DOE OSTI2024

Fabrication of yeast engineered porous 13X adsorbent layers for CO 2 capture

This study investigates a novel environmentally friendly coating technique using yeast fermentation to obtain super porous Zeolite 13X adsorbent layers through freeze-drying technique for CO 2 capture applications. Several mass ratios of sugar to yeast were used to control the porosity and pore sizes in the adsorbent layer. A unique peeling process was integrated to obtain foamy, hollow structures to have deeper layer accessibility of adsorbent for adsorption applications. These coated adsorbent layers were experimentally characterized as a function of the mass ratio of sugar to yeast and adsorbent solid fraction. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and Fourier-transform infrared spectroscopy (FT-IR) are used to analyze the coated layers. Here, the void fraction for coated samples is found to vary between 0.48 and 0.56, making the samples applicable for adsorption applications. Adsorption performance experiments are performed to test the coated samples' performance compared to 13X powder. Due to their simplistic fabrication, cost-effectiveness, rapid pore formation, and high adsorption capacity, these porous 13X layers hold potential for large-scale fabrication and CO 2 capture applications.

Adsorbent coating↗

DOE OSTI2022

Recent Progress on Emerging Applications of Hydrochar

Hydrothermal carbonization (HTC) is a prominent thermochemical technology that can convert high-moisture waste into a valuable product (called hydrochar) at a relatively mild treatment condition (180–260 °C and 2–10 MPa). With rapidly growing research on HTC and hydrochar in recent years, review articles addressing the current and future direction of this research are scarce. Hence, this article aims to review various emerging applications of hydrochars, e.g., from solid fuel to soil amendment, from electron storage to hydrogen storage, from dye adsorption, toxin adsorption, heavy metal adsorption to nutrient recovery, and from carbon capture to carbon sequestration, etc. This article further provides an insight in the hydrochar’s working mechanism for various applications and how the applications can be improved through chemical modification of the hydrochar. Finally, new perspectives with appropriate recommendations have been made to further unveil potential applications and its improvement through hydrochar and its modified version.

09 BIOMASS FUELS↗

DOE OSTI2021

Pretreatment of Biomass by Selected Type-III Deep Eutectic Solvents and Evaluation of the Pretreatment Effects on Hydrothermal Carbonization

Hydrothermal carbonization (HTC) is a novel thermochemical conversion that converts wet biomass into energy dense solid fuel. Residual moisture under subcritical conditions reacts with a lignin-cellulose-hemicellulose matrix with the major reactions being identified as dehydration and decarboxylation. Among other reaction parameters (e.g., temperature, time, pressure), biomass morphology often plays a key role in HTC. The hypothesis of this study was enhancing the porous structure of biomass without significantly affecting biopolymer composition would augment hydrothermal carbonization (HTC). To prove the hypothesis, two type-III deep eutectic solvents (DESs), namely choline chloride:urea (ChCl:Urea, 1:2 mol/mol) and methyltriphenylphosphonium bromide:ethylene glycol (MTPB:EG, 1:4 mol/mol), were studied to pretreat loblolly pine at room temperature and ambient pressure for 1 h. DES pretreatment shows swelling of the biomass, increasing the surface fiber-to-fiber gap length by 52% and 185% for ChCl:Urea and MPTB:EG pretreatments, respectively. The total pore volume remained intact (2.6 × 10 –3 cm 3 /g), although new small pores evolved, and existing pores were abated with DES pretreatment. Hydrochars prepared from DES pretreated loblolly pine showed a high O/C and H/C ratio resulting in a significant increase of energy content (up to 42%) and a decrease of mass yield (up to 50 wt %), indicating an enhancement of HTC severity due to the alteration of surface morphology by DES. Finally, a preliminary process economics revealed that integrated DES pretreatment-HTC would increase fixed capital investment but decrease the cost of operation and manufacturing than the standalone HTC process.

09 BIOMASS FUELS↗

DOE OSTI2021

Integration of Air Classification and Hydrothermal Carbonization to Enhance Energy Recovery of Corn Stover

Air classification (AC) is a cost-effective technology that separates the energy-dense light ash fraction (LAF) from the inorganic-rich high ash fraction (HAF) of corn stover. HAF could be upgraded into energy-dense solid fuel by hydrothermal carbonization (HTC). However, HTC is a high-temperature, high-pressure process, which requires additional energy to operate. In this study, three different scenarios (i.e., AC only, HTC only, and integrated AC–HTC) were investigated for the energy recovery of corn stover. AC was performed on corn stover at an 8 Hz fan speed, which yielded 84.4 wt. % LAF, 12.8 wt. % HAF, and 2.8 wt. % below screen particles. About 27 wt. % ash was reduced from LAF by the AC process. Furthermore, HTC was performed on raw corn stover and the HAF of corn stover at 200, 230, and 260 °C for 30 min. To evaluate energy recovery, solid products were characterized in terms of mass yield, ash yield, ultimate analysis, proximate analyses, and higher heating value (HHV). The results showed that the energy density was increased with the increase in HTC temperature, meanwhile the mass yield and ash yield were decreased with the increase in HTC temperature. Proximate analysis showed that fixed carbon increased 18 wt. % for original char and 27 wt. % for HAF char at 260 °C, compared to their respective feedstocks. Finally, the hydrochar resulting from HAF was mixed with LAF and pelletized at 180 bar and 90 °C to densify the energy content. An energy balance of the integrated AC–HTC process was performed, and the results shows that integrated AC with HTC performed at 230 °C resulted in an additional 800 MJ/ton of energy recovery compared to the AC-only scenario.

09 BIOMASS FUELS↗