Static Torsion Testing and Modeling of a Variable Thickness Hybrid Composite Bull Gear

Torsional strength of a variable thickness hybrid gear web was measured by performing static testing on the part in a large torsion test frame. The outer rim of the hybrid gear web was fixed to the bottom of the test frame and loading was applied to the web through a shaft. The test setup included the installation of digital image correlation (DIC) systems to obtain deformation and strain measurements from the surfaces of the hybrid gear web and the mechanical test equipment to ensure reliability of the test. The results indicated that the variable thickness hybrid gear web achieved approximately twice the torsional strength compared to that of previous hybrid gear designs. The DIC analysis showed significantly more straining of the loading shaft than the actual test article. Additionally, the results demonstrated the importance and affect that the metallic, lobed interlock features had on the principal strain and out-of-plane displacement fields. The analysis revealed that the fixed outer rim was in fact rotating and a rigid body motion compensation (RBMC) function was computed to determine the actual rotation of the hub and composite web relative to the outer rim. Modeling simulations were performed for the variable thickness hybrid gear web and correlated well with the RBMC rotational deformation seen in the DIC analysis. In addition to benchmarking the load capacity of the hybrid gear web, measuring its strength is useful information to define the parameters needed for dynamic, endurance, and other testing of the part.

Johnston, Joel P.↗

NASA NTRS2019

Quasi-Static and Dynamic Analysis of Composite Panels: Characterization and Validation

The predictive capability of a progressive damage model to simulate the quasi-static and dynamic crushing of composite specimens is evaluated in this article. The material model is commercially available within the ABAQUS finite element software package, i.e., “Damage for Fiber reinforced Composites”, and is often utilized to simulate damage progression and failure in static and dynamic failure scenarios such as crushing of a composite plate. The composite specimens used in this study consist of quasi-isotropic C-shaped and corrugated composite panels comprised of carbon fiber/epoxy braided fabric. The C-shaped panel specimen is used to calibrate the model and optimize material/model properties through comparison with experimental results. Then, using the same model parameters, the quasi-static crush response of the corrugated panel is predicted. The predictive capability of the model is further demonstrated by simulating the dynamic crushing response of both C-shaped and corrugated panels using the same material properties as in the quasi-static crush case with only minor adjustments for the dynamic elastic properties (i.e., rate dependent modulus). Results show that the in-built material model available in ABAQUS can successfully reproduce experimental results for both panels (C-shaped and corrugated) subjected to both quasi-static and dynamic loading scenarios. A small-scale parametric study on physical (experimentally measurable) and nonphysical (purely mathematical) model parameters was also conducted. It can be concluded that, achieving successful simulation results requires a more in-depth understanding of the influence of model parameter variation on the mechanical response of the composite together with the strategies and challenges of the utilized modeling methodology (e.g., FEA mesh density, etc.).

Naghipour Ghezeljeh, Paria↗

NASA NTRS2019

A Design Methodology for Optimizing and Integrating Composite Materials in Gear Structures

The application of composite materials to gear structures is complex because of the gear shape, the need for precise dimensional tolerances, and the complex dynamic load condition. Methods are presented in this work to design and optimize an integrated composite hub-web structure that can be used as part of a hybrid composite-steel gear. The composite hub-web structure is a planar structure with a large decrease in thickness from the hub to the rim. Methods for design and optimization of this variable-thickness structure are presented along with a method for forming braided prepreg material to conform to the shape of this structure. A layered approach is presented that integrates cut plies or filler materials for thickness buildup with continuous-fiber layers for the primary load path. An additional gear design concept is presented that has an axially extended continuous-fiber composite structure that can be combined with the planar structure. A proposed optimization methodology is introduced where an optimized design is output for each type of optimization simulation. Through this process, composite knowledge can be incorporated in the optimization, and more control is given over the design during the process. The methods in this study provide a tool for designing and optimizing composite structures for gears and other high-power-density applications.

optimization↗

NASA NTRS2018

Joint Strength Optimization and Damping Assessment of NiTi-Polymer Matrix Hybrid Composites

Approaches to optimize the adhesive joint strength between shape memory alloy ribbons and carbon fiber-reinforced epoxy composites were investigated for potential use as either an actuating structure or a dampening composite for structural applications. The interfacial bond strength between nickel-titanium (NiTi) and a polymer matrix composite (PMC) was measured by double lap shear testing as a function of NiTi surface treatment and adhesive material. The effect of NiTi surface treatment on damping was investigated using dynamic mechanical analysis. Lap shear data show that treating the surfaces of NiTi ribbons by light sandblasting and primer application increased the interfacial bond strength by 20 percent over the baseline composite structure. Lap shear data also reveal that out of three different film adhesives investigated, samples bonded with AF 191U and Hysol® 9696U display the highest adhesive joint strengths. Optical microscopy reveals that most samples failed by either cohesive failure within the adhesive or by adhesive failure at either the adhesive/PMC or NiTi/adhesive interface. Adhering NiTi to the PMC did not appear to negatively impact damping performance; however, a more thorough examination into NiTi's role on vibration damping should be investigated.

lap shear↗

NASA NTRS2018

Influence of Fiber Volume and Alignment on Impact Resistance of Braided Carbon Fiber Epoxy Composites

The effect of axial tow alignment within a laminate ply stack on the impact penetration threshold for a series of composite panels was evaluated; specifically, the effect of a lateral shift in alignment to induce fiber nesting. Panels were fabricated from braided T700S carbon fiber and TenCate Advanced Composites's TC275-1 epoxy resin prepreg. Axial tows in each ply were aligned, offset, or rotated to evaluate the influence of such parameters on impact penetration resistance. Panel-to-panel variation in thickness, resin content, and fiber volume ratio were measured. Ultimately, process-related deviations drove penetration limits on impact. Influence of axial tow alignment was difficult to discern outside of the processing-induced variations between panels.

process variation↗

NASA NTRS2018

Evaluation of a Variable Thickness Hybrid Composite Bull Gear

For several years, NASA Glenn Research Center and the U.S. Army Research Laboratory have been investigating hybrid (compositesteel) gear technology for use in vertical lift drive systems. The hybrid gear concept replaces the structural portion of a gear between the shaft and the gear rim with a lightweight carbon fiber composite, in an effort to reduce the overall weight of a gear and increase the drive system power density. An overview of the concept of the hybrid gear design is described in Ref. 1, 2, and 3. The research presented in these references includes both small-scale and large-scale hybrid gear concepts all of which have a constant composite thickness throughout. The design described in this paper is of a variable thickness, such that the composite is thickest at the inner diameter and this thickness is gradually reduced toward the outer diameter. The resulting stair stepped design stems from dropping plies of the braided carbon fiber composite fabric gradually with increased radius. Additionally, the interlock pattern at the inner metallic adapter was adjusted slightly from previous designs to obtain a better stress distribution on the inner metallic adapter. The manufactured variable thickness web was tested both in static torsion tests and operationally in a relevant gearbox environment. The results of these experiments will be presented and compared to a baseline steel configuration.

Rotorcraft Propulsion↗

NASA NTRS2018

Results of NASA Technical Challenge to Demonstrate Two-Speed Drive for Vertical Lift Vehicle

Currently, manned vertical lift vehicles are flown in a manner such that the rotors operate over a narrow range of rotating speed regardless if the vehicle's flight condition is one of vertical takeoff and landing, hover, or forward cruise. The propulsion systems are optimized for operation at the same, corresponding narrow range of rotor speed. However, certain missions and markets benefit greatly if the rotor speed can be adjusted over a wide range of speed to match demands of different missions and flight regimes. A vehicle that can operate with a wide range of rotor speeds would address key barriers to enable new markets and missions for vertical lift vehicles. Key barriers addressed by the wide-range of rotor speed include noise reduced via lower rpm rotor, increase of maximum forward flight speed, increased payload and range, reduced fuel burn, and lower operating costs. A new paradigm for the propulsion system is needed to enable these key benefits. One viable approach is to make use of a two-speed ratio drive system such that the engine can continue to operate over a narrow speed range, whereby engine performance is optimal, while adjusting the rotor speed as needed using the two-speed drive system. Motivated by such needs and by results of several system studies, a NASA Revolutionary Vertical Lift Technology Challenge was established to develop and demonstrate required technologies and designs for achieving a 50% reduction in rotor rpm via a two-speed drive system that incurs less than 2% power loss and maintains current power-to-weight ratios. The technical challenge work was completed and the technical objectives were achieved. This report describes the motivations, the research approach and the significant outcomes.

Transmissions↗

NASA NTRS2018

Comparison of Impact Damage from Spin Pit and Flat Panel Gas Gun Testing

Gas gun experiments can generate useful data for the design of jet engine containment shields at much lower costs. To replicate the damage modes similar to that on a containment shield in fan-blade-out (FBO) testing, the gas gun experiment has to be carefully designed. This work focuses on the design of projectiles. Gas gun experiments were performed for flat composite panel targets with three different projectiles. FBO conditions were simulated using spin pit tests. The damage modes on the flat panels used in the gas gun tests were compared with damage modes on cylindrical composite containment shields used in spin pit tests. The results show that to generate similar damage modes, it is critical to ensure the shape of the projectile used in a gas gun test accounts for the deformation of the released blade during initial contact in the spin pit test.

Vanderklok, Andy↗

NASA NTRS2017

High Speed Thermal Imaging on Ballistic Impact of Triaxially Braided Composites

Ballistic impact experiments were performed on triaxially braided polymer matrix composites to study the heat generated in the material due to projectile velocity and penetration damage. Quantifying the heat generation phenomenon is crucial for attaining a better understanding of composite behavior and failure under impact loading. The knowledge gained can also be used to improve physics-based models which can numerically simulate impact of composites. Triaxially braided (0/+60/-60) composite panels were manufactured with T700S standard modulus carbon fiber and two epoxy resins. The PR520 (toughened) and 3502 (untoughened) resin systems were used to make different panels to study the effects of resin properties on temperature rise. Ballistic impact tests were conducted on these composite panels using a gas gun, and different projectile velocities were applied to study the effect on the temperature results. Temperature contours were obtained from the rear surface of the panel during the test through a high speed, infrared (IR) thermal imaging system. The contours show that high temperatures were locally generated and more pronounced along the axial tows for the T700S/PR520 composite specimens; whereas, tests performed on T700S/3502 composite panels using similar impact velocities demonstrated a widespread area of lower temperature rises. Nondestructive, ultrasonic C-scan analyses were performed to observe and verify the failure patterns in the impacted panels. Overall, the impact experimentation showed temperatures exceeding 525 K (485degF) in both composites which is well above the respective glass transition temperatures for the polymer constituents. This expresses the need for further high strain rate testing and measurement of the temperature and deformation fields to fully understand the complex behavior and failure of the material in order to improve the confidence in designing aerospace components with these materials.

thermal imaging↗

NASA NTRS2017

Investigation of Carbon Fiber Architecture in Braided Composites Using X-Ray CT Inspection

During the fabrication of braided carbon fiber composite materials, process variations occur which affect the fiber architecture. Quantitative measurements of local and global fiber architecture variations are needed to determine the potential effect of process variations on mechanical properties of the cured composite. Although non-destructive inspection via X-ray CT imaging is a promising approach, difficulties in quantitative analysis of the data arise due to the similar densities of the material constituents. In an effort to gain more quantitative information about features related to fiber architecture, methods have been explored to improve the details that can be captured by X-ray CT imaging. Metal-coated fibers and thin veils are used as inserts to extract detailed information about fiber orientations and inter-ply behavior from X-ray CT images.

braided composites↗

NASA NTRS2017

Evaluation of a Variable Thickness Hybrid Composite Bull Gear

For several years, NASA Glenn Research Center and the U.S. Army Research Laboratory have been investigating hybrid (composite/steel) gear technology for use in vertical lift drive systems. The hybrid gear concept replaces the structural portion of a gear between the shaft and the gear rim with a lightweight carbon fiber composite, in an effort to reduce the overall weight of a gear and increase the drive system power density. Past research includes both small-scale and large-scale hybrid gear concepts, all of which have a constant composite thickness throughout. The design described in this paper is of a variable thickness, such that the composite is thickest at the inner diameter and this thickness is gradually reduced toward the outer diameter. The resulting "stair stepped" design stems from dropping plies of the braided carbon fiber prepreg composite fabric gradually with increased radius. Additionally, the interlock pattern at the inner metallic adapter was adjusted slightly from previous designs to obtain a better stress distribution on the inner metallic adapter. The manufactured variable thickness web was tested both in static torsion tests and operationally in a relevant gearbox environment. The results of these experiments will be presented and compared to a baseline steel configuration.

Gears; Drive Systems; Rotorcraft Propulsion;↗

NASA NTRS2017

Hybrid Gear Performance Under Loss-of-Lubrication Conditions

Hybrid composite gear technology is being investigated to increase power density in rotorcraft drive systems. These gears differ from conventional steel gears in that the structural web material is replaced with a lightweight carbon fiber composite. Past studies have focused on performance of this technology under normal operating conditions, however, for this technology to be viable it must also withstand adverse conditions. The study presented here evaluates the performance of hybrid gears under loss-of-lubrication conditions in NASA Glenn Research Centers Contact Fatigue Test Facility. Two experiments are presented using small-scale 3.5 inch (8.9 cm) pitch diameter hybrid gears and compared to a baseline steel gear pair. Results of these tests show that there are limitations to the use of a hexagonal interlock pattern between the steel and composite. There is also evidence that the presence of polymer in the gear during an oil out event has a potential to increase time to failure. Further studies are planned to expand on these initial findings.

Gearbox↗

NASA NTRS2017

Hybrid Gear Performance Under Loss-of-Lubrication Conditions

Gearbox↗

NASA NTRS2016

The Effects of Hygrothermal Aging on the Impact Penetration Resistance of Triaxially Braided Composites

An experimental study was conducted to measure the effects of long term hygrothermal aging on the impact penetration resistance of triaxially braided polymer composites. Flat panels of three different materials were subjected to repeated cycles of high and low temperature and high and low humidity for two years. Samples of the panels were periodically tested under impact loading during the two year time period. The purpose of the study was to identify and quantify any degradation in impact penetration resistance of these composites under cyclic temperature and humidity conditions experienced by materials in the fan section of commercial gas turbine engines for a representative aircraft flight cycle. The materials tested consisted of Toray ® T700S carbon fibers in a 2D triaxial braid with three different resins, Cycom® PR520, a toughened resin, Hercules® 3502, an untoughened resin and EPON 862, intermediate between the two. The fiber preforms consisted of a quasi-isotropic 0/+60/-60 braid with 24K tows in the axial direction and 12K tows in the bias directions. The composite panels were manufactured using a resin transfer molding process producing panels with a thickness of 0.125 inches. The materials were tested in their as-processed condition and again after one year and two years of aging (1.6 years in the case of E862). The aging process involved subjecting the test panels to two cycles per day of high and low temperature and high and low humidity. A temperature range of -60degF to 250degF and a humidity range of 0 to 85% rh was used to simulate extreme conditions for composite components in the fan section of a commercial gas turbine engine. Additional testing was conducted on the as-processed PR520 composite under cryogenic conditions. After aging there was some change in the failure pattern, but there was no reduction in impact penetration threshold for any of the three systems, and in the case of the 3502 system, a significant increase in penetration threshold. There was also an increase in the penetration resistance of the PR520 system impacted under cryogenic conditions.

composite↗

NASA NTRS2016

Hybrid Gear

A hybrid gear consisting of metallic outer rim with gear teeth and metallic hub in combination with a composite lay up between the shaft interface (hub) and gear tooth rim is described. The composite lay-up lightens the gear member while having similar torque carrying capability and it attenuates the impact loading driven noise/vibration that is typical in gear systems. The gear has the same operational capability with respect to shaft speed, torque, and temperature as an all-metallic gear as used in aerospace gear design.

Handschuh, Robert F.↗

NASA NTRS2015

Ballistic and Cyclic Rig Testing of Braided Composite Fan Case Structures

FAA fan blade-out certification testing on turbofan engines occurs very late in an engine's development program and is very costly. It is of utmost importance to approach the FAA Certification engine test with a high degree of confidence that the containment structure will not only contain the high-energy debris, but that it will also withstand the cyclic loads that occur with engine spooldown and continued rotation as the non-running engine maintains a low rotor RPM due to forced airflow as the engine-out aircraft returns to an airport. Accurate rig testing is needed for predicting and understanding material behavior of the fan case structure during all phases of this fan blade-out event.

spooldown↗

NASA NTRS2015

Impact Behavior of Composite Fan Blade Leading Edge Subcomponent with Thermoplastic Polyurethane Interleave

Impact damage tolerance and damage resistance is a critical metric for application of polymer matrix composites where failure caused by impact damage could compromise structural performance and safety. As a result, several materials and/or design approaches to improve impact damage tolerance have been investigated over the past several decades. Many composite toughening methodologies impart a trade-off between increased fracture toughness and compromised in-plane strength and modulus. In large part, mechanical tests to evaluate composite damage tolerance include static methods such as Mode I, Mode II, and mixed mode failures. However, ballistic impact damage resistance does not always correlate with static properties. The intent of this paper is to evaluate the influence of a thermoplastic polyurethane veil interleave on the static and dynamic performance of composite test articles. Static coupon tests included tension, compression, double cantilever beam, and end notch flexure. Measurement of the resistance to ballistic impact damage were made to evaluate the composites response to high speed impact. The interlayer material showed a decrease of in-plane performance with only a moderate improvement to Mode I and Mode II fracture toughness. However, significant benefit to impact damage tolerance was observed through ballistic tests.

Damage Tolerance↗

NASA NTRS2015

Materials, Manufacturing, and Test Development of a Composite Fan Blade Leading Edge Subcomponent for Improved Impact Resistance

Application of polymer matrix composite materials for jet engine fan blades is becoming attractive as an alternative to metallic blades; particularly for large engines where significant weight savings are recognized on moving to a composite structure. However, the weight benefit of the composite is offset by a reduction of aerodynamic efficiency resulting from a necessary increase in blade thickness; relative to the titanium blades. Blade dimensions are largely driven by resistance to damage on bird strike. Further development of the composite material is necessary to allow composite blade designs to approximate the dimensions of a metallic fan blade. The reduction in thickness over the state of the art composite blades is expected to translate into structural weight reduction, improved aerodynamic efficiency, and therefore reduced fuel consumption. This paper presents test article design, subcomponent blade leading edge fabrication, test method development, and initial results from ballistic impact of a gelatin projectile on the leading edge of composite fan blades. The simplified test article geometry was developed to realistically simulate a blade leading edge while decreasing fabrication complexity. Impact data is presented on baseline composite blades and toughened blades; where a considerable improvement to impact resistance was recorded.

Materials↗