Final report on assessment of molten salt corrosion testing of unirradiated and ion irradiated advanced manufactured high entropy alloys
Generation IV reactors and future fusion reactor designs have led to more demanding materials performance requirements due to their increased operating temperatures, corrosive coolants, and increased radiation doses compared to the current light-water reactor fleet. Among the innovative nuclear technologies under development, molten salt reactors stand out for their potential to offer superior fuel utilization, intrinsic safety characteristics, and economic viability. Of the proposed Generation IV designs, the gas fast reactor operates at 450 to 850°C and the molten salt reactor operates at 565 to 850°C, with the molten salt reactor design needing molten salt corrosion resistant materials [1, 2]. These increased temperatures and more extreme corrosion environments necessitate higher material performance, such as creep strength, radiation-tolerant microstructures, corrosion resistance, and high-temperature tensile properties. Hastelloy-N, a nickel-based alloy with additions of molybdenum and chromium, has been successfully employed to contain molten fluoride salt at temperatures up to 705°C. However, Hastelloy-N becomes embrittled upon neutron irradiation, primarily due to the accumulation of helium produced by (n,a) transmutation reactions. Furthermore, the corrosive nature of molten fluoride and chloride salts presents a formidable challenge, as these salts can react with and dissolve alloying elements such as Cr, Mo, and Fe, leading to selective leaching, loss of protective oxide layers, and accelerated degradation. High entropy alloys (HEAs) and refractory high entropy alloys (RHEAs) have emerged as a prominent area of interest, due to their ability to achieve tailored chemical compositions for specific applications. Unlike conventional alloys, HEAs are characterized by having multiple principal elements in equimolar or near equimolar ratios, leading to an unconventional alloying strategy [3]. This alloying strategy is believed to promote unique properties, such as single-phase stabilization of chemically compatible elements, lattice distortion effects due to atomic radius differences, and proposed sluggish diffusion effects. For extreme-environment applications, RHEAs have garnered much research interest because of the possibility of creating relatively ductile materials that can operate in extremely high-temperature environments, beyond the operating temperatures where other Ni-based superalloys begin to lose strength [4-6]. Idaho National Laboratory (INL) initiated a joint international effort with the Czech Republic to explore the feasibility of manufacturing HEAs for high-temperature nuclear applications using advanced manufacturing. This effort was funded at INL by the United States Department of Energy's Office of Nuclear Energy under the Advanced Reactor Technologies and Advanced Materials and Manufacturing Technologies (AMMT) Program. The HEAs were specifically designed for the corrosive and irradiation environments experienced in gas-cooled fast reactors, molten salt reactors, and fusion power. These alloys have been manufactured by multiple processes to determine the impact of manufacturing processes on the performance of the alloys in corrosive and irradiation environments. Preliminary molten salt corrosion testing showed that equimolar MoNbTiV and MoNbTi alloys exhibit exceptional performance, with arc-melted variants demonstrating only minimal degradation after 1000 hours of exposure to molten chloride salt at 700°C. Conversely, Nb2TiVZr2 showed significant molten salt corrosion susceptibility and microstructural instability during high-temperature molten salt exposures, and was, therefore deemed unfit for molten salt reactor applications. The MoNbTiV, MoNbTi, and Nb2TiVZr2 alloys were further evaluated through ion irradiation experiments conducted at the Michigan Ion Beam Laboratory at the University of Michigan. The microstructural stability and the evolution of irradiation-induced defects were characterized to assess the irradiation resistance of each of these alloys.