DOE OSTI2024

Finite Element Modeling of the Phase Change in Thermally-Grown SiO 2 in SiC Systems for Gas Turbines

The operating lifetimes of SiC-based components in combustion environments are directly linked to the adhesion of the protective environmental barrier coating (EBC) layer. One of the major known failure modes for EBCs is the formation of a thick SiO 2 thermally grown oxide (TGO), which decreases coating adhesion and encourages eventual coating spallation. The effect of the TGO thickness under Yb 2 Si 2 O 7 EBCs on silicon carbide was investigated using finite element models (FEMs) with various interfacial architectures and SiO 2 TGO thicknesses. Further, the FEMs incorporated a user-defined material to simulate the volume contraction of the TGO during the silica phase transformation from β-cristobalite to α-cristobalite upon cooling from the stress-free state at 1350°C to room temperature. Systems with and without a silicon bond coating intermediary layer were assessed. It was shown that the TGO phase transformation stress (1.6–1.7 GPa) dominated the increase in stress in the TGO and EBC layers. Furthermore, it was found that stress increase in the TGO was independent of TGO thickness and interface geometry. These results indicate that stabilization of the TGO to mitigate the phase transformation could dramatically improve the performance of SiC-base components with EBCs.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Holistic comparison of environmental barrier coating material candidates through design of a figure of merit

The first figure of merit for environmental barrier coating (EBC) materials was designed through a ranking system for material properties pertaining to established EBC failure modes in service. Seven past, present, and novel EBC candidate materials were used in the figure of merit design: SiO 2 , Ba 0.75 Sr 0.25 Al 2 Si 2 O 8 (BSAS), HfSiO 4 , Yb 2 Si 2 O 7 , Yb 2 SiO 5 , Yb 2 O 3 , and YbPO 4 . Utilizing compiled data from the literature, the presented figure of merit verified Yb 2 Si 2 O 7 as the state-of-the-art candidate with optimal EBC properties and inferred that YbPO 4 should be considered as a potentially viable EBC material candidate. Further, the figure of merit allows for a holistic comparison of EBC candidates and informs experimental and computational search efforts for next-generation complex EBCs. Clear knowledge gaps found through this work include CaO–MgO–Al 2 O 3 –SiO 2 (CMAS)-resistant coatings, EBC lifetimes before delamination, and oxidant diffusion rates in relevant EBC microstructures. It was shown that while some materials show promise for solving a single key failure mode for EBCs (i.e., CMAS reactivity), a community-wide goal should be placed on materials development to achieve acceptable resistance against all major failure modes, which are interconnected. Novel compositionally complex EBC materials, in addition to layered EBC architectures, show promise for the optimization of material properties for long-lifetime EBCs in combustion environments.

36 MATERIALS SCIENCE↗

DOE OSTI2024

In-situ determination of strain during transient burst testing and the temperature dependence of Zircaloy-4 claddings

Understanding fuel system behavior during postulated loss-of-coolant accidents is pertinent for continued safe and efficient operation of light water reactors, particularly as higher burnups are being pursued and safety margins re-evaluated. Conventional mechanical models for the incumbent Zr alloys typically rely on the assumption that steady-state creep is the dominant fuel cladding response during transient accident conditions. To investigate this assumption, simulated accident burst testing was performed on Zircaloy-4 claddings with balloon behavior measured in-situ. Here, two distinct loading conditions were utilized during burst testing: (1) constant-gas-inventory where pressure was allowed to increase with temperature and (2) constant pressure. In-situ strains and strain rates were measured via 2-dimensional digital image correlation techniques and synchronized with temperature to determine deformation dependencies. The temperature dependence of strain rate was characterized by a two segment Arrhenius relationship, with a distinct transition between the high and low temperature/strain regimes. The average activation energy of the lower temperature/strain regime was 328 ± 25 kJ/mol, in agreement with the ~320 kJ/mol used for conventional LOCA models. However, the higher temperature/strain segment, which encompassed most of ballooning, showed increased activation energies as well as a dependence on whether the burst region was in view. For tests that burst away from the camera view, the average high temperature/strain segment activation energy was 635 ± 150 kJ/mol. For samples where the rupture opening formed in view, the average activation energy was 1015 ± 179 kJ/mol. This observed shift in temperature dependence indicates a transition in deformation mechanism at the end of life, possibly to time independent failure mechanisms, which has not yet been visualized in the literature for Zr alloys. Parameters at the transition points were analyzed to determine thresholds for this change in behavior, which occurred at an average hoop strain of 6.9 ± 2.1 %.

36 MATERIALS SCIENCE↗

DOE OSTI2023

FWP FEAA149: “Next Generation Environmental Barrier Coatings”

Environmental barrier coatings (EBCs) are required coatings for utilization of SiC/SiC ceramic matrix composite (CMC) components in gas turbines, where the EBC represents the life-limiting factor for such components. EBC/CMC systems have shown success in aero-engine applications with increased turbine inlet temperatures and improved efficiencies, which are achieved through higher temperature stability, lower density, and decreased reliance on cooling air compared to traditional superalloys. While industrial gas turbines (IGTs) do not currently utilize SiC/SiC CMCs, the current shift towards low-carbon or carbon-free fuel sources for power generation could result in a need for EBC/CMC components with higher temperature capabilities. In this work, three tasks were outlined to improve understanding of EBC lifetimes to encourage use in IGTs with carbon-free fuel such as hydrogen: 1. Define the bond coating oxidation kinetics and EBC failure criteria, 2. Measure thermal expansion coefficients of each layered material, and 3. Perform advanced characterization and modeling to assess EBC lifetimes. Cyclic steam oxidation tests were conducted on various EBC/Si/SiC chemistries and EBC/SiC architectures to define substrate oxidation kinetics and EBC failure modes. An open-source code was developed to quantify the undulating thermally grown oxide thickness with thousands of measurements from specimen cross-section images. Bond coating oxidation kinetics were determined and used to develop a kinetic and thermodynamic model for predicting EBC lifetimes. High-temperature Raman spectroscopy was utilized for determining the SiO 2 thermally grown oxide phase transformation as the life-limiting feature for EBCs. Model efforts supported the claim that the SiO 2 phase transformation causes elevated stress during thermal cycling with associated cracking that decreases the adhesion strength of the EBC, eventually resulting in coating spallation. The finite element model subroutine will be made publicly available upon internal review. Further development of an EBC lifetime model for IGTs involves definition of a critical SiO 2 thickness for EBC spallation and must also consider both environmental (gas velocity, pressure, etc.) and specimen (EBC dopants, layer architectures, etc.) effects into predicted bond coating oxidation kinetics for long-lifetime components.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Oxidation performance and limitations of additively manufactured SiC/Si-O-C composites at elevated temperatures

Here, SiC preforms were infiltrated with polycarbosiloxane preceramic polymer to create low-cost SiC—Si x O y C z matrix composites for possible high temperature application. The effect of specimen annealing conditions on the steam and air oxidation resistance was analyzed. Air exposures from 900–1500°C showed stability of the Si x O y C z matrix phase with moderate oxidation resistance. After 900°C exposures, oxidation of the composite is primarily limited to the matrix phase, and only at 1200 and 1500°C was SiC consumption visualized. Steam cycle exposures at 1200°C resulted in rapid linear oxidation of the composites with induced specimen swelling from volume expansion associated with internal oxidation. Specimens annealed in argon were found to be the most oxidation resistant due to increased matrix crystallinity and carbon retention. The results of this work were used to develop clear strategies for improving the high-temperature properties of SiC—Si x O y C z composites.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Raman spectroscopic characterization of SiO 2 phase transformation and Si substrate stress relevant to EBC performance

To accurately model the long-term durability of environmental barrier coatings (EBCs), a more complete understanding of the phase composition and transformations of the thermally grown oxide SiO 2 (TGO) is desired. For the TGO formed during thermal cycling in steam, cristobalite formation and the subsequent β- to α-cristobalite transformation has been identified as a potentially life-limiting mechanism. In this study, Raman micro-spectroscopy was used to quantify the cristobalite transformation on a polycrystalline Si coupon that was exposed to steam at 1350°C for 100 h. The phase transformation was mapped at 200–260°C on the TGO surface at different ramp rates using a heating stage and a micro-positioning stage. The stress in the Si substrate was also determined using Raman spectroscopy by measuring the stress induced peak shift. The α→β phase transformation produced a 300–500 MPa tensile stress in the Si substrate, which compared well to the stress predicted from the volumetric expansion of the cristobalite. In conclusion, quantifying the phase transformation and residual stress are critical tools in developing the next generation of high performance EBCs.

36 MATERIALS SCIENCE↗