Rinkel, Bernardine L D

DOE OSTI2025

Alternative Solid‐State Synthesis Route for Highly Fluorinated Disordered Rock‐Salt Cathode Materials for High‐Energy Lithium‐Ion Batteries

Abstract Fluorination has been identified as a key element for enabling the stable cycling of earth‐abundant manganese‐based disordered rock salt (DRX) cathodes. However, fluorination in the DRX bulk remains a challenge for scalable solid‐state synthesis. In this study, a tailored reaction pathway is proposed to synthesize a highly fluorinated DRX. It is demonstrated for the first time that the unconventional precursors, Li 6 MnO 4 , MnF 2 , and TiO 2 , can avoid the formation of Mn‐based intermediates (such as Li 2 (Mn,Ti)O 3, LiMnO 2 , and Mn 3 O 4 ), which, once formed, persist until the synthesis temperature reaches close to or above that required for fluorine volatility. Therefore, this method can form a highly fluorinated DRX with a composition of Li 1.23 Mn 0.40 Ti 0.37 O 2−y F y ( y = 0.29–0.34) at a low temperature (800 °C) relative to that required for conventional DRX solid‐state reactions (≥900 °C). Li 1.23 Mn 0.40 Ti 0.37 O 2−y F y ( y = 0.29–0.34) delivers a specific capacity above 300 mAh g −1 and a specific energy of 980 Wh kg −1 at 30 °C. Detailed characterization reveals that this DRX phase reversibly utilizes Mn 2+/3+ redox in the low‐voltage region and Mn 3+/4+ redox in the middle‐voltage range, whereas reversible oxygen redox is observed at high potentials.

Avvaru, Venkata Sai↗

DOE OSTI2024

Oxygen redox activities governing high-voltage charging reversibility of Ni-rich layered cathodes

A schematic illustration indicative of the improved structural reversibility through stabilizing oxidized oxygen by Al doping. The chemical reactions and phase transitions at high voltages are generally considered to determine the electrochemical properties of high-voltage layered cathodes such as Ni-rich rhombohedral oxides. Even if significantly higher SOCs (states-of-charge) are utilized above the capability of transition metal redox (primarily Ni and Co), the effect of oxygen redox on Ni-rich rhombohedral oxides still looks mysterious thereby necessitating research that can clarify the relationship between redox reactions and phase transitions. Here, we performed a comprehensive and comparative study of the cationic and anionic redox reactions, as well as the structural evolution of a series of commercial Ni-rich layered oxides with and without Al doping. We combined the results from X-ray spectroscopy, operando electrochemical mass spectrometry, and neutron diffraction with electrochemical properties and thereby revealed the different oxygen redox activities associated with structural and electrochemical degradations. We reveal that Al doping suppresses the irreversible oxygen release but enhances the lattice oxygen oxidization. With this modulated oxygen redox activity, the Ni-rich layered oxides’ notorious H2–H3 structural phase transition becomes highly reversible. Our findings disentangle the different oxygen redox activities during high-voltage cycling and clarify the role of dopants in the Ni-rich layered oxides in terms of structural and electrochemical stability, shedding light on the future direction of optimizing layered cathode materials for safer high energy-density secondary batteries.

Lee, Gi-Hyeok↗