cathodic (reducing) exposure conditions, the corrosion rate in molten hydroxide under oxidizing conditions was found to be nonparabolic in nature. A cyclic voltammetry study provides the breakdown of the passive metal-oxide surface layer at the anodic overpotential region between 0.45 V and 2 V in molten hydroxide under oxidizing conditions. As a result, a thermochemical process for accelerated corrosion based on the oxide scale fluxing in hydroxide melt has been developed.

08 HYDROGEN↗

DOE OSTI2020

Corrosion of AISI 310 and 316 in Molten Hydroxide Under Steam Electrolysis Conditions

Steam electrolyzers, utilizing molten hydroxide electrolyte, offers potential for improvement in electrochemical efficiency, cost reduction, use of conventional materials of construction and process scale up for large scale hydrogen production. Stainless steels, used for the fabrication of cell components (current collector, gas separator, wet seals, and manifolds) experience accelerated corrosion in the presence of molten hydroxide electrolyte in both oxidizing (anodic) and reducing (cathodic) atmospheres. In this study, the corrosion behavior of AISI 310 and 316 in hydroxide melt has been studied at 600°C for 50 h. Melt immersion tests revealed formation of the porous lithium iron oxide at the melt-oxide interface for both AISI 310 and 316. Inductively coupled plasma optical emission spectrometry (ICP-OES) analysis showed the presence of Cr in the electrolyte melt obtained from samples exposed to oxidizing atmosphere. Thermochemical analysis was performed to validate the experimental results.

corrosion↗

DOE OSTI2020

Stability of ceramic matrix materials in molten hydroxide under oxidizing and reducing conditions

The degradation mechanism of ceramic matrix materials used as molten hydroxide electrolyte support for steam electrolysis cells, is not well documented. In this study, we have investigated the structural and chemical stability of non-oxide and oxide ceramics (SiC, YSZ, Li 2 ZrO 3, LiAlO 2 , and SrZrO 3 ) in the presence of molten hydroxide under oxidizing and reducing conditions with humidity levels of 3 and 85% at 550 °C. SiC, YSZ, Li 2 ZrO 3 and LiAlO 2 showed structural and chemical changes due to dissolution of the ceramic particles in the hydroxide melt followed by precipitation. The SrZrO 3 powder, on the other hand, remained both chemically and structurally stable during 500 h test under both oxidizing and reducing atmospheres. The findings of a stable ceramic matrix in molten hydroxide contribute to the enhancement of the durability and performance of intermediate temperature water electrolysis system.

08 HYDROGEN↗

DOE OSTI2020

Oxidation of porous stainless steel supports for metal-supported solid oxide fuel cells

Here, oxidation behavior of porous P434L ferritic stainless steel, used for the fabrication of metal-supported solid oxide fuel cells (MS-SOFC), is studied under anodic and cathodic atmospheres. Temperature- and atmosphere-dependence is determined for as-sintered and pre-oxidized stainless steel. Pre-oxidation reduced the long-term oxidation rate. For pre-oxidized samples, the oxidation rate in air exceeds that in humid hydrogen for temperatures above 700 °C. The influence of PrOx, LSCF-SDC, and Ni-SDC coatings is also examined. The coatings do not dramatically impact oxide scale growth. Oxidation in C-free and C-containing anodic atmospheres is similar. Addition of CO 2 , CH 4 , and CO to humidified hydrogen to simulate ethanol reformate does not significantly impact oxidation behavior. Cr transpiration in humid air is greatly reduced by the PrOx coating, and a PrCrO 3 reaction product is observed throughout the porous structure. A dense and protective chromia-based scale forms on steel samples during oxidation in all conditions. A thin silica enriched oxide layer also forms at the metal-scale interface. In general, the oxidation behavior at 700 °C is found to be acceptable.

25 ENERGY STORAGE↗

DOE OSTI2019

Strontium Manganese Oxide Getter for Capturing Airborne Cr and S Contaminants in High-Temperature Electrochemical Systems

Traces (ppm to ppb level) of airborne contaminants such as CrO 2 (OH) 2 and SO 2 irreversibly degrade the electrochemical activity of air electrodes in high-temperature electrochemical devices such as solid oxide fuel cells by retarding oxygen reduction reactions. The use of getter has been proposed as a cost-effective strategy to mitigate the electrode poisoning. However, owing to the harsh operating conditions (i.e., exposure to heat and moisture), the long-term durability of getter materials remains a considerable challenge. In this study, we report our findings on strontium manganese oxide (SMO) as a robust getter material for cocapture of airborne Cr and S contaminants. The SMO getter with a 3D honeycomb architecture, fabricated via slurry dip-coating, successfully maintains the electrochemical activity of solid oxide cells under the flow of gaseous Cr and S species, validating the getter's capability of capturing traces of Cr and S contaminants. Investigations found that both Sr and Mn cations contribute to the absorption reaction and that the reaction processes are accompanied by morphological elongation in the form of SrSO 4 nanorods and SrCrO 4 whiskers, which favors continued absorption and reaction of incoming S and Cr contaminants. The SMO getter also displays robust stability at high temperatures and in humid environments without phase transformation and hydrolysis. These results demonstrate the feasibility of the use of SMO getter under severe operating conditions representative of high-temperature electrochemical systems.

36 MATERIALS SCIENCE↗