Ren, Yaoyu | Search NASA

DOE OSTI2022

Oxide‐Based Solid‐State Batteries: A Perspective on Composite Cathode Architecture

Abstract The garnet‐type phase Li 7 La 3 Zr 2 O 12 (LLZO) attracts significant attention as an oxide solid electrolyte to enable safe and robust solid‐state batteries (SSBs) with potentially high energy density. However, while significant progress has been made in demonstrating compatibility with Li metal, integrating LLZO into composite cathodes remains a challenge. The current perspective focuses on the critical issues that need to be addressed to achieve the ultimate goal of an all‐solid‐state LLZO‐based battery that delivers safety, durability, and pack‐level performance characteristics that are unobtainable with state‐of‐the‐art Li‐ion batteries. This perspective complements existing reviews of solid/solid interfaces with more emphasis on understanding numerous homo‐ and heteroionic interfaces in a pure oxide‐based SSB and the various phenomena that accompany the evolution of the chemical, electrochemical, structural, morphological, and mechanical properties of those interfaces during processing and operation. Finally, the insights gained from a comprehensive literature survey of LLZO–cathode interfaces are used to guide efforts for the development of LLZO‐based SSBs.

25 ENERGY STORAGE↗

DOE OSTI2022

All Solid-State Li/LLZO/LCO Battery Enabled by Alumina Interfacial Coating

Li 7 La 3 Zr 2 O 12 (LLZO) garnet-type lithium-ion conductors are being investigated as a promising solid electrolyte for solid-state lithium batteries. To enable a functional all-solid-state configuration intensive investigations are needed to reduce the cathode/electrolyte interfacial resistance which contributes the most to cell performance loss. Among the commercial cathode materials investigated so far, LiCoO 2 (LCO) is one of the most stable with garnet electrolytes as only a superficial reaction has been detected between the two materials. However, even this minor reaction would block the Li-ion transport through the interface, resulting in deteriorated cell performance. In this work, we demonstrate that a thin aluminum oxide layer (5 nm) can be an effective interlayer to impede the formation of a harmful interphase and enable facile Li-ion transfer between LCO and the LLZO garnet. Room-temperature-sputtered LCO thin films were employed to form an interface with the garnet electrolyte and annealed at 800 °C to reveal the effect of the interfacial reaction on the Li-ion transfer across the interface. An aluminum oxide layer was then introduced between LCO and the garnet electrolyte by sputtering a metallic aluminum layer which is then annealed together with the upper LCO layer in oxygen, or by direct atomic layer deposition of the oxide. Compared to the LCO/LLZO/Li cells without an aluminum oxide interlayer, those with the interlayer exhibited improved performance, i.e., a stable discharge capacity of up to 90 mAh/(g LCO) at a C/10 rate, a rate capability up to 1.68C and a stable galvanostatic cycling at 0.1C for over 100 cycles with a discharge capacity fade rate of 0.15% per cycle. It was determined that aluminum diffused into the LCO layer after preventing the initial detrimental reaction between LCO and the LLZO garnet from happening during high temperature annealing, suggesting that the coating does not have to remain a physically blocking layer during cycling to function.

Electrochemistry↗