DOE OSTI2024

Ramifications of X-Site Ion Modification in a Zero-Dimensional Piezoelectric Tetrahalozincate

Using mixtures of A, B, or X site ions in piezoelectric hybrid organic inorganic materials has been shown to be an effective strategy to improve piezoelectric properties. Here, we investigated the effect of increasing Br content within histammonium tetrachlorozincate [HistNH3Zn(Cl x Br 1–x )4] by varying the relative amounts of Cl and Br from x = 0% to 100% on nonlinear optical and piezoelectric properties. We found that the crystal structures were unchanged with Br percentages up to 100%, but the melting point of the materials changed substantially with increasing Br content. On the other hand, the nonlinear optical properties were only moderately affected with increasing Br content. The piezoelectric response of each material was measured and compared with DFT calculated values, both of which agreed that the overall the materials had relatively similar d 33 coefficients. The x = 75% Br compound had the largest magnitude d 33 value at maximum strain at both 29 °C (−97.56 pm/V) and 40 °C (−92.00 pm/V). The observed negative piezoelectric response is a rare trait that was ascribed to the large number of intermolecular interactions between lattice elements, as described by others.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Micromechanical Fields Associated with Irregular Deformation Twins in Magnesium

Understanding and controlling the development of deformation twins is paramount for engineering strong and stable hexagonal close-packed (HCP) Mg alloys. Actual twins are often irregular in boundary morphology and twin crystallography, deviating from the classical picture commonly used in theory and simulation. In this work, the elastic strains and stresses around irregular twins are examined both experimentally and computationally to gain insight into how twins develop and the microstructural features that influence their development. A nanoprecession electron diffraction (N-PED) technique is used to measure the elastic strains within and around a $\left\{ {10\overline{1}2} \right\}$ tensile twin in AZ31B Mg alloy with nm scale resolution. A full-field elasto-viscoplastic fast Fourier transform (EVP-FFT) crystal plasticity model of the same sub-grain and irregular twin structure is employed to understand and interpret the measured elastic strain fields. The calculations predict spatially resolved elastic strain fields in good agreement with the measurement, as well as all the stress components and the dislocation density fields generated by the twin, which are not easily obtainable from the experiment. The model calculations find that neighboring twins, several twin thicknesses apart, have little influence on the twin-tip micromechanical fields. Furthermore, this work reveals that irregularity in the twin-tip shape has a negligible effect on the development of the elastic strains around and inside the twin. Importantly, the major contributor to these micromechanical fields is the alignment of the twinning shear direction with the twin boundary.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Boundary characterization using 3D mapping of geometrically necessary dislocations in AM Ta microstructure

Additive manufacturing (AM) of high strength metallic materials produces microstructures and defects that deviate substantially from those created through conventional manufacturing methods. It has recently been demonstrated that with application of extreme energy densities, a high-temperature refractory metal, tantalum (Ta), can be printed to a fully dense state with exceptionally low porosity. Here we employ a combination of three-dimensional electron backscattered diffraction (EBSD) TriBeam technology and crystallographic geometrically necessary dislocation (GND) theory to characterize the microstructure and defect boundaries of this unusual AM product. Two-dimensional (2D) EBSD and these three-dimensional (3D) measurements indicate that the microstructure of AM Ta is highly oriented <111> along the build direction, yet at the same time contains large crystallographic orientation gradients that span mm’s across the build. Crystallographic GND density analysis of the 3D microstructure reveals that highly misoriented subboundaries exist within this strongly textured microstructure that have large dislocation densities of 1×10 16 m –2 , just as large as those comprising the high-angle grain boundaries (HAGBs) in the same material. The 3D crystallographic GND density mapping reveals these subboundaries are part of a complex, finely spaced network that extends throughout the entire microstructure. Here, the orientation of these boundaries can be related to the scan strategy used during printing. TEM measurements corroborate an extremely high dislocation density at the microscale and indicate a cell-like dislocation network structure existing in the AM Ta at the sub-μm scale.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Multimodal 3D characterization of voids in shock-loaded tantalum: Implications for ductile spallation mechanisms

Predicting the failure of crystalline materials at high strain rates requires knowledge of the underlying failure mechanisms and their dependence on microstructure. However, little experimental consensus exists on the underlying micromechanics of spallation. In this study, a 3D-EBSD characterization experiment is performed on tantalum prior to and after partial spallation by plate impact, which allowed for the statistical assessment of the microstructural neighborhoods surrounding incipient voids. In analyzing the resulting dataset containing 5884 grains and 467 voids, it is observed that the voids were roughly spherical and consistent in size throughout the spalled material. The voids mostly resided at quadruple points, at triple junctions, at grain boundaries, and within grains, in decreasing order of prevalence. Moreover, voids tended to form at grain boundaries with high degrees of plastic incompatibility, growing into the plastically soft grain but orienting primarily with or perpendicular to the loading direction. Here, the statistics from these analyses of 3D microstructural data support dynamic cavitation models for ductile spallation.

36 MATERIALS SCIENCE↗