Critical instability at moving keyhole tip generates porosity in laser melting

Laser powder bed fusion is a dominant metal 3D printing technology. However, porosity defects remain a challenge for fatigue-sensitive applications. Some porosity is associated with deep and narrow vapor depressions called keyholes, which occur under high-power, low–scan speed laser melting conditions. High-speed x-ray imaging enables operando observation of the detailed formation process of pores in Ti-6Al-4V caused by a critical instability at the keyhole tip. We found that the boundary of the keyhole porosity regime in power-velocity space is sharp and smooth, varying only slightly between the bare plate and powder bed. The critical keyhole instability generates acoustic waves in the melt pool that provide additional yet vital driving force for the pores near the keyhole tip to move away from the keyhole and become trapped as defects.

47 OTHER INSTRUMENTATION↗
DOE OSTI2020

Microscale Observation via High-Speed X-ray Diffraction of Alloy 718 During In Situ Laser Melting

The laser melting process is accompanied by rapid evolution in temperature, phase, structure, and strain because of its high heating and cooling rates. In this study, the evolution of grains within a thin solid plate of Ni alloy 718 during laser processing was probed with in situ high-energy x-ray diffraction experiments. The high temporal and spatial resolution available in the measurement allowed us to study the rapid evolution of the melted region beneath the surface of the sample. The characterization of the evolution of secondary phases, i.e., Laves and carbide, was captured despite the weak diffracted peaks caused by small volume fractions. Thermal history was estimated based on changes in the lattice spacing from the thermal contraction upon cooling. In conclusion, the temporal variation in 2θ with azimuthal direction revealed the evolution in anisotropy of lattice spacing and thus of the mechanical state during laser processing.

36 MATERIALS SCIENCE↗
DOE OSTI2020

High-Energy X-Ray Diffraction Microscopy in Materials Science

High-energy diffraction microscopy (HEDM) is an implementation of three-dimensional X-ray diffraction microscopy. HEDM yields maps of internal crystal orientation fields, strain states, grain shapes and locations as well as intragranular orientation distributions, and grain boundary character. Because it is nondestructive in hard materials, notably metals and ceramics, HEDM has been used to study responses of these materials to external fields including high temperature and mechanical loading. Currently available sources and detectors lead to a spatial resolution of ~1 μm and an orientation resolution of <0.1°. With the penetration characteristic of high energies ( E ≥ 50 keV), sample cross-section dimensions of ~1 mm can be studied in materials containing elements across much of the Periodic Table. This review describes hardware and software associated with HEDM as well as examples of applications. Overall, these applications include studies of grain growth, recrystallization, texture development, orientation gradients, deformation twinning, annealing twinning, plastic deformation, and additive manufacturing. We also describe relationships to other X-ray-based methods as well as prospects for further development.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Effect of heat treatment on microstructural evolution and hardness homogeneity in laser powder bed fusion of alloy 718

The thermal history developed in laser powder bed fusion (LPBF) processes has been shown to be complex resulting in equally complex microstructures and mechanical properties. Microscopic observations and Vickers micro-hardness mapping measurements were carried out on diff ;erent section planes of LPBF alloy 718 cuboids. Three-dimensional finite element analysis was used to simulate thermal history and to predict the residual stress distribution in the as-built material. Computational thermodynamics was used to predict the micro-segregation and nucleation driving force of various phases in the bulk and in segregated regions. Varied heat-treatments such as simulated hot isostatic pressing, and double aging were applied. Their influence on the microstructure, microsegregation, precipitate formation, and micro-hardness variations of LPBF alloy 718 were investigated. Hardness map results showed heterogeneous micro-hardness on the xy- and xz-planes of the as-built parts where the bottom plane and center regions had larger hardness of ~315 HV 0.5 while the top plane and contours showed hardness of ~300 HV 0.5 . It was found that the aging treatment increased the overall hardness of the as-built condition from ~310 HV 0.5 to 470 HV 0.5 but also increased the hardness gradient throughout the coupon. After simulated hot isostatic pressing process (i.e., without applied pressure) at 1020 °C for 4 h followed by water quench (HIPWQ), the hardness gradient and hardness was minimized (~210 HV 0.5 ) as the microstructure transitioned from heterogeneous columnar grains in the as-built condition to more uniform recrystallized grains. A double aging treatment was applied to enhance hardness from ~210 HV 0.5 to ~440 HV 0.5 . Finally, HIPWQ followed by double aging produced a homogeneous microstructure and more uniform hardness map with enhanced mechanical properties in LPBF alloy 718 coupons.

36 MATERIALS SCIENCE↗