Study of Mechanical Grinding Effects on Niobium Surface

Mechanical grinding is commonly employed to eliminate surface defects such as scratches and pits from niobium cavity surfaces or sheets before cavity fabrication. Subsequently, chemically buffered polishing or electropolishing is often utilized to completely remove residues of the polishing media and any defects induced by mechanical grinding, ensuring a pristine surface. In this study, we conducted a systematic investigation to assess the influence of mechanical grinding using silicon carbide (SiC) and aluminium oxide (Al2O3) polishing media on niobium surfaces. Additionally, the study examines the effects of post-mechanical grinding chemical treatments on surface quality.

Chouhan, V.↗
DOE OSTI2024

Study of Mechanical Grinding Effects on Niobium Surface

Mechanical grinding is commonly employed to eliminate surface defects such as scratches and pits from niobium cavity surfaces or sheets before cavity fabrication. Subsequently, chemically buffered polishing or electropolishing is often utilized to completely remove residues of the polishing media and any defects induced by mechanical grinding, ensuring a pristine surface. In this study, we conducted a systematic investigation to assess the influence of mechanical grinding using silicon carbide and aluminum oxide polishing media on niobium surfaces. Additionally, the study examines the effects of post-mechanical grinding chemical treatments on surface quality.

Chouhan, V.↗
DOE OSTI2023

Low Particulates Nitrogen Purge and Backfill During pHB650 Cryomodule String Assembly

A low particulate vacuum and purging system was developed to support PIP-II cryomodule string assembly. The overpressure can be controlled at a precision of 1 mbar above the atmospheric pressure regardless of the cavity or string assembly air volume. The system minimized the risk of uncontrolled nitrogen flow during the string assembly. Design features are presented.

Ring, T.↗
DOE OSTI2023

Low Particulates Nitrogen Purge and Backfill During Prototype HB650 Cryomodule String Assembly

A low particulate vacuum and purging system was developed to support PIP-II cryomodule string assembly. The overpressure can be controlled at a precision of 1 mbar above the atmospheric pressure regardless of the cavity or string assembly air volume. The system minimized the risk of uncontrolled nitrogen flow during the string assembly. Design features are presented.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2023

Electropolishing Study on Nitrogen-doped Niobium Surface

The nitrogen doping (N-doping) process is applied to niobium (Nb) superconducting cavities to enhance their quality factors. The N-doping is followed by an electropolishing process that provides the final surface of the cavities. A controlled EP process is necessary to get the benefit of N-doping and achieve a high accelerating gradient. We have performed electropolishing of N-doped Nb surface under various conditions to understand their impact on the surface. A modified EP process was developed to obtain a smooth pit-free surface.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2023

Electropolishing parameters study for surface smoothening of low-$\beta$650 MHz five-cell niobium superconducting radio frequency cavity

Electropolishing (EP) is applied to niobium (Nb) superconducting radio frequency (SRF) cavities, which are used in particle accelerators for their surface treatment. The EP process for 1.3 GHz cavities has been extensively studied earlier. In this work, a parametric study on EP of low-β (0.61) 650 MHz Nb SRF cavities (LB650), which will be used in pre-production cryomodule for proton improvement plan-II (PIP-II) linear accelerator, was conducted to determine adequate EP conditions for attaining a smooth surface of the cavities. EP performed with the standard parameters and an initial cathode (cathode-I) having a cathode surface area of ~5% of the cavity surface area yielded a rough equator surface of the cavity. The grain step height on the equator weld position was measured to be ~ 32 μm. The rough surface was attributed to preferential grain etching confirmed by a polarization curve showing a linear relationship between the EP current and voltage and the absence of the current plateau region. The cathode was modified to make its surface area twice that of cathode-I. The modified cathode (cathode-M) provided a current plateau region in the corresponding I-V curves measured at different cavity temperatures. The onset voltage for the plateau was found to be higher at higher cavity temperatures. Here this study revealed that even with cathode-M, the standard 18 V was low for EP of such large-sized cavities when the cavity temperature was 18 °C. EP performed at a higher voltage of 22–24.5 V with cathode-M yielded a smooth surface with a grain step height of only 0.6 μm. The applied EP conditions also improved removal uniformity along the cavity length. In contrast to the cavity treated with cathode-I, the cavities treated with cathode-M achieved a significantly higher accelerating gradient (E acc ) in vertical tests conducted in a cryostat at 2 K. The modified EP was found efficient to produce the cavities that achieved E acc of 22.4 MV/m, required by PIP II project in the baseline RF tests, to qualify for further surface processing used to enhance their quality factors.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2022

Effect of Electropolishing on Nitrogen Doped and Undoped Niobium Surfaces

Cold electropolishing (EP) of a nitrogen-doped (N-doped) niobium (Nb) superconducting RF (SRF) cavity was found to improve its quality factor. In order to understand the effect of EP temperature on N-doped and undoped surfaces, a systematic EP study was conducted with 2/0 N-doped and heat-treated Nb samples in a beaker. The Nb samples were electropolished at different surface temperatures ranging from 0 to 42 C. The results showed that the doped surface was susceptible to the sample temperature during EP. EP resulted in the surface pitting on the doped samples where the number density of pits increased at a higher temperature. The surface results were compared with the surface of cutouts from a 9-cell cavity which was 2/0 N-doped and electropolished. This paper shows de-tailed surface features of the N-doped and undoped Nb surfaces electropolished at different temperatures.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2022

Study on Electropolishing Conditions for 650 MHz Niobium SRF Cavity

The PIP II linear accelerator includes different types of niobium SRF cavities including 650 MHz elliptical low (0.61) and high (0.92) beta cavities. The elliptical cavity surface is processed with the electropolishing method. The elliptical cavities especially the low-$\beta$ 650 MHz cavities showed a rough equator surface after the EP was per-formed with the standard EP conditions. This work was focused to study the effect of different EP parameters, including cathode surface area, temperature and voltage, and optimize them to improve the cavity surface.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2021

Computational Fluid Dynamic Simulation for Electrolyte Flow in Horizontal EP of Nb SRF Elliptical Cavities

An electrolyte flow velocity on an electropolishingsurface affects a material removal rate where higherremoval is observed with a higher velocity of theelectrolyte. In horizontal EP (HEP) of an ellipticalcavity, an electrolyte flow near the equator positionmight remain slow and responsible for a lowerremoval compared to that on the iris and beam pipepositions. In order to understand the flow dynamicon an elliptical cavity surface in the horizontal EPprocess, a computational fluid dynamic simulationwas conducted. This study was conducted on 1.3GHz cavity with different cathodes and acid flowrates. Final aim of the study is to improve the flowuniformity to attain uniform removal especially inmulticell cavities.

Chouhan, V.↗