Angle-Resolved Polarized Raman Study of Layered Cr 2 Se 3

The polarization-resolved Raman spectra of two-dimensional Cr 2 Se 3 synthesized via chemical vapor deposition (CVD) and chemical vapor transport (CVT) techniques were investigated in detail. The samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and energy-dispersive X-ray spectroscopy (EDS). A distinct polarization dependence was observed in the Raman intensity of all the Cr-Cr, Cr-Se, and Se-Se modes in both samples. The observed angle-dependent Raman intensities of each peak could be related to the crystal structure-specific Raman tensor. XRD results of the bulk Cr 2 Se 3 sample synthesized via CVT confirm its trigonal crystal structure, and the Raman peaks can be fitted using the Raman tensors for the A g and E g modes for both the parallel and crossed polarizations. However, for the Cr 2 Se 3 samples directly grown on Si/SiO 2 substrates by CVD, it was necessary to assume the triclinic crystal structure in order to explain the polarized Raman dependence of all the peaks in both parallel and crossed polarization directions. Furthermore, this is the first experimental result suggesting the existence of triclinic Cr 2 Se 3 crystal structure, which has been theoretically predicted in the Materials Project database.

36 MATERIALS SCIENCE↗

DOE OSTI2024

The effects of thickness, polarization, and strain on vibrational modes of 2D Fe 3 GeTe 2

In this study, we investigated the effects of thickness, light polarization, and strain on the Raman spectra of two-dimensional (2D) Fe 3 GeTe 2 (FGT) crystals synthesized via chemical vapor transport. The crystals are thoroughly characterized using a combination of microscopic, diffraction, and spectroscopic techniques. Particularly, a systematic angle-resolved polarized Raman spectroscopy study reveals a clear polarization dependence of the Raman intensity in both parallel and crossed polarization directions, with the $A$$^{1}_{g}$ mode completely disappearing in the crossed polarization direction. The angle-dependent intensity of both the $A$$^{1}_{g}$ and $E$$^{2}_{2g}$ modes in parallel polarization and the intensity of the $E$$^{2}_{2g}$ mode in the crossed polarization remain constant at all angles. These findings align with predictions from Raman tensor analysis, providing compelling evidence for the unambiguous assignment of the $A$$^{1}_{g}$ and $E$$^{2}_{2g}$ modes to specific peaks observed in the Raman spectrum of FGT, resolving existing confusion in the literature regarding their assignment. Furthermore, we examine the effect of strain on the Raman spectrum of 2D FGT in-situ using a bending device. Our study, conducted on a monolayer to few-layer 2D FGT deposited onto polyethylene terephthalate and subjected to outward (inward), i.e., tensile (compressive) bending, demonstrates appreciable downshifting (upshifting) of the Raman peak position of both $A$$^{1}_{g}$ and $E$$^{2}_{2g}$ modes. Furthermore, these findings are particularly significant given that strain engineering represents an effective approach to modulate the magnetic properties of FGT and other 2D magnetic materials.

2D materials↗