NASA NTRS2020

CMC / EBC Research at NASA Glenn in 2020: Recent Progress and Plans

As part of NASA's Aeronautics research, Glenn Research Center has developed SiC/SiC Ceramic Matrix Composites for 2700°F turbine engine applications in the next generation of ultra-efficient aircraft. In this presentation, the development of fiber and matrix constituents and fabrication processes that enabled this advancement will be reviewed, and characterization of the resulting improvements in CMC mechanical properties and durability will be summarized. Progress toward the development and validation of models predicting the effects of the engine environment on durability of Ceramic Matrix Composites and Environmental Barrier Coatings will be summarized. Results from current collaborative research with industry and other government agencies will be reviewed. Research plans for 2020 and opportunities for future collaborations with NASA will also be summarized.

Grady, Joseph E.↗

NASA NTRS2005

Quick Access Rocket Exhaust Rig Testing of Coated GRCop-84 Sheets Used to Aid Coating Selection for Reusable Launch Vehicles

The design of the next generation of reusable launch vehicles calls for using GRCop-84 copper alloy liners based on a composition1 invented at the NASA Glenn Research Center: Cu-8(at.%)Cr-4%Nb. Many of the properties of this alloy have been shown to be far superior to those of other conventional copper alloys, such as NARloy-Z. Despite this considerable advantage, it is expected that GRCop-84 will suffer from some type of environmental degradation depending on the type of rocket fuel utilized. In a liquid hydrogen (LH2), liquid oxygen (LO2) booster engine, copper alloys undergo repeated cycles of oxidation of the copper matrix and subsequent reduction of the copper oxide, a process termed "blanching". Blanching results in increased surface roughness and poor heat-transfer capabilities, local hot spots, decreased engine performance, and premature failure of the liner material. This environmental degradation coupled with the effects of thermomechanical stresses, creep, and high thermal gradients can distort the cooling channel severely, ultimately leading to its failure.

Raj, Sai V.↗

NASA NTRS2005

Advanced Environmental Barrier Coatings Development for Si-Based Ceramics

Advanced environmental barrier coating concepts based on multi-component HfO2 (ZrO2) and modified mullite systems are developed for monolithic Si3N4 and SiC/SiC ceramic matrix composite (CMC) applications. Comprehensive testing approaches were established using the water vapor cyclic furnace, high pressure burner rig and laser heat flux steam rig to evaluate the coating water vapor stability, cyclic durability, radiation and erosion resistance under simulated engine environments. Test results demonstrated the feasibility and durability of the environmental barrier coating systems for 2700 to 3000 F monolithic Si3N4 and SiC/SiC CMC component applications. The high-temperature-capable environmental barrier coating systems are being further developed and optimized in collaboration with engine companies for advanced turbine engine applications.

Zhu, Dong-Ming↗

NASA NTRS2004

Characterization of an Ultra-High Temperature Ceramic Composite

Levine, Stanley R.↗

NASA NTRS2004

Oxidation of Ultra High Temperature Ceramics in Water Vapor

Ultra High Temperature Ceramics (UHTCs) including HfB2 + 20v/0 SiC (HS), ZrB2 + 20v/0 SiC (ZS), and ZrB2 + 30v/0 C + 14v/0 SiC (ZCS) have been investigated for use as potential aeropropulsion engine materials. These materials were oxidized in water vapor (90 percent) using a cyclic vertical furnace at 1 atm. The total exposure time was 10 h at temperatures of 1200, 1300, and 1400 C. CVD SiC was also evaluated as a baseline for comparison. Weight change, X-ray diffraction analyses, surface and cross-sectional SEM and EDS were performed. These results are compared with tests ran in a stagnant air furnace at temperatures of 1327 C for 100 min, and with high pressure burner rig (HPBR) results at 1100 and 1300 C at 6 atm for 50 h. Low velocity water vapor does not make a significant contribution to the oxidation rates of UHTCs when compared to stagnant air. The parabolic rate constants at 1300 C, range from 0.29 to 16.0 mg(sup 2)cm(sup 4)/h for HS and ZCS, respectively, with ZS results between these two values. Comparison of results for UHTCs tested in the furnace in 90 percent water vapor with HPBR results was difficult due to significant sample loss caused by spallation in the increased velocity of the HPBR. Total recession measurements are also reported for the two test environments.

Nguyen, QuynhGiao N.↗

NASA NTRS2004

Oxidation of Ultra-High Temperature Ceramics in Water Vapor

Ultra High Temperature Ceramics (UHTCs) including HfB2 + 20% SiC (HS), and ZrB2 + 20% SiC (ZC), and ZrB2 + 30% C + 14% SiC (ZCS) have been investigated for use as potential aeropropolsion engine materials. These materials were oxidized in water vapor (90%) using a cyclic vertical furnace at 1 atm. The total exposure time was 10 hours at temperature of 1200, 1300, and 1400 C. CVD SiC was also evaluate as a baseline for comparison. Weight change, X-ray diffraction analysis, surface and cross-sectional SEM and EDS were performed. These results are compared with tests conducted in a stagnant air furnace at temperatures of 1327 C for 100 minutes, and with high pressure burner rig (HPBR) results at 1100 and 1300 C at 6 atm for 50 h. Total recession measurements are also reported for the two tests environments.

Nguyen, QuynGiao N.↗

NASA NTRS2004

Ultra-high Temperature Ceramic Composites for Leading Edges, 2004

Ultrahigh temperature ceramics (UHTC) have performed unreliably due to material flaws and attachment design. These deficiencies are brought to the fore by the low fracture toughness and thermal shock resistance of the UHTC. If these deficiencies are overcome, we are still faced with poor oxidation resistance as a limitation on UHTC applicability to reusable launch vehicles. We have been addressing the deficiencies of UHTC for the past two years via a small task at GRC that is in the Airframe part of the Next Generation Launch Technology Program. Our focus is on composite constructions and functional grading to address the mechanical issues and on composition modification to address the oxidation issue. The progress on approaches to improving oxidation resistance by alloying and functional grading will be reported.

Levine, Stanley R.↗

NASA NTRS2003

Oxidation of Ultra-High Temperature Ceramics in Water Vapor

Ultra high temperature ceramics (UHTCs) including HfB2 + SiC (20% by volume), ZrB2 + SiC (20% by volume) and ZrB2 + SiC (14% by volume) + C (30% by volume) have historically been evaluated as reusable thermal protection systems for hypersonic vehicles. This study investigates UHTCs for use as potential combustion and aeropropulsion engine materials. These materials were oxidized in water vapor (90%) using a cyclic vertical furnace at 1 atm. The total exposure time was 10 hours at temperatures of 1200, 1300, and 1400 C. CVD SiC was also evaluated as a baseline comparison. Weight change measurements, X-ray diffraction analyses, surface and cross-sectional SEM and EDS were performed. These results will be compared with tests ran in static air at temperatures of 1327, 1627, and 1927 C. Oxidation comparisons will also be made to the study by Tripp. A small number of high pressure burner rig (HPBR) results at 1100 and 1300 C will also be discussed. Specific weight changes at all three temperatures along with the SIC results are shown. SiC weight change is negligible at such short duration times. HB2 + SiC (HS) performed the best out of all the tested UHTCS for all exposure temperatures. ZrB2 + Sic (ZS) results indicate a slightly lower oxidation rate than that of ZrBl + SiC + C (ZCS) at 1200 and 1400 C, but a clear distinction can not be made based on the limited number of tested samples. Scanning electron micrographs of the cross-sections of all the UHTCs were evaluated. A representative area for HS is presented at 1400 C for 26 hours which was the composition with the least amount of oxidation. A continuous SiO2 scale is present in the outer most edge of the surface. An image of ZCS is presented at 1400 C for 10 hours, which shows the most degradation of all the compositions studied. Here, the oxide surface is a mixture of ZrSiO4, ZrO2 and SO2.

Nguyen, QuynhGiao N.↗

NASA NTRS2003

Ultra-High Temperature Ceramic Composites for Leading Edges

Ultra-high temperature ceramics (UHTC) have performed unreliably due to material flaws and attachment design. These deficiencies are brought to the fore by the low fracture toughness and thermal shock resistance of UHTC. If these deficiencies are overcome, we are still faced with poor oxidation resistance as a limitation on UHTC applicability to reusable launch vehicles. We have been addressing the deficiencies of UHTC for the past two years via a small task at GRC that is in the Airframe part of the Next Generation Launch Technology Program. Our focus is on composite constructions and functional grading to address the mechanical issues and on composition modification to address the oxidation issue. The progress on approaches to improving oxidation resistance by alloying and functional grading will be reported. In particular, initial tests of tantalum additions have shown potential for major improvement. Results for additional tests at higher temperatures will be presented. These oxidation improvements are being incorporated in the composites approaches. Two fabrication approaches are being persued to produce carbon fiber reinforced UHTC composites: prepregging and rigid perform infiltration. Fabrication procedures, microstructures, and initial mechanical property and oxidation results for composites will be reported.

Levine, Stanley R.↗

NASA NTRS2003

Characterization of a Ultra-high Temperature Ceramic Composite

Ultra-high temperature ceramics (UHTC) are of interest for hypersonic vehicle leading edge applications. Monolithic UHTCs are of concern because of their low fracture toughness and brittle behavior. UHTC composites (UHTCC) are being investigated as a possible approach to overcome these deficiencies. In this study a small sample of a UHTCC was evaluated by limited mechanical property tests, furnace oxidation exposures, and oxidation exposures in a flowing environment. The composite was prepared from a carbon fiber perform using ceramic particulates and a preceramic polymer. The as-received composite plate was non-uniform from front to back surface. Plate dimensions were 150 x 150 x 6 mm. The back surface had a fibrous, uniform appearance; XRD analysis revealed the presence of Sic and C. The front surface was smooth and non-uniform in appearance with evidence of a coarse grain structure produced by a liquid phase; XRD analysis revealed the presence of HfB2. Microcracks were present throughout the thickness as one might expect from a carbon fiber reinforced composite with attendant large thermal expansion mismatch between the matrix phases and the fibers. The HfB2 phase on the front surface was comparable in thickness to a fiber ply or about 0.6 mm, and surface microcracks were evident. Limited four point flexural tests were carried out at span to depth ratios of approximately 14 and 16 with markedly different results. Tests were run with the front or the back surface in tension. At the shorter span to depth failures occurred under a loading pin for both orientations. At a span to depth of 16 failures occurred in the center of the span with fracture clearly initiating from a tensile failure. Ultimate flexural strength, strain at ultimate stress, stress and strain at deviation from linear elastic behavior are reported. Strains at ultimate stress ranged from about 0.6 to 0.7 % for the back surface in tension, and 0.4 to 0.6 for the front surface in tension. At constant span to depth the strain at ultimate stress was about 0.2% greater for the back surface in tension and the ultimate strength was also higher. Strengths were in line with predictions from theory. Furnace oxidation studies were carried out at 1627 and 1927OC in a static furnace environment using ten minute cycles and one, five, and ten cycles. Limited oxidation studies were also carried out in a flowing oxyacetylene torch environment. Specimens were photographed, and weight and dimensional changes were determined. XRD and SEM characterizations were performed. Weight losses were attributed primarily to carbon fiber oxidation. The composite survived the torch test with little visible distress. Further details will be determined once metallographic studies are completed.

Levine, Stanley R.↗

NASA NTRS2002

Upper Temperature Limit of Environmental Barrier Coatings Based on Mullite and BSAS

Current state-of-the-art environmental barrier coatings (EBCs) for Si-based ceramics consist of three layers: a silicon bond coat, an intermediate mullite (3Al2O3-2SiO2) or mullite + BSAS (1-xBaO-xSrO-Al2O3-2SiO2) layer, and a BSAS top coat. Areas of concern for long-term durability are environmental durability, chemical compatibility, silica volatility, phase stability, and thermal conductivity. Variants of this family of EBCs were applied to monolithic SiC and melt infiltrated SiC/SiC composites. Reaction between BSAS and silica results in low melting (approx. 1300 C) glasses at T > 1400 C, which can cause the spallation of the EBC. At temperatures greater than 1400 C, the BSAS top coat also degrades by formation of a porous structure, and it suffers significant recession via silica volatilization in water vapor-containing atmospheres. All of these degradation mechanisms can be EBC life-limiting factors. BSAS undergoes a very sluggish phase transformation (hexagonal celsian to monoclinic celsian), the implications of which are not fully understood at this point. There was evidence of rapid sintering at temperatures as low as 1300 C, as inferred from the sharp increase in thermal conductivity.

Lee, Kang N.↗

NASA NTRS2002

High Temperature Corrosion of Silicon Carbide and Silicon Nitride in Water Vapor

Silicon carbide (SiC) and silicon nitride (Si3N4) are proposed for applications in high temperature combustion environments containing water vapor. Both SiC and Si3N4 react with water vapor to form a silica (SiO2) scale. It is therefore important to understand the durability of SiC, Si3N4 and SiO2 in water vapor. Thermogravimetric analyses, furnace exposures and burner rig results were obtained for these materials in water vapor at temperatures between 1100 and 1450 C and water vapor partial pressures ranging from 0.1 to 3.1 atm. First, the oxidation of SiC and Si3N4 in water vapor is considered. The parabolic kinetic rate law, rate dependence on water vapor partial pressure, and oxidation mechanism are discussed. Second, the volatilization of silica to form Si(OH)4(g) is examined. Mass spectrometric results, the linear kinetic rate law and a volatilization model based on diffusion through a gas boundary layer are discussed. Finally, the combined oxidation and volatilization reactions, which occur when SiC or Si3N4 are exposed in a water vapor-containing environment, are presented. Both experimental evidence and a model for the paralinear kinetic rate law are shown for these simultaneous oxidation and volatilization reactions.

Opila, E. J.↗

NASA NTRS2001

Environmental Barrier Coatings for Silicon-Based Ceramics

Silicon-based ceramics, such as SiC fiber-reinforced SiC (SiC/SiC ceramic matrix composites (CMC) and monolithic silicon nitride (Si3N4), are prime candidates for hot section structural components of next generation gas turbine engines. Silicon-based ceramics, however, suffer from rapid surface recession in combustion environments due to volatilization of the silica scale via reaction with water vapor, a major product of combustion. Therefore, application of silicon-based ceramic components in the hot section of advanced gas turbine engines requires development of a reliable method to protect the ceramic from environmental attack. An external environmental barrier coating (EBC) is considered a logical approach to achieve protection and CP long-term stability. The first generation EBC consisted of two layers, mullite (3Al2O3-2SiO2) bond coat and yttria-stabilized zirconia (YSZ, ZrO2-8 Wt.% Y2O3) top coat. Second generation EBCs, with substantially improved performance compared with the first generation EBC, were developed in the NASA High Speed Research-Enabling Propulsion Materials (HSR-EPM) Program. The first generation EBC consisted of two layers, mullite (3Al2O3-2SiO2) bond coat and yttria-stabilized zirconia (YSZ, ZrO2-8 wt.% Y2O3) top coat. Second generation EBCs, with substantially improved performance compared with the first generation EBC, were developed in the NASA High Speed Research-Enabling Propulsion Materials (HSR-EPM) Program (5). They consist of three layers, a silicon first bond coat, a mullite or a mullite + BSAS (BaO(1-x)-SrO(x)-Al2O3-2SiO2) second bond coat, and a BSAS top coat. The EPM EBCs were applied on SiC/SiC CMC combustor liners in three Solar Turbines (San Diego, CA) Centaur 50s gas turbine engines. The combined operation of the three engines has accumulated over 24,000 hours without failure (approximately 1,250 C maximum combustor liner temperature), with the engine in Texaco, Bakersfield, CA, accumulating about 14,000 hours. As the commercialization of Si-based ceramic components in gas turbines is on the horizon, a major emphasis is placed on EBCs for two reasons. First, they are absolute necessity for the protection of Si-based ceramics from water vapor. Second, they can enable a major enhancement in the performance of gas turbines by creating temperature gradients with the incorporation of a low thermal conductivity layer. Thorough understanding of current state-of-the-art EBCs will provide the foundation upon which development of future EBCs will be based. Phase stability and thermal conductivity of EPM EBCs are published elsewhere. This paper will discuss the chemical/environmental durability and silica volatility of EPM EBCs and their impact on the coating's upper temperature limit.

Lee, Kang N.↗

NASA NTRS1999

SiC and Si3N4 Recession Due to SiO2 Scale Volatility Under Combustor Conditions

Silicon carbide (SiC) and Si3N4 materials were tested in various turbine engine combustion environments chosen to represent either conventional fuel-lean or fuel-rich mixtures proposed for high-speed aircraft. Representative chemical vapor-deposited (CVD), sintered, and composite materials were evaluated by furnace and high-pressure burner rig exposures. Although protective SiO2 scales formed in all cases, the evidence presented supports a model based on paralinear growth kinetics (i.e., parabolic growth moderated simultaneously by linear volatilization). The volatility rate is dependent on temperature, moisture content, system pressure, and gas velocity. The burner tests were thus used to map SiO2 volatility (and SiC recession) over a range of temperatures, pressures, and velocities. The functional dependency of material recession (volatility) that emerged followed the form A[exp(-Q / RT)](P(sup x)v(sup y). These empirical relations were compared with rates predicted from the thermodynamics of volatile SiO and SiOxHy reaction products and a kinetic model of diffusion through a moving boundary layer. For typical combustion conditions, recession of 0.2 to 2 micrometers/hr is predicted at 1200 to 1400 C, far in excess of acceptable long-term limits.

Smialek, James L.↗

NASA NTRS1999

Durability of Ceramic Matrix Composites in Combustion Environments

SiO2 scale volatility and the resulting recession of SiC has been previously identified for CVD, as well as sintered, SiC and Si3N4 materials. Linear weight loss and surface recession of SiC was observed as a result of SiO2 volatility for both fuel-lean and fuel-rich gas mixtures. A strong Arrhenius temperature dependence exist and parametric studies using multiple linear regression were used to develop recession relationships as a function of e(sup -Q/RT) central dot P(sup X)V(sup y) for both lean and rich combustion conditions. Recession of 0.2 - 2.0 micron/hr is predicted for typical combustion conditions at 1200 - 1400 C, with a somewhat higher absolute recession rate and activation energy for rich combustion versus lean.

Robinson, Raymond C.↗

NASA NTRS1998

SiC Recession Due to SiO2 Scale Volatility Under Combustion Conditions: Thermodynamics and Gaseous Diffusion Model - Part 2

In combustion environments, volatilization of SiO2 to Si-O-H(g) species is a critical issue. Available thermochemical data for Si-O-H(g) species were used to calculate boundary layer controlled fluxes from SiO2. Calculated fluxes were compared to volatilization rates Of SiO2 scales grown on SiC which were measured in Part 1 of this paper. Calculated volatilization rates were also compared to those measured in synthetic combustion gas furnace tests. Probable vapor species were identified in both fuel-lean and fuel-rich combustion environments based on the observed pressure, temperature and velocity dependencies as well as the magnitude of the volatility rate. Water vapor is responsible for the degradation of SiO2 in the fuel-lean environment. Silica volatility in fuel-lean combustion environments is attributed primarily to the formation of Si(OH)4(g) with a small contribution of SiO(OH)2(g).

Opila, Elizabeth J.↗

NASA NTRS1994

Hot Corrosion Test Facility at the NASA Lewis Special Projects Laboratory

The Hot Corrosion Test Facility (HCTF) at the NASA Lewis Special Projects Laboratory (SPL) is a high-velocity, pressurized burner rig currently used to evaluate the environmental durability of advanced ceramic materials such as SiC and Si3N4. The HCTF uses laboratory service air which is preheated, mixed with jet fuel, and ignited to simulate the conditions of a gas turbine engine. Air, fuel, and water systems are computer-controlled to maintain test conditions which include maximum air flows of 250 kg/hr (550 lbm/hr), pressures of 100-600 kPa (1-6 atm), and gas temperatures exceeding 1500 C (2732 F). The HCTF provides a relatively inexpensive, yet sophisticated means for researchers to study the high-temperature oxidation of advanced materials, and the injection of a salt solution provides the added capability of conducting hot corrosion studies.

Robinson, Raymond C.↗