DOE OSTI2026

Improved Mechanical Adhesion Enabled by Bilayer Hole Transport Layers in Perovskite Solar Cells

We investigate buried-interface mechanical integrity in metal-halide perovskite half-cells using carbazole-based self-assembled monolayers (SAMs) and bilayer hole transport layers composed of metal oxide underlayers and SAMs. Combining macroscopic and microscopic characterization, we quantify interfacial fracture energy (Gc) and identify delamination pathways. SAM deposition on NiOx increases Gc by approximately 10-fold compared with ITO, highlighting the importance of oxide underlayer selection. To isolate the effect of removing noncovalently bonded SAM molecules, we use vapor-deposited perovskite as a solvent-free model system, decoupling the rinse step inherent to solution processing. Removing loosely bound SAM molecules increases Gc from 0.94 +- 0.08 J.m-2 to 4.82 +- 0.79 J.m-2. These results show that oxide selection and SAM binding quality are both critical for strengthening buried interfaces and designing mechanically robust perovskite solar cells.

14 SOLAR ENERGY↗

DOE OSTI2025

C60-Based Ionic Salt Electron Shuttle for High-Performance Inverted Perovskite Solar Modules

Although C60 is usually the electron transport layer (ETL) in inverted perovskite solar cells, its molecular nature of C60 leads to weak interfaces that lead to non-ideal interfacial electronic and mechanical degradation. Here, we synthesized an ionic salt from C60, 4-(1',5'-dihydro-1'-methyl-2'H-[5,6] fullereno-C60-Ih-[1,9-c]pyrrol-2'-yl) phenylmethanaminium chloride (CPMAC), and used it as the electron shuttle in inverted PSCs. The CH2-NH3+ head group in the CPMA cation improved the ETL interface and the ionic nature enhanced the packing, leading to ~3-fold increase in the interfacial toughness compared to C60. Using CPMAC, we obtained ~26% power conversion efficiencies (PCEs) with ~2% degradation after 2,100 hours of 1-sun operation at 65degrees C. For minimodules (four subcells, 6 centimeters square), we achieved the PCE of ~23% with <9% degradation after 2,200 hours of operation at 55degrees C.

14 SOLAR ENERGY↗