Engineering topics
Ren, Chunlei
Publications and source records attributed to Ren, Chunlei.
Direct methane fueled thin film SOFC technology
Described herein are novel alumina substrate-supported thin film SOFCs that may be produced at significantly reduced cost while providing improved robustness, high electrochemical performance, and the capability of effective carbon deposition resistance while still using Ni-cermet as an anode functional layer.
Upscaling of asymmetric hollow fiber‐supported thin film membranes for oxygen separation from air: Proof of concept
Abstract Hollow fiber membranes demonstrate various advantages for high performance oxygen separation. However, the small diameters of hollow fibers and the brittleness of ceramics limit their mechanical strength, imposing great difficulties on stack and module development. Gas‐tight sealing is another challenge for upscaling of hollow fiber membrane technology. Low temperature sealant materials of epoxy resin or silicon are typically used for hollow fiber stacks, requiring that the sealing portions be located out of hot zone. Consequently, only partial length of hollow fibers participates in oxygen permeation. In this study, upscaling of our recently developed asymmetric hollow fiber‐supported thin film membranes is conducted, where individual hollow fibers are assembled in parallel to form a stack. A reliable gas‐tight sealing is obtained by combining ceramic paste with conductive adhesive ink cohesively. Comprehensive oxygen permeation test is conducted with the sealing portions being in hot zone and compared with a single hollow fiber membrane. Fundamental mechanism is discussed to understand the performances and their differences. An accelerated long‐term test (∼320 h, 16 thermal cycles) demonstrates excellent stability and robustness of the stack and sealing. The characterization of post‐test samples further confirms excellent stability and robustness of the phases and microstructures of the stack.
Fabrication and accelerated long-term stability test of asymmetrical hollow fiber-supported thin film oxygen separation membrane
Asymmetrical hollow fiber-supported thin film membrane may provide microstructural advantages for air separation and oxygen production. The fabrication of such a membrane is usually very difficult, particularly the sintering behaviors and thermal expansion coefficient (TEC) mismatch among multiple layers. This directly affects the reliability and long-term stability of the membrane. Here, in this research, the sintering behaviors of a set of simple oxides are systematically studied and ZnO is identified as a material component for composite substrate La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ (LSCF)-ZnO. The LSCF-ZnO ratios are further optimized by trading off several factors, e.g., matching the sintering behaviors and TECs of the LSCF-ZnO composite with those of LSCF thin film separation layer while enhancing the substrate strength. With the identified LSCF-ZnO ratio, the LSCF-ZnO composite hollow fiber substrate precursor is formed through slurry spinning process with porous microstructure being formed via phase inversion process. The thin film LSCF dense separation layer is then dip-coated on the substrate followed by co-sintering process. A thin, porous PrBaCo(Fe 0.6 Zr 0.2 Y 0.2 )O 5+δ (PBCFZY) catalyst layer is fabricated on the dense LSCF separation layer with dip-coating and sintering process, forming an asymmetrical membrane device LSCF-ZnO/LSCF/PBCFZY. Oxygen permeation test of the device is systematically conducted, and the fundamental mechanisms are analyzed. An accelerated long-term stability test of the membrane is also conducted (~550h, 46 thermal cycling loads), demonstrating excellent robustness and durability. The device is characterized and analyzed before and after the test. By replacing a considerable amount of high cost LSCF with low cost ZnO in the substrate, it not only enhances the stability but also reduces the capital cost of the membrane for practical applications.
Structural evolution, electrochemical kinetic properties, and stability of A-site doped perovskite Sr 1−x Yb x CoO 3−δ
Structural evolution occurs upon A-site partial substitution of Sr by Yb in SrCoO 3−δ , leading to enhanced performance and stability.