Friction-based recycling: an evaluation of friction extrusion for fabricating Ti-6Al-4 V wire fabricated from machining chip feedstock

Abstract Titanium and its alloys are used in aviation and automobile industries due to their remarkable strength to weight ratio, but machining loss commonly is high with ~ 80 wt% of the material being converted to scrap. Recycling post-consumer Ti scrap directly into solid bulk products is a potential solution for repurposing valuable material. Further, eliminating fresh Ti sponge during recycling might lead to lower energy and greenhouse gas emissions. In this study, a solid-phase process known as friction extrusion was utilized to recycle Ti-6Al-4 V machining chips into solid wires which could be used as feedstock in additive manufacturing. The friction consolidation technique was first used to convert chips with varying degrees of oxygen content into solid billets for its use as feedstock material in subsequent friction extrusion. The extrudates were fabricated above the beta transition temperature, which was achieved by selecting the rotation rate and feed rate, to process the billets near 1000 °C using a tungsten-lanthana extrusion die. This work presents the first occurrence of friction extruded titanium alloy wires. The effect of friction extrusion on microstructural features, tensile properties, and texture are reported. Overall, the friction extrusion method is capable of directly recycling Ti-6Al-4 V scrap into extruded wire.

Friction Extrusion↗

DOE OSTI2024

Recycling of Titanium Scrap by Shear Assisted Processing and Extrusion (ShAPE)

Titanium and its alloys are used in the aviation and automobile industries due to their remarkable strength to weight ratio, but, commonly, machining loss is high with ~90 wt.% of the material being converted to scrap. Recycling post-consumer Ti scrap directly into solid bulk products is a potential solution for repurposing valuable material. Further, reducing or even eliminating fresh Ti sponge during recycling might lead to lower energy and greenhouse gas emissions. In this study, a solid-phase process known as friction extrusion was utilized to recycle Ti-6Al-4V machining chips into solid wires which could be used as feedstock in additive manufacturing. The friction consolidation technique was first used to convert chips with varying degrees of oxygen content into solid billets for its use as feedstock material in subsequent friction extrusion. The extrudates were fabricated above the beta transition temperature, which was achieved by selecting rotation rate and feed rate, to process the billets near 1000°C using a tungsten-lanthana extrusion die. This work presents the first occurrence of friction extruded titanium alloy wires. The effect of friction extrusion on microstructural features, tensile properties, and texture are reported. Overall, the friction extrusion method is capable of recycling Ti-6Al-4V scrap directly into extruded wire.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Solid Phase Processing at the Extreme

The effective application of high-flow-stress materials in the realm of Solid Phase Processing frequently necessitates operating at elevated temperatures and substantially high force. These rigorous processing conditions give rise to intricate predicaments concerning the durability of the tools and dies involved, as well as the efficient utilization of process energy. This project is centered on the investigation of the fundamental scientific aspects inherent to these challenges. We aim to delve into the details of how materials react when subjected to intense shear forces at die interfaces, determine the metallurgical interactions occurring at the interfaces with the dies, and investigate the consequences of extreme temperatures on material flow, microstructural evolution, and resultant properties.

36 MATERIALS SCIENCE↗

NASA NTRS2001

Development of a Novel Method for Determination of Residual Stresses in a Friction Stir Weld

Material constitutive properties, which describe the mechanical behavior of a material under loading, are vital to the design and implementation of engineering materials. For homogeneous materials, the standard process for determining these properties is the tensile test, which is used to measure the material stress-strain response. However, a majority of the applications for engineering materials involve the use of heterogeneous materials and structures (i.e. alloys, welded components) that exhibit heterogeneity on a global or local level. Regardless of the scale of heterogeneity, the overall response of the material or structure is dependent on the response of each of the constituents. Therefore, in order to produce materials and structures that perform in the best possible manner, the properties of the constituents that make up the heterogeneous material must be thoroughly examined. When materials exhibit heterogeneity on a local level, such as in alloys or particle/matrix composites, they are often treated as statistically homogenous and the resulting 'effective' properties may be determined through homogenization techniques. In the case of globally heterogeneous materials, such as weldments, the standard tensile test provides the global response but no information on what is Occurring locally within the different constituents. This information is necessary to improve the material processing as well as the end product.

Reynolds, Anthony P.↗

NASA NTRS1999

Fundamental Study of Material Flow in Friction Stir Welds

The presented research project consists of two major parts. First, the material flow in solid-state, friction stir, butt-welds as been investigated using a marker insert technique. Changes in material flow due to welding parameter as well as tool geometry variations have been examined for different materials. The method provides a semi-quantitative, three-dimensional view of the material transport in the welded zone. Second, a FSW process model has been developed. The fully coupled model is based on fluid mechanics; the solid-state material transport during welding is treated as a laminar, viscous flow of a non-Newtonian fluid past a rotating circular cylinder. The heat necessary for the material softening is generated by deformation of the material. As a first step, a two-dimensional model, which contains only the pin of the FSW tool, has been created to test the suitability of the modeling approach and to perform parametric studies of the boundary conditions. The material flow visualization experiments agree very well with the predicted flow field. Accordingly, material within the pin diameter is transported only in the rotation direction around the pin. Due to the simplifying assumptions inherent in the 2-D model, other experimental data such as forces on the pin, torque, and weld energy cannot be directly used for validation. However, the 2-D model predicts the same trends as shown in the experiments. The model also predicts a deviation from the "normal" material flow at certain combinations of welding parameters, suggesting a possible mechanism for the occurrence of some typical FSW defects. The next step has been the development of a three-dimensional process model. The simplified FSW tool has been designed as a flat shoulder rotating on the top of the workpiece and a rotating, cylindrical pin, which extends throughout the total height of the flow domain. The thermal boundary conditions at the tool and at the contact area to the backing plate have been varied to fit experimental data such as temperature profiles, torque and tool forces. General aspects of the experimentally visualized material flow pattern are confirmed by the 3-D model.

Reynolds, Anthony P.↗

NASA NTRS1994

Multi-lab comparison on R-curve methodologies: Alloy 2024-T3

In an effort to determine an optimum method for ranking the fracture toughness of developmental aluminum alloys for High Speed Civil Transport applications, five labs performed K and/or J based fracture tests on aluminum alloy 2024-T3. Two material thicknesses were examined: 0.063 in. and 0.125 in. Middle crack tension and compact tension specimens were excised from 60 in. wide middle crack tension panels which had been previously tested at Boeing. The crack resistance curves generated were compared to the R-curves from 60 in. wide specimens. The experimental program indicated that effective stress intensity from secant compliance based crack length and stress intensity calculated from J-integral testing were equivalent. In addition, comparison of different specimen sizes and configurations indicated that standard validity requirements for compact tension specimens may be overly restrictive.