NASA NTRS1990

Functionalized poly(arylene ethers) as toughness modifiers for bismaleimides

A family of novel, low molecular weight functionalized poly(arylene ether) resins has been investigated to ascertain its members' toughness-imparting contribution to neat bismaleimide (BMI) resin and BMI-matrix laminate composite properties. Attention is given to the contribution of the reactive poly(arylene ether)'s backbone chemistry to fracture toughness, as well as to the comparative influence of high and low molecular weight reactive poly(arylene ether) types on the modified BMI resin systems. The modified BMIs possess a polyphase morphology, with good adhesion between the thermoplastic nodules and the host thermoset systems.

Stenzenberger, H. D.↗

NASA NTRS1989

Tough poly(arylene ether) thermoplastics as modifiers for bismaleimides

Several aspects of research on thermoplastics as toughness modifiers are discussed, including the contribution of the backbone chemistry and the concentration of the poly(arylene ether) thermoplastic to fracture toughness, influence of the molecular weight of the poly(arylene ether) thermoplastic on neat resin fracture toughness, and the morphology of the thermoplastic modified networks. The results show that fracture toughness of brittle bismaleimide resins can be improved significantly with poly(arylene ether) thermoplastic levels of 20 percent by weight, and that high molecular weight poly(arylene ether) based on bisphenol A provides the highest degree of toughening. Preliminary composite evaluation shows that improvements in neat resin toughness translate into carbon fabric composite.

Stenzenberger, H. D.↗

NASA NTRS1979

Development and fabrication of bismaleimide-graphite composites

The successful fabrication of high temperature resistant composites depends mainly on the processability of the resin binder matrix. For two new bismaleimide type resins the processing of graphite fabric prepregs to composites is described. One resin coded M 751 has to be processed from N-Methylpyrrolidone, the other resin evaluated is a so-called hot melt solvent-less system. Commercial T300/3000 Graphite fabrics were used as reinforcement. The M 751 - Resin is a press grade material and laminates are therefore moulded in high pressure conditions (400 N/sq cm). The solvent-less resin system H 795 is an autoclave grade material and can be cured at 40 N/sq cm. The cure cycles for both the press grade and the autoclave grade material (Fiberite W 143 fabric prepregs) are provided and the mechanical properties of laminates at low (23 C) and high (232 C) temperatures were measured. For comparison, the neat resin flexural properties are also presented. The water absorption for the neat resins and the graphite fabric laminates after a 1000 hour period was evaluated.

Stenzenberger, H.↗