DOE OSTI2023

Material and component developments for the DEMO divertor using fibre reinforcement and additive manufacturing

Within the research along the European Fusion Roadmap, water-cooled divertor PFCs are foreseen in the design of a first fusion demonstration power plant (DEMO) in order to provide reliable heat removal capability. In the frame of this concerted attempt, the Max Planck Institute for Plasma Physics is concentrating on the development and testing of composite materials based on tungsten (W, preferred armour material) and copper (Cu, preferred heat sink material). W fibres (W f ) as monofilaments and yarns as reinforcement play a central role in these investigations due to their extraordinary properties concerning ductility already at room temperature and high tensile strength. Recent investigations on the impact of radiation damage suggest that the fibres retain their ductility upon irradiation. W reinforced with W fibres (W f /W) allows to overcome the intrinsic brittleness of W. Quantitative mechanical fracture tests of W f /W confirm the basic mechanisms of fibre reinforcement and the increased resistance to mechanical fatigue. The good wettability of W with liquid Cu and the absence of any metallurgical solubility make up an ideal material pairing for composite production. W fibre-reinforced Cu (W f /Cu) cooling tubes provide a rather high thermal conductivity (> 250 W mK -1 ) and at least twice the strength of CuCrZr in hoop direction in the temperature range up to at least 500 °C. Very recent neutron irradiation experiments confirm the sustainment of ductility of the W f /Cu composite. Numerical simulations suggest that thermal stresses in W-Cu PFCs could be strongly reduced by tailoring the local W and Cu volume fraction. This 'freely' distributed material composition can be achieved by means of additively manufactured W skeletons consecutively infiltrated by Cu. Investigations with W preforms produced by Laser Beam Powder Bed Fusion and infiltrated by Cu demonstrate the feasibility of this approach while testing of specifically prepared specimen is ongoing.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

DOE OSTI2021

Irradiation effects in tungsten—From surface effects to bulk mechanical properties

Advanced materials such as tungsten fibre-reinforced composites allow to overcome severe weaknesses of the baseline materials for plasma-facing components — copper and tungsten. The effect of the fusion environment on the mechanical properties of these materials, e.g. the embrittlement by neutron irradiation, plays a key role for the development of future fusion reactors. To simulate this effect, high-energy ions are used as a substitute for the displacement damage by neutrons. We propose the use of very fine tungsten wire as a possibility of studying the influence of irradiation damage on the mechanical properties. This is possible as they allow full-depth irradiation of almost the entire volume despite the limited penetration depth of ions. Geometrical size effects are mitigated due to the nanoscale microstructure of the wire. In addition, similar wire is used in tungsten fibre-reinforced composites. Thus, the investigation of irradiated wire can directly be used for the prediction of the bulk composite properties. For the proof of this concept tungsten wire with a diameter of 16 μm was electrochemically thinned to 5 μm and irradiated with 20.5 MeV W 6+ ions. The mechanical properties were subsequently determined by macroscopic tensile testing. Irradiation to 0.3, 1 and 9 dpa did not lead to a change of the mechanical behaviour. Both strength and ductility, the latter indicated by the reduction of area, were similar to the as-fabricated state.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Modeling and experimental validation of a W f /W-fabrication by chemical vapor deposition and infiltration

Tungsten (W) has a unique combination of excellent thermal properties, low sputter yield, low hydrogen retention, and acceptable activation. Therefore, W is presently the main candidate for the first wall material in future fusion devices. However, its intrinsic brittleness and its further embrittlement during operation bears the risk of a sudden and catastrophic component failure. As a countermeasure, tungsten fiber-reinforced tungsten (W f /W) with extrinsic toughening is being developed. A possible synthesis route is chemical vapor deposition (CVD) using heated W fabrics as substrate. The challenge is that the growing CVD-W can isolate domains from precursor access leading to strength-reducing pores. To deepen the process understanding and to optimize the CVD parameters, models were developed with COMSOL Multiphysics and validated experimentally. W deposition rate equations as function of the temperature and the partial pressures of the precursors H 2 and WF 6 were experimentally validated in previous work. In the present article, these equations are applied to obtain partial pressures within the CVD reactor. The results are taken as input for transient simulations in the microscale, in which W coatings, growing onto multiple adjacent W fibers, were simulated via mesh deformation and remeshing. The surface-to-surface contact of the W coatings and the corresponding potential pore formation were simulated by implementing sophisticated deposition rate stop conditions. Within the measuring uncertainties of ≃ ±1%, the models are validated successfully by experimental comparison regarding the deposition rate, pore structure, and relative densities ranging from 0.6 to 0.9.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗