Engineering topics

Reza-E-Rabby, Md

Publications and source records attributed to Reza-E-Rabby, Md.

9 records

DOE OSTI2024

Microstructural refinement of an Al-Ce-Mg alloy via Shear Assisted Processing and Extrusion

Al-Ce alloys have attracted recent interest because of their high thermal stability due to the low solubility of Ce in the Al matrix. The Al 11 Ce 3 eutectic phase gives excellent strain hardening behavior and moderate high-temperature strength in the as-cast state. However, its strengthening effect is limited by its coarse as-cast structure. Therefore, alternative manufacturing methods such as additive manufacturing or equal channel angular pressing have been applied to refine the Al 11 Ce 3 phase to good effect. However, these techniques are both expensive and time-consuming. Therefore, this study aims to use Shear Assisted Processing and Extrusion (ShAPE), an emerging solid phase processing technique that is more easily scalable than the previously mentioned methods. ShAPE can produce useful cross-sections of an Al-8Ce-4Mg alloy while refining the Al 11 Ce 3 phase to produce a higher strength material. It was found that a low temperature ShAPE process can improve the room temperature yield strength by ~60 % compared to a binary Al-4Mg alloy. Additionally, the high-temperature yield strength of the Al-Ce alloys increased by 20%, with a simultaneous 15% improvement in ductility compared to the binary Al-Mg alloy. Finally, these results highlight the potential for ShAPE as a processing technique for Al-Ce alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Unprecedented electrical performance of friction-extruded copper-graphene composites

Copper-graphene composites show remarkable electrical performance surpassing traditional copper conductors albeit at a micron scale; there are several challenges in demonstrating similar performance at the bulk scale. In this study, we used shear extrusion to synthesize macro-scale copper-graphene composites with a simultaneously lower temperature coefficient of resistance (TCR) and improved electrical conductivity over copper-only samples. We showed that the addition of 18 ppm of graphene decreased the TCR of C11000 alloy by nearly 11%. A suite of characterization tools involving scanning and transmission electron microscopy along with atom probe tomography were used to characterize the grain size, crystallographic orientation, structure, and composition of copper grains and graphene additives in the feedstock and processed samples. We posit that the shear extrusion process may have transformed some of the feedstock graphene additives into higher defect-density agglomerates while retaining the structure of others as mono-to-trilete flakes with lower defect density. The combination of these additives with heterogeneous structures may have been responsible for the simultaneous decrease in TCR and enhanced electrical conductivity of the copper-graphene ShAPE composites.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Friction stir welding of thick 7175 aluminium alloy plates for deepwater riser applications

To substantially reduce the cost of extracting petroleum from ultra-deepwater sources, manufacturing risers from 7175 aluminium (Al) alloys rather than steels is being considered. Friction stir welding (FSW), a solid-phase joining technique, is widely applied to 7XXX Al alloys because its mechanical properties are retained within the nugget zone. And, the primary technical objective of the current study is the development of high-strength, corrosion-resistant weldments that connect 7175 Al riser flanges and pipes. However, as the welding thickness increases, the welding speed can be greatly impeded, which lowers the manufacturing efficiency and weakens the mechanical properties in the heat affected zone (next to the nugget). Therefore, obtaining high-performance thick plate 7175 Al alloy joints via FSW is challenging. To overcome this dilemma, the current work optimises the tool design and welding parameters for achieving high-performance joints between 25.4 mm thick 7175 Al alloy plates in butt joint configuration.

Wang, Tianhao↗

DOE OSTI2023

Extent of interlocking and metallurgical bonding in friction riveting of aluminum alloy to steel

In this study, the joining of 6061-T6 aluminum alloy and DP590 steel using a M42 steel rivet via friction riveting technique is investigated. The surface morphology and microstructure characterization reveal the formation of an anchor zone that imparts mechanical interlock as well as the formation of metallurgical bonds at the interface of aluminum and steel. A combination of interlocking and bonding results in the achievement of a high load-carrying capacity of 5.7 kN during lap shear testing at room temperature. A finite element-based computational model was developed which accurately predicted the lap shear response of the joint. The model revealed that the metallurgical bond formed during fric-riveting adds 39% peak load strength to the joint. An extensive microstructural investigation, post-lap-shear fractography, and the modeling results, together provided insights on the joint failure mechanism. In conclusion, this study highlights that friction riveting is a promising method for aluminum-to-steel dissimilar joining, which is important for lighweighing automotive vehicles for energy efficiency.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Porthole die extrusion of aluminum 6063 industrial scrap by shear assisted processing and extrusion

Shear Assisted Processing and Extrusion (ShAPE) is presented as a new manufacturing technology for converting aluminum scrap directly into extruded products. In this work, a porthole die configuration is integrated within the rotating ShAPE process to extrude circular, square, trapezoidal, and two-cell trapezoidal profiles from aluminum alloy 6063 industrial scrap. This is the first time that a rotating billet has been used to impart severe plastic deformation (SPD) during extrusion of noncircular profiles. Microstructural characterization is presented for a trapezoidal profile having an average grain size of 6.7 µm in the as-extruded condition. Dimensional stability was evaluated by measuring wall thickness along the extrusion length; the thickness varied by <5%. Round tubes achieved yield strength (246.9 ± 10.4 MPa), ultimate tensile strength (270.8 ± 9.6 MPa), and uniform elongation (16.5 ± 2.4%) exceeding industry standards.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Process parameters and system responses in friction extrusion

We report friction extrusion is an emerging manufacturing process that imparts improved properties and unique microstructures to materials. In this study, the effects of die features (i.e., the absence or presence of die face scrolling) and process parameters (i.e., die rotational speeds and feed rates) on response variables (e.g., extrusion force, torque, power, and temperature) were investigated. During this work, wires with good integrity and similar geometries were extruded over a range of experimental trials with different rotational speeds and feed rates at a constant extrusion ratio. The extrusion force linearly varies with die advance per revolution, which is the ratio of feed rate and rotational speed. The extrusion energy per kilogram mass of extrudate varies non-linearly and asymptotically such that energy consumption is highest at the lowest feed rate and lowest at the highest feed rate. Additionally relationships among other variables (i.e., die advance per revolution, torque, power heat input, and temperature) also were evaluated to elucidate their interdependences.

42 ENGINEERING↗

DOE OSTI2022

Analysis of contact conditions and microstructure evolution in shear assisted processing and extrusion using smoothed particle hydrodynamics method

Shear assisted processing and extrusion (ShAPE) is a solid-phase processing technique that adds an additional shear force as compared with a conventional extrusion approach. Recently, ShAPE has demonstrated the capability of extruding high-performance aluminum alloy 7075 (AA7075) tubes at speeds up to 12.2 m/min without surface tearing. However, the relationship among the ShAPE processing parameters, thermomechanical conditions, contact conditions, heat generation, and microstructure evolution remains primarily empirical because an insightful understanding of the associated physics is still lacking. To help elucidate these relationships, this work proposes a thermomechanical meshfree model for the first time for ShAPE processing of AA7075 using the smoothed particle hydrodynamics (SPH) method. The meshfree model is first validated thoroughly by experimental data in terms of material flow, die face temperature, and extrusion force with various processing parameters. The validated model is then used to analyze the steady-state contact conditions and heat generation rates during ShAPE processing. Distributions of the average grain size of AA7075 being extruded are calculated using the SPH model output. The meshfree model results reveal that extrusions conducted at lower temperatures and higher strain rates yield more refined grains and possibly higher material strength, which is also consistent with the experimental observations.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Extrusion of Unhomogenized Castings of 7075 Aluminum via ShAPE

Extrusion of unhomogenized castings of 7075 aluminum (Al) alloy has been accomplished using shear assisted processing and extrusion (ShAPE). The simultaneous plastic deformation and heat generation during ShAPE rapidly fracture and dissolve interdendritic and intragranular secondary phases of Al-Zn-Mg-Cu, accomplishing homogenization in seconds rather than many hours in a furnace prior to extrusion. ShAPE thereby eliminates the energy-intensive and time-consuming homogenization step required to prepare as-cast microstructures for conventional extrusion. Concurrently, extensive grain refinement occurs due to gradient activation of dynamic recrystallization during ShAPE, which facilitates a threefold increase in extrusion speed compared to the conventional extrusion method. Evident enhancement of the mechanical properties of ShAPE+T6 samples is achieved, compared to the ASTM standard values for conventional extrusion products. The microstructural evolution pathway, involving the processes of grain refinement and secondary particle dissolution, is explained using scanning and transmission electron microscopy.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Shear assisted processing and extrusion of enhanced strength aluminum alloy tubing

Hollow extrusions are used in many industries to make strong, lightweight, and affordable structures. Shear Assisted Processing and Extrusion (ShAPE) enables the extrusion of many alloys, often with noteworthy properties. In this investigation, ShAPE was used to extrude 1 and 2 mm wall tubes of aluminum alloy 6063 measuring 12 mm in diameter at extrusion speeds up to 3.8 m/min. This speed is 10 and 15 times faster than has been reported for any alloy using ShAPE and friction stir back extrusion, respectively. Increasing the extrusion speed from 0.7 to 3.8 m/s resulted in using 68% less process energy at steady state. Microstructural analysis and tensile testing were performed on as-extruded tubes and tubes with a direct T5 heat treatment. Grain refinement from 65 µm to below 20 µm was observed. Growth of macroscale Mg 2 Si strengthening precipitates was not observed. ShAPE processing resulted in recrystallization, and extrusion speed was shown to influence final extrudate texture. Here, transmission electron microscopy analysis revealed that the as-extruded microstructure was free of nanoscale ß" strengthening precipitates. Nanoscale ß" was prominent in direct-aged (T5) ShAPE tubes, similar to a slightly over-aged conventional T6 microstructure. As-extruded tubes had ultimate tensile strengths on par with conventional T5 extrusions and approximately double the total elongation. Tubes that underwent a T5 heat treatment had yield and ultimate strengths averaging 198 and 234 MPa, respectively, with an average total elongation of 11%. The tensile test results are comparable to a conventional T6 heat treatment, but without the solutionization heat treatment step. Mechanical properties either remained flat or improved with increased extrusion speed, which suggests that ShAPE can be scaled up to an industrial process to create energy- and economically efficient high-strength extrusions.

36 MATERIALS SCIENCE↗