Engineering topics

Rodrigues, Marco-Tulio [Argonne National Laboratory]

Publications and source records attributed to Rodrigues, Marco-Tulio [Argonne National Laboratory].

5 records

DOE OSTI2026

Solid-state prealkylation of electrode architectures to tune solid electrolyte interphase composition

Efficient electrochemical cycling of certain Si anodes is limited by irreversible Li consumption to form and continually reform the solid electrolyte interface (SEI) due to Si expansion/contraction and fracture. Prelithiation can compensate for these losses; however, the starting open circuit potential (VOC) becomes highly reducing and, therefore, the electrolyte reduction chemistry that influences the SEI composition can change. Herein, we compare SEI formation for electrodes prelithiated using Solid State Prealkylation of Electrode Architectures (SPEAR) versus traditional electrochemically lithiated architectures (ECLAR), focusing on SEI compositional changes as a function of stoichiometry (0.28 ≤ x ≤ 1.38 in LixSi). Increasing SPEAR prelithiation decreased the initial VOC of Si anodes vs. Li/Li+ from ∼3 V (Li0.28Si) to < 0.5 V for Li1.38Si, enabling simultaneous competitive reduction of EC, EMC, and LiPF6 at low potentials. Ex situ7Li and 29Si cross-polarization NMR and XPS reveal that SPEAR drives thicker SEI formation with substantially increased P/F contributions and a predominantly inorganic insoluble SEI (71.4% inorganic for Li1.38Si), consistent with accelerated LiPF6-derived POx/LiPFx/LiF formation relative to ECLAR analogs which exhibit carbonate-rich organic SEI compositions. Symmetric-cell EIS further indicates SPEAR-specific impedance features consistent with pore reduction (filling) during LixSi formation. In full cells, SPEAR prelithiation increases the initial coulombic efficiency (ICE) and accelerates SEI formation and stabilization with Li1.38Si reaching 99.4% coulombic efficiency (CE) by cycle 2.

Musgrove, Amanda [ORNL] (ORCID:0009000220910389)↗

DOE OSTI2025

On the Efficacy of Repeat Voltage Holds for Conditioning and Calendar Life Testing of Graphite and Silicon Cells

Voltage-hold (V-hold) protocols have shown promise toward calendar lifetime analysis of cells with graphite (Gr) and silicon (Si) anodes. In this work, repeat V-holds are performed on Gr and Si cells paired with lithium iron phosphate cathodes to delineate their beneficial role in formation and conditioning. We find that V-hold at the top of charge supplements constant current cycling in conditioning the cell to higher capacities for both Gr and Si cells after the first V-hold. A reduced order model provides the irreversible capacity proportions of each V-hold. With each repeat V-hold, parasitic loss of lithium to the solid electrolyte interphase (SEI) decreases on both Gr and Si cells. Gr cells show the square-root-of-time capacity loss behavior within 200 h of V-hold, indicative of its fast relaxation and low impact of reference performance test cycles on the SEI growth. Lifetime estimates from repeat V-holds on Gr can reach years. Si exhibits longer transition times from kinetic to diffusion-limited SEI growth, evidenced by the 400 h and 200 h holds showing square-root-of-time and linear behavior, respectively. Lifetime predictions from repeat V-holds on Si only reach 1–2 months, highlighting its limitations. Recommended duration of V-holds for Si cells should be ≥400 h.

25 ENERGY STORAGE↗

DOE OSTI2025

Solid‐State Prealkylation of Electrode Architectures (SPEAR): Direct Control of Prelithiation Levels in Silicon Anodes and Electrochemical Cycling

The Solid-state Prealkylation of Electrode ARchitectures (SPEAR) is different than traditional electrochemical prealkylation processes. Through SPEAR, alkylation is driven by solid-state diffusion without the simultaneous SEI formation concomitant with polarization. Here, we investigate the prelithiation of 80 wt. % Si-based anodes to varying amounts (up to Li 1.38 Si) to understand the trade-off between improved Li capacity and expansion-induced stress. Through dilatometry, we found that solid-state lithiation led to filling of the electrode pores through silicon expansion. This swelling changed the SEI formation process and accessibility of the silicon compared to an electrochemically lithiated electrode. Indeed, optimal prelithiation to Li 0.82 Si increases the initial C/3 cycling capacity post-SEI formation up to 43%, consistent with deeper Si activation through the electrode bulk. Prelithiation and cycling cells prelithiated beyond Li 0.82 Si results in a state of charge (SOC) close to 100% which facilitates parasitic degradation mechanisms and volume expansion of the Si electrode. The results demonstrate a pathway to modify silicon activation/SEI formation to enable high-energy electrodes.

Musgrove, Amanda L. [Oak Ridge National Laboratory↗

DOE OSTI2025

High tensile alloy of copper to mitigate current collector deformation in silicon electrodes for lithium-ion batteries

The volumetric changes of silicon electrodes, along with the strong adhesive properties of certain binders, can lead to plastic deformation of the current collector and create damage in the electrode coating. Here, in this study, we report a detailed study of silicon coatings on a high-tensile alloy (HTA) foil of copper with strength over twice that of conventional copper foils. The HTA current collectors with high mechanical strength can mitigate plastic deformation upon continuous cycling. At moderate areal capacities (2.5–3 mAh cm −2 ), conventional copper foils show significant wrinkling after only a few electrochemical cycles, whereas the HTA foils remain intact. We demonstrate viability of the HTA foils in large format xx6395 pouch cells, in which the HTA current collectors remain intact even at an areal capacity of 4.5 mAh cm −2 ; in contrast, wrinkles form in conventional copper current collectors increasing the likelihood of lithium plating. Computational studies show that stresses generated during cycling of silicon electrodes are very high in the current collector and at the current collector-coating interface, explaining the wrinkling of conventional Cu foils. Our studies highlight importance of current collector to solve the electrochemical and chemo-mechanical performance challenges associated with high-loading silicon electrodes.

Chemo-mechanical degradation↗

DOE OSTI2025

Surprising Relationship between Silicon Anode Calendar Aging and Electrolyte Components in a Localized High-Concentration Electrolyte System

Although localized high-concentration electrolytes (LHCEs) have been shown to improve the calendar lifetime of silicon anodes, the roles of the electrolyte constituents in calendar aging are not well understood. Here, in this work, we utilize a voltage hold protocol and an LHCE with varying molar ratios of lithium bis(fluorosulfonyl)imide (LiFSI), tetramethylene sulfone (TMS), and 1,1,2,2-tetrafluoroethyl-2,2,3,3-tetrafluoropropyl ether (TTE) to probe the component roles during aging. Interestingly, the estimated calendar lifetime and irreversible lithium losses from the V-hold experiments are independent of the electrolyte formulations. Contrarily, the solid electrolyte interphase (SEI) composition depends on the electrolyte formulation. X-ray photoelectron spectroscopy shows that TMS-coordinated species decompose to form insoluble alkanes and lithium hydroxide (LiOH), while lithium fluoride (LiF) originates from the anion-coordination complex. The SEI composition does not appear to play a significant role in the silicon anode passivity, as measured by parasitic current, suggesting that the SEI-electrolyte interactions dictate the calendar aging mechanisms.

Si anode↗