Engineering topics

Romedenne, Marie

Publications and source records attributed to Romedenne, Marie.

22 records · Page 2

DOE OSTI2021

Compatibility of SiC with ODS FeCrAl in flowing Pb-Li at 600° - 700°C

To establish the maximum operating temperature for the dual coolant lead lithium (DCLL) blanket concept, thermal convection loop (TCL) experiments were conducted for 1000 h with a peak temperature of 700 °C to determine compatibility with commercial eutectic Pb~17at.%Li. Two TCLs were fabricated from alloy APMT (FeCrAlMo) and the baseline TCL experiment contained only APMT specimens. The second TCL experiment exposed more fusion relevant CVD SiC and ODS Fe-10Cr-6Al specimens in the hot and cold legs. In the second experiment, the mass losses were much larger for the ODS FeCrAl specimens and most of the CVD SiC specimens experienced a mass gain as SiC reacted to form an Fe- and Cr-rich carbide reaction product. Dissolved Fe and Cr reacted with the SiC and removing Fe and Cr from the liquid appeared to increase ODS FeCrAl dissolution. Such a dissimilar material interaction appears consistent with thermodynamic calculations. Significant attack at the top of the hot leg in both experiments suggests that the Pb-Li compatibility of FeCrAl alloys is inadequate at 700 °C in a flowing environment and the maximum PbLi temperature is < 675 °C.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Oxidation Behavior of Candidate NiCr Alloys for Engine Exhaust Valves: Part I—Effect of Minor Alloying Elements

Oxidation-induced degradation of structural materials employed as exhaust valves within internal combustion engines (ICEs) will be a relevant life-limiting mechanism, in addition to creep and mechanical fatigue, due to ever-increasing severity of operating temperatures and pressures. Ni–Cr-based alloys, which form external chromia-based scales at the relevant operating temperatures are being considered as suitable candidate materials. Thermal cycling of these alloys in water vapor-containing atmospheres, such as those present during hydrocarbon fuel combustion within ICEs, can considerably influence their oxidation behavior. Here, the role of typical alloying additions such as Mn, Si, Al and Ti on the cyclic oxidation behavior of model NiCr–X (X = Mn,Si,Al,Ti) alloys exposed in dry air and air + 10% H 2 O at 800°C and 950°C was investigated. Combined additions of Mn and Si reduced scaling rates compared to binary Ni–22Cr alloys. The presence of water vapor possibly suppressed formation of NiMnCr spinel and thereby the Cr depletion in the alloy. Combined Al and Ti additions mainly resulted in accelerated oxidation kinetics due to the Ti doping of chromia scales. More porous external scales were observed in water vapor leading to a much deeper depth of nitridation in the Ni–22Cr–Al–Ti alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Quantitatively accounting for the effects of surface topography on the oxidation kinetics of additive manufactured Hastelloy X processed by electron beam melting

In this work, the effects of surface roughness on the high-temperature corrosion of nickel-based superalloy X produced through electron-beam melting (EBM) additive manufacturing were studied. Surface area of samples in the rough, as-fabricated condition was measured using a 2D cross-section image analysis technique and a 3D image analysis technique. To verify the accuracy of surface area measurements, oxidation testing of samples in the as-fabricated and polished conditions was performed; polished sample oxidation curves were then compared to the as-fabricated sample oxidation curves before and after being adjusted using obtained surface area measurements. It was found that the 2D technique accurately measured surface area and accounted for the overlapping features present on EBM sample surfaces, whereas the 3D technique did not. Further, it was also observed that oxidation kinetics were moderately faster on the alloy X samples in the as-fabricated condition than for the polished condition.

36 MATERIALS SCIENCE↗

DOE OSTI2020

High temperature air oxidation behavior of Hastelloy X processed by Electron Beam Melting (EBM) and Selective Laser Melting (SLM)

The microstructure and oxidation behavior of Laser Beam Melted, Electron Beam Melted and wrought Hastelloy X were studied at 950 °C in dry air, 50 h cycles, up to 1000 h. The variability of processing parameters and powder compositions strongly impacted the oxidation and spallation behavior. Finally, the alloys with high Mn and Si were associated with higher oxidation rates, finer Cr 2 O 3 grain microstructure and increased spallation was observed for the alloys with large elongated grain microstructures (aspect ratio of 10 ± 3).

36 MATERIALS SCIENCE↗