Flux effects in precipitation under irradiation simulation of Fe-Cr alloys

Radiation-enhanced precipitation of Cr-rich α’ in irradiated Fe-Cr alloys, which results in hardening and embrittlement, depends on the irradiating particle and the displacement per atom (dpa) rate. Here, we utilize a Cahn-Hilliard phase-field based approach, that includes simple models for nucleation, irradiating particle and rate dependent radiation-enhanced diffusion and cascade mixing to simulate α’ evolution under neutrons, heavy ions, and electron irradiations. Different irradiating particles manifest very different cascade mixing efficiencies. The model was calibrated using neutron data. For cascade inducing neutron/heavy-ion dpa rates at 300 °C between 10-8 and 10-6 dpa/s the model predicts approximately constant number density, decreasing radius, decreasing α’ Cr composition, and lower α’ volume fraction. The model then predicts a dramatic transition to no α’ formation above approximately 10-5 dpa/s, while electron irradiation, with weak mixing, had little effect at dpa rates up to 10-3 dpa/s. These model predictions are consistent with experiments. We explain the results in terms of the flux dependence of the radiation enhanced diffusion, cascade mixing, and their ratio, which all vary significantly in relevant flux ranges for neutron and cascade inducing ion irradiations. These results show that both cascade mixing and radiation enhanced diffusion must be accounted for when attempting to emulate neutron-irradiation effects using accelerated ion irradiations.

Ke, Jia-Hong↗
DOE OSTI2025

Thermodynamics and kinetics of core-shell versus appendage co-precipitation morphologies

What determines precipitate morphologies in co-precipitating alloy systems? We focus on alloys of two precipitating phases, with the fast-precipitating phase acting as heterogeneous nucleation sites for a second phase manifesting slower kinetics. Kinetic lattice Monte Carlo simulations show that the interplay between interfacial and ordering energies, plus active diffusion paths, strongly affect the selection of core-shell verses appendage morphologies. We study a FeCuMnNiSi alloy using the combination of atom probe tomography and simulations, and show that the ordering energy reduction of the MnNiSi phase heterogeneously nucleated on a pre-existing copper-rich precipitate exceeds the energy penalty of a predominantly Fe/Cu interface, leading to initial appendage, rather than core-shell, formation. Diffusion of Mn, Ni and Si around and through the Cu core towards the ordered phase results in subsequent appendage growth. We further show that in cases with higher primary precipitate interface energies and/or suppressed ordering, the coreshell morphology is favored.

Shu, Shipeng↗
DOE OSTI2025

6cr

A series of model Fe–Cr alloys containing 3–18 at.% Cr was neutron irradiated at a nominal temperature of 563 K to 1.82 dpa. Solute distributions were analyzed by atom probe tomography, which revealed α′ precipitation for alloys containing more than 9 at.% Cr. Both the Cr concentration dependence of α′ precipitation and the measured matrix compositions are in agreement with the recently published Fe–Cr phase diagrams. An irradiation-accelerated precipitation process is strongly suggested. Irradiation was carried out in the Advance Test Reactor (ATR) at Idaho National Laboratory. A series of six Fe–Cr alloys of nominal compositions 3, 6, 9, 12, 15 and 18 at.% Cr was irradiated at a neutron fluence (E > 1 MeV) of 1.1 × 1021 n cm−2 at 563 ± 15 K and to a damage level of 1.82 displacements per atom (dpa). Nominal neutron flux and dpa rate are 2.3 × 1014 n cm−2 s−1 and 3.4 × 10−7 dpa s−1, respectively. The microstructures of the Fe–Cr alloys were studied by atom probe tomography (APT) using a Cameca 4000X HR instrument. APT specimens were prepared by a standard lift-out process using a Quanta 3D 200i dual beam scanning electron microscope ensuring that the analyses were performed away from grain boundaries.

Bachhav, Mukesh↗
DOE OSTI2024

Atom probe datasets from neutron irradiated Fe-Cr alloys

A series of model Fe–Cr alloys containing 3–18 at.% Cr was neutron irradiated at a nominal temperature of 563 K to 1.82 dpa. Solute distributions were analyzed by atom probe tomography, which revealed α′ precipitation for alloys containing more than 9 at.% Cr. Both the Cr concentration dependence of α′ precipitation and the measured matrix compositions are in agreement with the recently published Fe–Cr phase diagrams. An irradiation-accelerated precipitation process is strongly suggested. Irradiation was carried out in the Advance Test Reactor (ATR) at Idaho National Laboratory. A series of six Fe–Cr alloys of nominal compositions 3, 6, 9, 12, 15 and 18 at.% Cr was irradiated at a neutron fluence (E > 1 MeV) of 1.1 × 1021 n cm−2 at 563 ± 15 K and to a damage level of 1.82 displacements per atom (dpa). Nominal neutron flux and dpa rate are 2.3 × 1014 n cm−2 s−1 and 3.4 × 10−7 dpa s−1, respectively. The microstructures of the Fe–Cr alloys were studied by atom probe tomography (APT) using a Cameca 4000X HR instrument. APT specimens were prepared by a standard lift-out process using a Quanta 3D 200i dual beam scanning electron microscope ensuring that the analyses were performed away from grain boundaries.

Bachhav, Mukesh↗