Effects of Reactive Power on Photovoltaic Inverter Reliability and Lifetime

This paper performs research on predicting Photovoltaic (PV) inverters reliability and lifetime based on thermal cycling. Thermal cycling is considered the most important stressors in an inverter system. In order to achieve this, a detailed electro-thermal model of the PV inverter will be developed along with their controllers capable of providing voltage support through reactive power. An in-house inverter was built, and a PV inverter model was developed to match the physical inverter. The PV inverter electrothermal model was validated for different ambient temperatures to match the in-house inverter hardware. The in-house inverter was placed inside a thermal chamber to emulate different ambient temperatures and their losses and temperature rises within the system were measured. After the validation of the model, a reduced order model of the inverter will be implemented to translate the mission profile of ambient temperature and solar irradiance into load profile of junction temperatures of the switches. The junction temperature data will be used to identify the reliability indices and hence predict the useful lifetime of the inverter system. Along with the model to predict useful lifetime of the system, the impact of reactive power on the overall reliability of the system will be studied. The key observation in this paper shows that lifetime of the inverter decreases as the operating power factor moves away from unity.

14 SOLAR ENERGY↗

DOE OSTI2020

Movement of Cracked Silicon Solar Cells During Module Temperature Changes

Cracks in crystalline silicon solar cells can lead to substantial power loss. While the cells' metal contacts can initially bridge these cracks and maintain electrical connections, the bridges are damaged by mechanical loads, including those due to temperature changes. We investigated the metallization bridges that form over cracks in encapsulated silicon solar cells. Microscopic characterization showed that the crack in the silicon can immediately propagate through the metal grid, but the grid can maintain electrical contact once the load is removed. We also quantified the movement of the cell fragments separated by a crack as a function of temperature. Cell fragments are free to move diagonally and to rotate, so the change in gap across the crack during a temperature change varies along the length of the crack. In one sample, we showed that a 10 degrees C temperature change, causing a 2 um increase in the separation of cell fragments, was sufficient to cause a reversible electrical disconnection of metallization bridging a crack.

14 SOLAR ENERGY↗

DOE OSTI2020

The Effects of Absorber Thickness on Reverse-Bias Damage in Cu(In,Ga)Se2 Solar Cells

We studied a variety of absorber thicknesses in Cu(In,Ga)Se 2 devices to examine the ability of the cell to withstand reverse current flow without damage. Absorbers were varied from 2.5 um to 0.4 um, with the expectation that larger reverse current would be allowed to flow at lower voltages as absorbers were made thinner. Our initial experiments showed promise. However, as the efficiency of thin devices was improved, the reverse current allowed at a given voltage decreased. Here we present our negative results on the ability of thin devices to allow higher reverse currents at lower voltages. We also give details on our procedures for reverse-bias testing small-area solar cells. We hope this information will be useful for those who want to study reverse-bias at the cell level.